In this study, polymeric coating was developed by incorporating nano graphene in the polymer blend with applications to oil storage tanks. The oil storage tanks samples were brought from the oil Pipeline Company / Doura refinery in Baghdad. The coating polymer was formed with a blend (epoxy resin and repcoat ZR). The proportion of mixing the mixture was 3:1:1 epoxy resin 21.06 gm: repcoat ZR 10.53 gm: hardener 10.53 gm. The blend/graphene was prepared using in stui-polymerization method with different weight percentage 1, 3, 5, and 7 wt % added to blend. The resulting solution was put in a glass tube on a magnetic stirrer for one hour at a temperature of 40 °C. The result of contact angle and water absorption the best ratio of 3wt

Permanent magnets of different intensities were used to investigate the effect of a magnetic field in the process of preventing deposits of calcium carbonate. The magnets were fixed on the water line from the tap outside. Then heating a sample of this water in flasks and measuring the amount of sediment in a manner weighted differences. These experiments comprise to the change of the velocity of water flow, which amounted to (0.5, 0.75, 1) m/sec through the magnetic fields that are of magnetic strength (2200, 6000, 9250, 11000) Gauss, and conduct measurements, tests and compare them with those obtained from the use of ordinary water.The results showed the effectiveness of magnetic treatment in reducing the rate of deposition of calcium carb

The present study was conducted to evaluate the effect of variation of influent raw water turbidity, bed composition, and filtration rate on the performance of mono (sand) and dual media (sand and anthracite) rapid gravity filters in response to the effluent filtered water turbidity and headloss development. In order to evaluate each filter pe1formance, sieve analysis was made to characterize both media and to determine the effective size and uniformity coefficient. Effluent filtered water turbidity and the headloss development was recorded with time during each experiment.

The problem of water scarcity is becoming common in many parts of the world, to overcome part of this problem proper management of water and an efficient irrigation system are needed.  Irrigation with a buried vertical ceramic pipe is known as a very effective in the management of irrigation water.  The two- dimensional transient flow of water from a buried vertical ceramic pipe through homogenous porous media is simulated numerically using the HYDRUS/2D software.  Different values of pipe lengths and hydraulic conductivity were selected.  In addition, different values of initial volumetric soil water content were assumed in this simulation as initial conditions.  Different value

I attended some amides non grassy substitutes such as acrylic compounds Amaid Electron Amaid and Alsinamamaid interaction unsaturated acids such as acrylic acid or Ketronk ????????? with primary amines Malkhtlfah of acrylic monomers Alamayd

Phenoxathiin was prepared by the reaction of diphenyl ether with sulfur in the presence of anhydrous aluminum chloride. This work comprised the synthesis of new phenoxathiin derivatives containing heterocyclic moieties. These heterocyclic compounds were synthesized in three groups. The first group was made up of 2-(oxoalken-1-yl) phenoxathiin derivatives (3a-3j) obtained from the reaction of 2-acetylphenoxathiin with different aromatic aldehyde in the presence of sodium hydroxide. The other two groups involved compounds produced from the reaction of (3a-3j) with hydrazine hydrate in acetic acid to get 2-(1-acetyl pyrazolin-3-yl) phenoxathiin derivatives (4a-4j), and phenyl hydrazine in the presence of piperidine to afford 2-(1-phenyl pyrazo

The MTX was converted to MTX nanoparticles by the modified method based on changing the pH gradually with exposure to ultrasound and shaking , changing the pH with exposure to ultrasound plays an significant role in the formation of nanoparticles, and this is shown in some previous studies. As the change in pH affects the nature of bonding between molecules, as well as the strength of bonding that depends on the change of electrical charges The exposure to ultrasound waves will greatly affect the breakdown of large particles into small particles that reach the level of nanoparticles. The MTX NPs formation was characterized by UV-Vis spectra analysis , Atomic force microscopy (AFM) analysis, Scanning electron microscope (SEM) and Fou

Well dispersed Cu2FeSnSe4 (CFTSe) nanofilms were synthesized by hot-injection method. The structural and morphological measurements were characterized using XRD (X-ray diffraction), Raman spectroscopy, SEM (scanning electron microscopy), and TEM (transmission electron microscopy). Chemical composition and optical properties of as-synthesized CFTSe nanoparticles were characterized using EDS (energy dispersive spectroscopy) and UV-Vis spectrophotometry. The average particle size of the nanoparticles was about 7-10 nm. The UV-Vis absorption spectra showed that the synthesized CFTS nanofilms have a band gap (Eg) of about 1.16 eV. Photo-electrochemical characteristics of CFTSe nanoparticles were studied and indicated their potential application