Effect of water absorption on some mechanical and physical properties of epoxy/polyurethane blend reinforced with nano silica powder
...Show More Authors

The aim of this work is to evaluate some mechanical and physical
properties (i.e. the impact strength, hardness, flexural strength,
thermal conductivity and diffusion coefficient) of
(epoxy/polyurethane) blend reinforced with nano silica powder (2%
wt.). Hand lay-up technique was used to manufacture the composite
and a magnetic stirrer for blending the components. Results showed
that water had affected the bending flexural strength and hardness,
while impact strength increased and thermal conductivity decreased.
In addition to the above mentioned tests, the diffusion coefficient
was calculated using Fick’s 2nd law.

Crossref
View Publication
Publication Date
Sun Apr 08 2018
Journal Name
Al-khwarizmi Engineering Journal
Microstructural Characterization and Mechanical Properties of Similar and Dissimilar Al Alloys Joined using Friction Stir Welding
...Show More Authors

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sat Apr 01 2023
Journal Name
Iop Conference Series: Earth And Environmental Science
Effect of Nano and Mineral NPK in Vegetative Growth Parameter of Pear Saplings
...Show More Authors
Abstract<p>An experiment during the two seasons 2019, 2020. The experiment conducted according to Split Plot Design by two factors; the first was addition Nano NPK with five levels (control, addition 7.5 g.plant<sup>-1</sup>, addition 15 g.plant<sup>-1</sup>, spray 1 g.L<sup>-1</sup>, spray 2 g.L<sup>-1</sup>). The second factor was four levels of Mineral NPK which were (control, 50 g.plant<sup>-1</sup>, 100 g.plant<sup>-1</sup>, 50 g.plant<sup>-1</sup>+1.5 g.L<sup>-1</sup>) respectively. N<sub>3</sub> (spray 1 g.L<sup>-1</sup> ) increased plant height, stem diameter first season, branch number se</p> ... Show More
View Publication
Scopus (1)
Scopus Crossref
Publication Date
Sun Mar 13 2011
Journal Name
Baghdad Science Journal
Effect of some plant extracts on germination and seeding of Raphanus sativus and effect on surface growth of Rhizoctonia solani
...Show More Authors

The experiment was conducted to study the effect of leaves extract of Salvia sclarea , Rosmarinus officinalis and Thymus vulgaris with 10% and 30% concentration on germination of seeds and growth of seedlings . The effect of these extracts on infection percentage of seeds decay and surface growth of Rhizoctonia solani . The results showed that the three extracts effected significantly to reduced percentage of seeds germination, acceleration of germination , promoter indicator , infection percentage of seeds decay and surface growth of R. solani especially in 30% concentration .

Publication Date
Tue Jul 22 2025
Journal Name
Journal Of Baghdad College Of Dentistry
A Study the Effect of Addition of Silanized Zirconium Oxide Nanoparticles on Some Properties of High-Impact Heat-Cured Acrylic Resin
...Show More Authors

Background: The incorporation of rubber has not been entirely successful because it can have detrimental effects on the transverse Strength and hence the rigidity of the denture base. Materials and methods: Zirconium oxide nanoparticales were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 3% by weight then mixed with powder using conventional procedure.(100) samples were prepared and divided into five groups according to the test performed ,Each group consisted of 20 specimens and these were subdivided into 2 groupsGroup (A): control group (10 specimens of high impact acrylic resin without zirconium oxide) and Group (B):zirconium oxide group(10 specimens of high impac

... Show More
View Publication Preview PDF
Crossref (10)
Crossref
Publication Date
Wed Jun 01 2022
Journal Name
Iraqi Journal Of Physics
Enhanced Mechanical Property of Acrylic Polymer/Graphene/Carbon Fibers Hybrid for Water Proof Coating
...Show More Authors

In this work, some mechanical properties of the polymer coating were improved by preparing a hybrid system containing Graphene (GR) of different weight percentages (0.25, 0.5, 1, and 2wt%) with 5wt% carbon fibres (CF) and added to a polymer coating by using casting method. The properties were improved as GR was added with further improvement on adding 5wt% of CF. The impact strength of acrylic polymer with GR increases with increasing weight ratio‏‏ of GR; maximum value was obtained when the polymer coating was incorporated with 1wt% GR and 5wt% CF. The impact strength of acrylic polymer with GR and GR/CF composites incorporated with GR at 1wt% and CF at 5wt%. Hardness increase with increasing weight ratio of Gr and a significant imp

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sun Mar 02 2008
Journal Name
Baghdad Science Journal
The synergistic effect of borax and chlorinated paraffin as flame – retardants for epoxy and unsaturated polyester resins
...Show More Authors

In this investigation , borax (B) (additive I) and chlorinated paraffin (CP.) (additive II) ,were used as flame retardants for each of epoxy and unsaturated polyester resins in the weight ratios of 2,4,6, & 8% by preparing films of (130×130×3) mm dimensions. Also films of these resins with a mixture of [50%(B.)+50%(CP.)] (additive III) in the same weight ratios were prepared in order to study the synergistic effect of these additives on the flammability of the two resins . Three standard test methods were used to measure the flame retardation which are : 1-ASTM : D-2863 2-ASTM : D-635 3-ASTM : D-3014

... Show More
View Publication Preview PDF
Crossref
Publication Date
Wed Dec 01 2021
Journal Name
Journal Of Physics: Conference Series
Analytical Study of the Royal-Jelly Effect on Sperms Morphological Characteristics and some Liver Function Parameters and their Correlation with some Antioxidants in Male Albino Rats Treated with Pregabalin Drug
...Show More Authors
Abstract<p>In recent years, the consideration of natural products as anti-inflammatory and antioxidative treatments has more interested worldwide. Moreover, natural products are easily obtained and are relatively safe the Royal jelly (RJ) is one of them. The current study was carried to evaluate the effects of pregabalin (PGB) on physiological activity of sperms, reproductive hormones assay and some biochemical analysis. Forty (40) male albino rats (10-weeks-old) were divided into four groups (10 rats each): G1 (treated with PGB drug, 150 mg/kg B.wt (Lyrica-Pfizer-Pharmaceutical Industries), G2 (treated with RJ 1g/kg), G3 (treated with PGB drug and RJ together), and G4 control treated with norma</p> ... Show More
View Publication Preview PDF
Scopus (1)
Scopus Crossref
Publication Date
Thu Jan 31 2019
Journal Name
Journal Of Engineering
Mechanical Properties Enhancement of Conventional Glass Ionomer Cement by Adding Zirconium Oxide Micro and Nanoparticles
...Show More Authors

The aim of this work is to enhance the mechanical properties of the glass ionomer cement GIC (dental materials) by adding Zirconium Oxide ZrO2 in both micro and nano particles. GIC were mixed with (3, 5 and 7) wt% of both ZrO2 micro and nanoparticles separately. Compressive strength (CS), biaxial flexural strength (BFS), Vickers Microhardness (VH) and wear rate losses (WR) were investigated. The maximum compression strength was 122.31 MPa with 5 wt. % ZrO2 micro particle, while 3wt% nanoparticles give highest Microhardness and biaxial flexural strength of 88.8 VHN and 35.79 MPa respectively. The minimum wear rate losses were 3.776µg/m with 7 wt. % ZrO2 nanoparticle. GIC-contai

... Show More
View Publication Preview PDF
Crossref (13)
Crossref
Publication Date
Sat Sep 30 2023
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
2D and 3D Modeling of Rock Mechanical Properties of Khasib Formation in East Baghdad Oil Field
...Show More Authors

Knowing the distribution of the mechanical rock properties and the far field stresses for the field of interest is an important task for many applications concerning reservoir geomechanics, including wellbore instability analysis, hydraulic fracturing, sand production, reservoir compaction, and subsidence. A major challenge with determining the rock's mechanical properties is that they cannot be directly measured at the borehole. Furthermore, the recovered carbonate core samples for performing measurements are limited and they provide discrete data for specific depths.

   The purpose of this study is to build 2D and 3D geomechanical models of the Khasib reservoir in the East Baghdad oil field/ Central area. TECHLOG.2015.3 softwa

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Mar 06 2025
Journal Name
International Journal Of Applied Mechanics And Engineering
Evaluation of microstructure and mechanical properties resulting from gas nitriding process for different types of steel
...Show More Authors

This work investigates the effect of the gas nitriding process on the surface layer microstructure and mechanical properties for steel 37, tool steel X155CrVMo12-1 and stainless steel 316L. Nitriding was conducted at a temperature of 550 °C for 2 hours during the first stage and at 750 °C for 4 hours during the second stage. SEM and X-ray diffraction tests were performed to evaluate the microstructural features and the major phases formed after surface treatment. SEM and X-ray diffraction tests were performed to assess the microstructural features and the primary phases formed after surface treatment. The new secondary precipitates were identified as γ′-Fe4N, ε (Fe2–3N), and α-Fe, exhibiting an uneven chain-like pattern wit

... Show More
View Publication
Scopus Crossref