In this work, silicon nitride (Si₃N₄) thin films were deposited on metallic substrates (aluminium and titanium sheets) by the DC reactive sputtering technique using two different silicon targets (n-type and p-type Si wafers) as well as two Ar:N₂ gas mixing ratios (50:50 and 70:30). The electrical conductivity of the metallic (aluminium and titanium) substrates was measured before and after the deposition of silicon nitride thin films on both surfaces of the substrates. The results obtained from this work showed that the deposited films, in general, reduced the electrical conductivity of the substrates, and the thin films prepared from n-type silicon targets using a 50:50 mixing ratio and deposited on both

Powders for (TiO 2 ) 1−x(MoO 3 ) x composites have been prepared with the use of a dry mix of TiO2 and MoO3 oxides with a variety of compositions (x = 0, 0.2, 0.4, 0.6, 0.8, and 1), then sintering at 1473 K. The materials have been ground and formed into pellets so that they could be used as targets for the pulsed laser deposition (PLD) process, which produced thin flms with a thickness of ≈150 nm on a glass substrate. When MoO3 is added to TiO2 , the crystal size has been observed to decrease from 33.3 to 25.8 nm, yet it after that continued to expand as MoO3 was added. The molybdenum ions were confrmed by XRD patterns, indicating that the substitution regarding Mo+6 ions for Ti +4 ions in TiO2 matrix is what is re

In oil and gas well cementing, a strong cement sheath is wanted to insure long-term safety of the wells. Successful completion of cementing job has become more complex, as drilling is being done in highly deviated and high pressure-high temperature wells. Use of nano materials in enhanced oil recovery, drilling fluid, oil well cementing and other applications is being investigated. This study is an attempt to investigate the effect of nano materials on oil well cement properties. Two types of nano materials were investigated, which are Nano silica (>40 nm) and Nano Alumina (80 nm) and high sulfate-resistant glass G cement is used. The investigated properties of oil well cement included compressive strength, thickening

Nanomaterials enhance the performance of both asphalt binders and asphalt mixtures. They also improve asphalt durability, which reduces resource consumption and environmental impact in the long term associated with the production and transportation of asphalt materials. Thus, this paper studies the effectiveness of Nano Calcium Carbonate (Nano CaCO3) and Nano Hydrated Lime (NHL) as modifiers and examines their impact on ranges from 0% to 10% through comprehensive laboratory tests. Softening point, penetration, storage stability, viscosity, and mass loss due to short-term aging using the Rolling Thin Film Oven Test (RTFO) were performed on asphalt binders. Results indicated a significant improvement in binder stiffness, particularly

One of the most recent research areas in subsurface applications, including well drilling, is the use of eco-friendly and sustainably synthesized nanoparticles to improve drilling fluid efficiency. Typically, Shale formations present significant challenges to traditional drilling fluids, including fluid infiltration and shale swelling, which jeopardize wellbore stability. Although water-based drilling fluids (WBM) are environmentally preferred, their performance often requires enhancement through advanced additives. This study thus examines the synthesis of silica (SiO₂) and alumina (Al₂O₃) nanoparticles (NPs) using sustainable methods, employing Iraqi bentonite for silica and recycled aluminum scrap for alumina, to improve WBM effici

In this paper, silicon carbonitried thin films were prepared by the method of photolysis of the silane (SiH4) and ethylene (C2H4) gases, with and without ammonia gas (NH3), which is represented by the ratio between the (PNH3) and (PSiH4 + PC2H4 + PNH3), (which assign by the letter X), X has the values (0, 0.13, 0.33). This method carried out by using TEA-CO2 laser, on glass substrate at (375 oC), deposition rate (0.416-0.833) nm/pulse thin film thickness of (500-1000) nm. The optical properties of the films were studied by using Absorbance and Transmittance spectrums in wavelength range of (400-1100) nm, the results showed that the electronic transitions is indirect and the energy gap for the SiCN films increase with increasing of nitrog

Thin films of (CdO)x (CuO)1-x (where x = 0.0, 0.2, 0.3, 0.4 and 0.5) were prepared by the pulsed laser deposition. The CuO addition caused an increase in diffraction peaks intensity at (111) and a decrease in diffraction peaks intensity at (200). As CuO content increases, the band gap increases to a maximum of 3.51 eV, maximum resistivity of 8.251x 104 Ω.cm with mobility of 199.5 cm2 / V.s, when x= 0.5. The results show that the conductivity is ntype when x value was changed in the range (0 to 0.4) but further addition of CuO converted the samples to p-type.