Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), and surface roughness tester. Following these tests, resin cement application to titanium discs was performed. Shear bond strength (SBS) values were determined by universal testing machine. ANOVA and Tukey HSD tests were used for analyzing of data (α = 0.05).Results: Higher average surface roughness (Ra) value was observed in (10 W) group followed by (20 W) group and the lowest surface roughness value was in the control group, additionally lowest SBS value was obtained from the control group and the highest SBS value was obtained from (20 W) group followed by (10 W) group. Conclusion: bond strength between titanium and resin cement can be significantly enhanced by using fiber laser as a surface treatment. Average power of fiber laser is essential parameter in enhancing the roughness of titanium surface and bonding to resin cement.
Background: The purpose of this study was to compare regional bond strength at middle and cervical thirds of the root canal among glass fiber-reinforced composite (FRC) endodontic posts cemented with different cements, using the push-out test to compare the performance (retention) of two types of luting cements; polycarboxylate cement and Zinc phosphate cement used to cement translucent fiber post and to compare the result of the push-out test at different storage times;1 week ,1month and 2 months. Materials and methods: Ninety caries-free, recently extracted single-rooted human teeth with straight root canals was used in this study, The root canals were endodontically instrumented at a working length of 0.5 mm from the apex by m
... Show Morethis research seeks to shed light on the study of the impact of Putinism on the Russian-Ukrainian war that broke out in early 2022, by studying the contents of the speeches of Russian President Vladimir Putin before the start of the war. This research uses the structural approach in analyzing the components of the Russian political regime. The research tools used in this research include case studies, content analysis of Russian speeches, and personal meetings of researchers and specialists in Russian affairs. It sums up a number of important conclusions, most notably are : 1) Putinism is a totalitarian regime that includes the political doctrine during the era of Russian President Vladimir Putin. 2) Duginism represents the totality of t
... Show More
اجري البحث لد ا را رسة تأثير اضافة مستويات مختمفة من مسحوق الشبنت المجفف الى علالائق اف ا را رخ فروج المحم في بعض صفات مصل بعمر يوم واحد بمعدل وزن 46 غم / فرخ ، وزعت الطيور عشوائياًً عمى 4 معاملالات Ross الدم. استخدم 336 فرخ من سلالالة 308 T و 4 T3 ،، T معاممة السيطرة )خالية من اي اضافة(، 2 T بواقع ثلالاث مكرا را رت لكل معاممة )طير/مكرر(،شممت المعاملالات عمى :- 1 0 % عمى التوالي. استمرت التجربة لمدة 5 اسابيع. قدر في نهايتها ت ا را ركي
... Show MoreThis research aims to identify the relationship between occupational hypocrisy and organizational strategic success, It was done by analyzing the correlations and influence between variables, applied to a random sample of university professors at the University of Kufa faculty of administration and economic.
The main tool for data collection is the survey were questionnaires were distributed randomly to the professors , and (43) questionnaires were returned, and test its validity by using (SEM) (Structural Equation Modeling), Hypothesis has been tested by using Statistical Package for Social Sciences (SPSS v. 18), The research found a set of conclusions:(The occupational hypocrisy has
... Show MoreElectrochemical Machining is a term given to one of nontraditional machining that uses a chemical reaction associated with electric current to remove the material. The process is depending on the principle of anodic dissolution theory for evaluating material removal during electrochemical process. In this study, the electrochemical machining was used to remove 1 mm from the length of the a workpiece (stainless steel 316 H) by immersing it in to electrolyte (10, 20 and 30 g) of NaCl and Na2SO4 to every (1 litter of filtered water). The tool used was made from copper. Gap size between the workpiece and electrode is (0.5) mm. This study focuses on the effect of the changing the type and concentration of electroly
... Show MoreIn this work, varying compositions of SiO2 micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO2/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.
Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups
... Show MoreThe study was conducted to identify the toxicity of chromium on scenedesmus quadricauda algae alone and in the presence of nutrient metal (Nitrogen). Different concentrations of chromium (0.5, 1.5 , 2.5, 3.5 , 4.5mg/L) were used and the presence nitrogen is (5 ,10 ,50 ,100mg/L) on cultur media(chu-10) with used for cultivation of the algae in controlled conditions(25oC , light intensity 380 –?E/m2 /s. The results showed increasing in the toxicity of the metal when is alone , excess of concentrations an time of exposure. The growth rate decreased from 0.44 to 0.06 cell/ hour after 12 day of the biging of the experiment and of concentrate 4.5 mg/L of chromium. The intermediate active concentrations of the chromium(EC50) was increase
... Show More
The current study was conducted to determine the sensitivity of some pathogenic bacterial isolates isolated from wounds and burns water toward the disposer of the Yas Rue tested five crude bacterial isolates isolated from wounds and burns which these isolates sensitive to aqueous extract crude
Background: Elastomeric chains are one of the most commonly used force delivery systems. They have the ability to exert a continuous force, convenience of use, compatibility to oral environment and cost effectiveness but one of the inherited disadvantages is force degradation. Materials and methods: This in vitro study was designed to evaluate the effect of alcohol presence in mouthwashes on force decay of different configurations of clear elastomeric chains from (Ortho Technology company) which are: closed , short and long under the effect of time at (Initial, 1, 2, 3 and 4 weeks) intervals with exposure to different chemical solutions. A total (540) modules of elastomeric chains of three different types (long, short and closed) trans