The present work aimed to study the SiO2μPs, and NPs effect on the biodegradability of St/PVA blends. The samples were prepared by casting method as PVA, St/PVA blends with different concentrations (30, 40, 50, and 60 %). FTIR test was carried out for the samples preparation. The results proved some changes which might be related to changing in crystallinity of St/PVA matrix as well as physical incorporation of SiO2 μPs, and NPs addition. The enzymatic test and water uptake results proved that increase in weight loss with increases of starch ratio. The lowest weight loss was PVA; the highest weight loss is 60% St/PVA whereas the lowest weight loss is 30%St/PVA for blends involved. SiO2μPs (753.7 nm), and NPs (263.1 nm) were added at d

In this study porcelain was prepared by using composition consisting of raw materials with in following fractions , 50% kaolin , 25% feldspar, and 25% silica( SiO2) tested by XRay diffraction (XRD) method .Study the effect additives at different concentration from zirconia (ZrO2) (2,5,10,15,20) Wt% on some physical properties of porcelain, the sample is prepared by the conventional manufacturing method , It is found that some physical properties of porcelain changes considerably with the substituent sample, It was found that the increase of zrconia (ZrO2) additive of all our sample produce. Increasing in dielectric constant and bulk density and decreasing with open porosity and dielectric loss tangent

    Different percents(1.0,2.5,5.0 and 10)wt%of MgO powders were added to ZnO powder to study their effects on the physical properties of ZnO.Density, porpsity and water absorption of ZnO were decreased as MgO weigth percentage content increased. The values of vickers hardneess have double values especially at 1.0 wt % of MgO.

In the present study, synthesis of bis Schiff base [I, II] by reaction of one mole of terephthalaldehyde with two mole of 2-amino-5-mercapto-1,3,4-thiadiazole or 4-amino benzene thiol in the ethanol absolute, then compounds [I,II]  were reacted with Na₂CO₃ of distilled H₂O, then chloroacetic acid was added to yield compounds [III,IV]. O-chitosan derivatives [V,VI] were synthesized by reaction of chitosan with compounds [III,IV] in acidic media in distilled water according to the steps of Fischer. O–chitosan (grafted chitosan) [V,VI] was blended with synthetic polymer polyvinyl alcohol (PVA) to produce polymers [VII,VIII], then these polymers were blended with nano: Gold or Silver by u

Two different polyvinyl alcohol/polyvinyl chloride (PVA/PVC) hollow fiber composite nanofiltration membranes were prepared after PVC hollow fiber membranes were coated using dip-coating method with PVA aqueous solution, which was composed of PVA, fatty alcohol polyoxyethylene ether (AEO9), and water [PVA/AEO9/water (4:0.5:95.5) wt%]. Effect of two different PVC hollow fiber immersion times in coating solution were studied. Cross-section, internal and external surfaces of the PVC hollow fibers and PVA/PVC composite nanofiltration membranes structures were characterized by scanning electron microscopy (SEM), pure water permeation flux and solutes rejection. It was found that, the coating layer thickness on the outer surface of the 19 wt% P

  Two arylenedisuccinamic acids, namely 1,4-phenylene-disuccinamic acid and 4,4'biphenyl-disuccinamic acid were prepared from the reaction of two moles of succinic anhydride with one mole of 1,4-phenylenediamine dihydrochloride and beinzidine respectively.Dehydration of arylenedisuccinamic acid in the pressence of polyvinyl alcohol (PVA) and catalytic amount of concentrated.H2SO4,gives N,N'-arylenedisuccinimidesPVAcomposite polymers. Dehydration of arylenedisuccinamic acid (without PVA) in the pressence of catalytic amount of conc. H2SO4 gives N,N'-arylenedisuccinimides. Arylenedisuccinamic acid and arylenedisuccinimides characterized by CHN-analysis,FT.IR and 1H,C13-NMR.Spectral analysis

This study included preparation for the unsaturated polyester samples before and after reinforced by Alumina oxide powder and copper oxide powder of different volume fraction amounting (3%,5%,8%). And this reearch included study of some of mechanical properties such as (hardness,compressive and wear).The results showed that increase of the hardness and compressive strength after the reinforced and increase with the volume fraction increase.As the wear test show that the wear rate increases with applied load from the different load(5,10,15)N,and the wear rate decreases with the volume fraction increase.

The ceramic compound Mg1-xSixAl2O4 (x= 0, 0.1, 0.2, 0.3, 0.4) was prepared from nano powder of Al2O3 and MgO doped with Nano powder of SiO2 at different molar ratios. The specimens were prepared by standard chemical solid reaction technique and sintered at 1450 oC. Structure of the specimens was analyzed by using X-ray diffraction (XRD). The X-ray patterns of the specimens showed the formation of pure simple cubic spinel structure MgAl2O4 phase with space group of ̅ . The average grain size and surface topology were studied by atomic force microscopy. The results showed that the average grain size was about 73-90 nm. The DC electrical properties of the specimen were measured. The apparent density was found to increase and the porosity a

The inhibitive power of Polyvinyl Alcohol (PVA) was investigated toward the corrosion of carbon steel in 0.2N H₂SO₄ solution in the temperature range of 30-60˚C and PVA concentration range of 150-2000 ppm.

   The corrosion rate was measured using both the weight loss and the electrochemical techniques. The weight loss results showed that PVA could serve as a corrosion inhibitor but its inhibition power was found to be low for the corrosion of carbon steel in the acidic media. Electrochemical analysis of the corrosion process of carbon steel in an electrochemical corrosion cell was investigated using 3-Electrode corrosion cell. Polarization technique was used for carbon steel corrosion in 0.2N H

       A new class of biologically active nanocomposites and modified polymers based on poly (vinyl alcohol) (PVA) with some organic compounds [II, IV, V and VI] were synthesized using silver nanoparticles (Ag-NPs). All compounds were synthesized using nucleophilic substitution interactions and characterized by FTIR, DSC and TGA. The biological activity of the modified polymers was evaluated against: gram (+) (staphylococcus aureus) and gram (-): (Es cherichia coli bacteria). Antimicrobial films are developed based on modified poly (vinyl alcohol) MPVA and Ag-NPs nanoparticles. The nanocomposites and modified polymers showed better antibacterial activities against Escherichia coli (Gram negative) than against Staphyloc