In this work, silver (Ag) self-metallization on a polyimide (PI) film was prepared through autocatalytic plating. PI films were prepared through the solution casting method, followed by etching with potassium hydroxide (KOH) solution, sensitization with tin chloride (SnCl₂), and the use of palladium chloride (PdCl₂) to activate the surface of PI. Energy-dispersive X-ray analysis (EDX) showed the highest peak in the (Ag) region and confirmed the presence of AgNPs. The diffraction peaks at 2θ = 38.2^°, 44.5^°, 64.6^°, and 78.2^° represented the 111, 200, 220, and 311 planes of Ag, respectively. The FT–IR an

Catalase (EC 1.11.1.6) is a well known enzyme which exists in almost all living creatures exposing to oxygen (such as plants, bacteria, and animals). It is a very necessary enzyme to protect the cell from oxidative detriment by reactive oxygen species (ROS). The aim of this study is the partial purification and characterization of Catalase enzyme from Banana peels. In this study, fresh banana peels are treated with 70 % ethanol ,further separated with chloroform ,water and ethyl acetate respectively .The supernatant of the enzymatic sample which is treated with chloroform is loaded into gel filtration column with Sephadex G-100 (1.0 x 90 cm) equilibrated with pH7 buffer media (phosphate buffer 0.1 M). Kinetic studies of the purified en

Iraqi kaolin was used for the preparation and characterization of NaY zeolite for biodiesel production via esterification reaction. Oleic acid was used usually as a typical simulated feedstock of high acid number for the esterification reaction.

   The chemical composition for the prepared Nay zeolite is as following:  (Ca₂.6Na₁.K_0.1)(Al₆.3Si₁₇.₇)O₄₈.16H₂O, the silica to alumina ratio in the prepared catalyst was found equal to 2.6 and Na₂O content was 12.26 wt. %, with relative crystallinity equal to 147.4 % obtained by the X-ray diffraction. The surface area result shows that the prepared catalyst has 330 m²

Selexipag is an orally selective long-acting prostacyclin receptor agonist, which indicated for the treatment of pulmonary arterial hypertension. It is practically insoluble in water ( class II, according to BCS). This work aims to prepare and optimized Selexipag nanosuspensions to achieve an enhancement in the in vitro dissolution rate. The solvent antisolvent precipitation method was used for the production of nanosuspension, and the effect of formulation parameters (stabilizer type, drug: stabilizer ratio, and use of co-stabilizer) and process parameter (stirring speed) on the particle size and polydispersity index were studied. SLPNS prepared with Soluplus® as amain stabilizer (F15) showed the smallest particle size 47nm wi

This study was carried out to prepare and characterize domperidone nanoparticles to enhance solubility and the release rate. Domperidone is practically insoluble in water and has low and an erratic bioavailability range from 13%-17%. The domperidone nanoparticles were prepared by solvent/antisolvent precipitation method at different polymer:drug ratios of 1:1 and 2:1 using different polymers and grades of poly vinyl pyrolidone, hydroxy propyl methyl cellulose and sodium carboxymethyl cellulose as stabilizers. The effect of polymer type, ratio of polymer:drug, solvent:antisolvent ratio, stirring rate and stirring time on the particle size, were investigated and found to have a significant (p? 0.05) effect on particle size. The best formul

Aim To develop a low-density polyethylene–hydroxyapatite (HA-PE) composite with properties tailored to function as a potential root canal filling material. Methodology Hydroxyapatite and polyethylene mixed with strontium oxide as a radiopacifier were extruded from a single screw extruder fitted with an appropriate die to form fibres. The composition of the composite was optimized with clinical handling and placement in the canal being the prime consideration. The fibres were characterized using infrared spectroscopy (FTIR), and their thermal properties determined using differential scanning calorimetry (DSC). The tensile strength and elastic modulus of the composite fibres and gutta-percha were compared, dry and after 1 month storage in

The increasing requirement and use of dental implant treatments has rendered dental implantology indispensable in dentistry. The aim of this study is to determine the optimum concentration of calcium silicate to be incorporated into a polyetherketoneketone (PEKK) matrix used as an implant material to enhance the bioactivity and mechanical properties of the composite compared with unmodified PEKK. In this study, different weight percentage (wt%) of micro-calcium silicate (m-CS) is incorporated into PEKK with ethanol as a binder. Subsequently, the mixture is dried in a forced convection oven at 120°C and poured into customized molds to fabricate a bioactive composite via compression molding (310°C, 15 MPa, and 20 min holding time

Steps were taken to obtain the Kojic acid crystals from local fungal isolation A. flavus WJF81 by separating the fermentation products from the fungus mycelium from the production plant at the centrifuge at a speed of 5000 cycles for 10 minutes. The extraction was followed by ethyl acetate then supernatant concentrate by using rotary evaporator, and dried with heat oven 37ºC. Long, yellowish, pristine acid crystals were obtained that examined the optical microscope with a magnification force of 10x and 40x. The melting point of kojic acid was determined between 152.9-153.5 °C Results of the diagnosis of Kojic acid by applying High pressure liquid chromatography HPLC technique showed that the acid was at one peak, which was close to the

يهدف البحث الحالي إلى معرفة اثر التدريس بطريقة التنقيب الحواري في حفظ النصوص الأدبية لدى طلبة قسم اللغة الكردية، اختارت الباحثة طلبة المرحلة الثانية في قسم اللغة الكردية بكلية التربية ابن رشد، للعام الدراسي
(2008-2009) ميدان لتطبيق تجربتها.
تألفت عينة الدراسة من (48) طالبا وطالبة، تم توزيعها عشوائيا إلى مجموعتين، مجموعة ضابطة (درست بالطريقة الاعتيادية) تألفت من (23) طالبا وطالبة ومجموعة تجريبية (درست بطريقة الت