This study includes the synthesis of new derivatives of 1, 2, 4- Triazole which are contain Schiff bases derived from 1, 4, 5, 6- tetrahydropyrimidine. The structures of these derivatives were characterized from their melting points, infrared spectroscopy and elemental analysis. These derivatives were tested for inhibition of E-coli and were all found to be active.

Several azo dyes were synthesized through coupling reaetion of some substituted phenols and B.naphthol with diazonium salt of 2- amino-1,3-4- thiadiazol -5- thiol. All the synthesized compounds during this work were characterized using some speetral data (F.TIRand UV)andM.P . 2-[4 --Hydroxy napthyl-azo ] -1,3,4-Thiadiazol -5-Thiol • 2- [2-- hydroxy –4- NO2 – phenyl- azo]- 1,3,4 - Thiadiazol –5-Thiol. • 2- [3--Amino-4-Hydroxy phenyl –azo]-1,3,4 - Thiadiazol –5-Thiol. . • 2-[2--Amino-4-Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol . • 2- [3--Amino-6- Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol. • 2-[2-- Hydroxy- 5 – chloro – Pheny - azo]- 1,3,4 - Thiadiazol –5-Thiol . • 2- [4-- Hydroxy phenyl -azo] -1,

Shiranish formation has been divided into two microfacies units: 1-Marly biowacke stone facies 2-Biogenic pack stone facies These microfacies reflected marine deep shelf margin in the upper part of the formation, the lower part was deeper. 238 slides were investigated depending on Mineralogical, compositional and Biological processes, which reflect deep shelf margin at upper part of the formation, but at the lower part open sea environment. The age of the formation is estimated depending on the recognized biostratigraphic zone using the index fossils to be Upper- Middle Maestrichtian.

This project sought to fabricate a flexible gas sensor based on a short functionalized multi-walled carbon nanotubes (f-MWCNTs) network for nitrogen dioxide gas detection. The network was prepared by filtration from the suspension (FFS) method and modified by coating with a layer of polypyrrole conductive polymer (PPy) prepared by the oxidative chemical polymerization to improve the properties of the network. The structural, optical, and morphological properties of the f-MWCNTs and f-MWCNTs/PPy network were studied using X-ray diffraction (XRD), Fourie-transform infrared (FTIR), with an AFM (atomic force microscopy). XRD proved that the structure of f-MWCNTs is unaffected by the synthesis procedure. The FTIR spectra verified the existence o

This work was conducted to study the ability of locally prepared Zeolite NaY for the reduction of sulfur compounds from Iraqi natural gas by a continuous mode adsorption unit. Zeolite Y was hydrothermally synthesized using abundant kaolin clay as aluminum precursor. Characterization was made using chemical analysis, XRD and BET surface area. Results of the adsorption experiments showed that zeolite Y is an active adsorbent for removal H2S from natural gas and other gas streams. The effect of temperature was found inversely related to the removal efficiency. Increasing bed height was found to increase the removal efficiency at constant flow rate of natural gas. The adsorption capacity was evaluated and its maximum uptake was 5.345 mg H2S/g z

This work was conducted to study the ability of locally prepared Zeolite NaY for the reduction of sulfur compounds from Iraqi natural gas by a continuous mode adsorption unit. Zeolite Y was hydrothermally synthesized using abundant kaolin clay as aluminum precursor. Characterization was made using chemical analysis, XRD and BET surface area. Results of the adsorption experiments showed that zeolite Y is an active adsorbent for removal H2S from natural gas and other gas streams. The effect of temperature was found inversely related to the removal efficiency. Increasing bed height was found to increase the removal efficiency at constant flow rate of natural gas. The adsorption capacity was evaluated and its maximum uptake was 5.345 mg H2S/g z

   A new nano-sized NiMo/TiO₂-γ-Al₂O₃ was prepared as a Hydrodesulphurization catalyst for Iraqi gas oil with sulfur content of 8980 ppm, supplied from Al-Dura Refinery. Sol-gel method was used to prepare TiO₂- γ-Al₂O₃ nano catalyst support with 64% TiO_2, 32% Al₂O₃, Ni-Mo/TiO-γ-Al₂O₃ catalyst was prepared under vacuum impregnation conditions to loading metals with percentage 3.8 wt.% and 14 wt.% for nickel and molybdenum respectively while the percentage for alumina, and titanium became 21.7, and 58.61 respectively. The synthesized TiO₂- γ-Al₂O₃ nanocomposites and Ni-Mo /TiO₂

In this study, the mechanical properties of an epoxy and unidirectional woven carbon with fiberglass composite were experimentally investigated. When preparing the composite samples, American Society for Testing and Materials (ASTM)standard was used. Tensile, impact and flexural test were conducted to investigate the mechanical properties of the new produced epoxy Unidirectional Woven Carbon and Epoxy Fiberglass composites. The outcome showed that the strength of the produced samples increased with the increase in the number of unidirectional woven carbon layers added. Two methods were utilized: (1) woven carbon composite with glass fiber (2) woven carbon composite). The two methods of composite were compared with each other.  The resul