Polymers, being one of the most important materials in dentistry, offer great physical and mechanical qualities, as well as good biocompatibility. Aim of this study was done to evaluate the Polyetherketoneketone and Polyetherketoneketone polymer composite material used as dental implant through tensile strength, Fourier Transform Infrared analysis FTIR, and wettability). Polyetherketoneketone composites (Polyetherketoneketone and Strontium-containing hydroxyapatite) with selected weight percentage ratios of (0, 10%, 20%, 30%), were fabricated using a compression molding technique”, The study involved Samples preparation (sheets) shaped and form into the desired shape according to standard for tests which included tensile strength,

Electrochemical method was used to prepare carbon quantum dots (CQDs). Size of matter was nature when evaluate via X-ray diffraction (XRD). A distinct peak at 2θ equal to 31.6° and three other small peaks at 38.28°, 56.41° and 66.12° were observed. The measures of Fourier Transform Infrared Spectroscopy (FTIR) showed the bonds in the transmittance spectrum are manufactured with carbon nanostructures in view. The first peaks are the O–H stretching vibration bands at (3417 and 2922) cm−1, (C–O–H at 1400, and 1317) cm−1, (C–H), (C=C), (C–O–H), (C=O), and (C–O) bonds at 2850, 1668, 1101, and 1026 cm−1 sequentially. The transmission electron microscopy (TEM) results presented that the spherical CQDs are in shape and on a

In this study, aluminum nanoparticles (Al NPs) were prepared using explosive strips method in double-distilled deionized water (DDDW), where the effect of five different currents (25, 50, 75, 100 and 125 A) on particle size and distribution was studied. Also, the explosive strips method was used to decorate zinc oxide particles with Al particles, where Al particles were prepared in suspended from zinc oxide with DDDW. Transmission electron microscopy (TEM), UV-visible absorption spectroscopy, and x-ray diffraction are used to characterize the nanoparticles. XRD pattern were examined for three samples of aluminum particles and DDDW prepared with three current values (25, 75 and 125 A) and three samples prepared with the same currents for zin

Study was made on the optical properties of Ge2oSe8othinfilms prepared by vac-uum evaporation as radiated by (0,34,69) Gy of 13 ray.The optical band gab Eg and tailing band A.Et were studied in the photon energy range ( 1 to 3)eV. The a-Ge20Se8o film was found to be indirect gap with energy gap of (1.965,1.9 , 1.82) eV at radiated by B ray with absorption doses of (0,34,69)Gy respectively.The Ea and AEt of Ge20Se80 films showed adecrease in E8 and an increase in AEt with radiation. This be-havior may be related to structural defects and dangling bonds.

1 - is not affected by illiteracy cells painful eggs after the first and seventh of the various concentrations used but found the effect of 21 and 35 days after treatment2 - repeat chromosomal aberrations illiteracy eggs cells no different distortions occurring sperm cells During Altnavra phase3 - increased chromosomal aberrations increase the dose especially for 21 and 35 days4 - The connective tissue is more sensitive phase of the pesticide from Altnavra phase

In this research, salbutamol sulphate (SAS) has been determined by a simple, rapid and sensitive spectrophotometric method. Salbutamol sulphate in this method is based on the coupling of SAS with diazotized ρ- bromoaniline reagent in alkaline medium of Triton X-100 (Tx) to form an orange azo dye which is stable and water-soluble. The azo dye is exhibiting maximum absorption at 441 nm. A 10 - 800 µg of SAS is obeyed of Beer^'s law in a final volume of 20 ml, i.e., 0.5- 40 ppm with ε, the molar absorptivity of 48558 L.mol^-1.cm^-1 and Sandell's sensitivity index of 0.01188 µg.cm^-2. This new method does not need solvent extraction or temperature control which is well applied to determine SAS in d

ABSTRACT

Naproxen(NPX) imprinted liquid electrodes of polymers are built using polymerization precipitation. The molecularly imprinted (MIP) and non imprinted (NIP) polymers were synthesized using NPX as a template. In the polymerization precipitation involved, styrene(STY) was used as monomer, N,N-methylenediacrylamide (N,N-MDAM) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The molecularly imprinted membranes and the non-imprinted membranes were prepared using acetophenone(AOPH) and di octylphathalate(DOP)as plasticizers in PVC matrix. The slopes and detection limits of the liquid electrodes ranged from)-18.1,-17.72 (mV/decade and )4.0 x 10^-

Mn2+ and Ce3+ Doped ZnS nanocrystals were prepared by a simple microwave irradiation method under mild condition. The starting materials for the synthesis of Mn2+ and Ce3+ Doped ZnS P nanocrystals were zinc acetate as zinc source, thioacetamide as a sulfur source, manganese chloride and Cerium chloride as manganese and cerium sources respectively (R & M Chemical) and ethylene glycol as a solvent. All chemicals were analytical grade products and used without further purification. The nanocrystals of Mn2+ and Ce3+ Doped ZnS P with cubic structure were characterized by X-ray powder diffraction (XRD), the morphology of the film is seen by field effect scanning electron microscopy (FESEM). The composition of the samples is analyzed by EDS. The s

A series of liquid crystals comprising a heterocyclics dihydro pyrrole and 1,2,3-triazole rings [VII]-[X] were synthesized by many steps starting from a reaction of 3,3'-dimethyl-[1,1'-biphenyl]- 4,4'-diamine with chloroacetyl chloride in a mixture of solutions DMF and TEA to synthesise the compounds [I], then the compounds [I] reacted with malononitrile in 1,4-dioxane and TEA solutions to produce compounds [II], then the first step is repeated with compound [II] where it reacted with chloroacetyl chloride in mixture of DMF and TEA to give compound [III], this compound reacted with sodium azide in the presence of sodium chloride and DMF as solvent to produce the compound [IV], which reacted with acrylic acid by a 1.3 dipolar reaction in sol