The study of the bending property of the epoxy (Ep / MgO) and (Ep/SiO2) composites in natural conditions and after immersion in chemical solution

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material reinforced by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3, 6, 9 and 12) wt %. The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the reinforcement material (MgO, SiO2). The Bending of samples reinforced by SiO2 was found to be less than the bending of samples reinforced by particles (MgO). For example, the bending of the SiO2 sample (0.32 mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample at the weight ratio were the same weighted load (100 g). It was found that the bending values of all samples exceeded the value after immersion in sulfuric acid. For example, the percentage of weight (6%) at the load level (500 g) was changed from 1.16 mm in normal conditions to 1.48mm for the same weight ratio after immersion. In sulfuric acid diluted with 0.3N for 10 days at the same applied load.

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Apr 30 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Study Reinforcing and Applied Load of Wear Rate for Epoxy Composites

This research studies Reinforcing and applied load of  Wear Rate for Epoxy composites contains from epoxy resin (Ep) as a matrix material and reinforced by Gawain red wood flour , Russian white wood flour , glass powder and rock wool fibers , with volume fraction (20%) for all samples in lab conditions.  by using the load (10,20 ,30 ,40) Newton of iron disc for testing  time(10) minute, and the results have shown that the reinforcing of epoxy resin led to decrease  wear rate for all samples except the hybrid composites reinforced earth glass powder , that the wear rate values  decrease  from   (22×10-9g/cm) to (4×10-9g/cm) of composite material(Ep+R.W.F) and thus(Ep+W.W.F)   at la

... Show More
View Publication Preview PDF
Publication Date
Wed Jun 30 2010
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Effect of the Forming Conditions in the Production of Gamma Alumina Catalyst Support on the Crushing Strength Property

An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time
Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .
The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no inter

... Show More
View Publication Preview PDF
Publication Date
Mon Jul 01 2013
Journal Name
Journal Of Kerbala University
study the optimum conditions of synthesis AgNP by chemical reduction method

Abstract :- In this paper, silver nanoparticles had been prepared by chemical reduction method. Many tests had been done to it such as UV-Visible spectrophotometer, XRD, AFM&SEM test. finally an attempt had been done to get the optimum condition to control the grain size of silver Nanoparticles by variation the heating period and other parameters which has an effect in silver Nanoparticles synthesis process. in this method we can get a silver nanoparticles in the size range from 52 to 97 nm.

Preview PDF
Publication Date
Wed Dec 30 2009
Journal Name
Iraqi Journal Of Physics
The Effect of PVC Powder content on the Elastic Moduli and Acoustic Impedance of Epoxy Composites

The primary purpose of the present research was to study the effect of polyvinyl chloride (PVC) powder content on ultrasonic wave velocity in PVC/Epoxy composites. The second part is concerned with the relations of dynamic elastic moduli with the ultrasonic wave velocities, to determine how ultrasonic waves can affect them.
Experimental data have been obtained using the sonic viewer (model -5217 A) device to generate two types of waves, longitudinal waves of frequency 63 kHz and transverse waves of frequency 33 kHz and to measure the transit time required for those waves to travel through individual sample.
The experimental results have shown that the propagation of the ultrasonic velocity increases directly with PVC content in the

... Show More
View Publication Preview PDF
Publication Date
Sun Apr 08 2018
Journal Name
Al-khwarizmi Engineering Journal
Evaluation the Mechanical Properties of Kaolin Particulate Reinforced Epoxy Composites

Epoxy resin has many chemical features and mechanical properties, but it has a small elongation at break, low impact strength and crack propagation resistance, i.e. it exhibits a brittle behavior. In the current study, the influence of adding kaolin with variable particle size on the mechanical properties (flexural modulus E, toughness Gc, fracture toughness Kc, hardness HB, and Wear rate WR) of epoxy resin was evaluated. Composites of epoxy with varying concentrations (0, 10, 20, 30, 40 weights %) of kaolin were prepared by hand-out method. The composites showed improved (E, Gc, Kc, HB, and WR) properties with the addition of filler. Also, similar results were observed with the decrease in particle size. In addition, in this study, mult

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Sun Mar 01 2015
Journal Name
Baghdad Science Journal
Mechanical and Thermal Properties of Epoxy-Graphite Composites

This search study the effect of particle size of graphite on the mechanical and thermal properties of epoxy composites, where graphite adopted with particle sizes (45,53,75) ?m, respectively, and the percentages by weight (0,1,3,5,7,9)% for each size of this three particle sizes.Mechanical properties represented by the bending (three-point bending) and through which the conclusion is bending stress and modulus of elasticity, thermal properties were either through thermal conductivity tests.The results showed that the ratio(1%) is the maximum value of bending stress at the three particle size and the (45 ?m) is the maximum.Thermal conductivity result show is the maximum value at ratio (1%) of particle size(53 ?m)

View Publication Preview PDF
Crossref
Publication Date
Sat Mar 01 2008
Journal Name
Iraqi Journal Of Physics
The effect of Aluminum Oxide, Iron Oxide on the thermal conductivity of (Epoxy-Aluminum Oxide, Epoxy-Iron Oxide) Composites

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3

View Publication Preview PDF
Publication Date
Sun Dec 06 2015
Journal Name
Baghdad Science Journal
The Effect of Fillers on the Chemical, Mechanical and Dielectric Properties of Polyvinyl Chloride Composites

The compounding of polyvinyl chloride (PVC) with two types of fillers and some additives were studied for the manufacturing of acid resistant tile. Various concentrations of two types of fillers namely; calcium carbonate and recycled glass powder were used along with different additives generally categorized as plasticizers, stabilizers, and lubricants were mixed in the standard concentration unit parts per hundred resins (phr) with the PVC as base polymer. The effects of filler materials on acid resistant towered different acids like sulphuric, nitric and hydrochloric at different concentration were studied. Samples which passed the test were further checked for dielectric strength and mechanical properties. It was found that the recycl

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sun Dec 07 2014
Journal Name
Baghdad Science Journal
The effect of temperature and chemical solutions on the Compressive strength of particulate hybrid composites

In this work a hybrid composite materials were prepared containing matrix of polymer (polyethylene PE) reinforced by different reinforcing materials (Alumina powder + Carbon black powder CB + Silica powder). The hybrid composite materials prepared are: • H1 = PE + Al2O3 + CB • H2 = PE + CB + SiO2 • H3 = PE + Al2O3 + CB + SiO2 All samples related to electrical tests were prepared by injection molding process. Mechanical tests include compression with different temperatures and different chemical solutions at different immersion times The mechanical experimentations results were in favour of the samples (H3) with an obvious weakness of the samples (H1) and a decrease of these properties with a rise in temperature and the increasing

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Sep 10 2020
Journal Name
Journal Of Advances In Mathematics
A Study of The Density Property in Module Theory

In this paper, there are two main objectives. The first objective is to study the relationship between the density property and some modules in detail, for instance; semisimple and divisible modules. The Addition complement has a good relationship with the density property of the modules as this importance is highlighted by any submodule N of M has an addition complement with Rad(M)=0. The second objective is to clarify the relationship between the density property and the essential submodules with some examples. As an example of this relationship, we studied the torsion-free module and its relationship with the essential submodules in module M.