In this research, deposition of titanium oxide (TiO₂) and vanadium oxide (V₂O₅) thin film  in different mixing percentage  (0, 25 ,50, 75 and100)%   on the substrate of glass .The coating thickness was ( 50 nm  ).

In this research contact angle was measured and the effect of weather conditions. Results showed that the value of the contact angle of the prepared films reached its highest value at 50% (TiO₂+V₂O₅) was 160º.

The results showed that the optical transmittance of TiO₂ and V₂O₅ thin film decrease with increasing the deposition angle and decrease with increasing V₂O₅ pro

The new, standard molecular biologic system for duplicating DNA enzymatically devoid of employing a living organism, like E. coli or yeast, represents polymerases chain reaction (PCR). This technology allows an exponential intensification of a minor quantity of DNA molecule several times. Analysis can be straightforward with more DNA available. A thermal heat cycler performs a polymerization chain reaction that involves repeated cycles of heating and cooling the reactant tubes at the desired temperature for each reaction step. A heated deck is positioned on the upper reaction tube to avoid evaporating the reaction mixture (normally volumes range from 15 to 100 l per tube), or an oil layer can be placed on a reaction mixture su

Linear attenuation coefficient of polymer composite for beta particles and bremsstrahlung ray were investigated as a function of the absorber thickness and energy. The attenuation coefficient were obtained using NaI(Tl) energy selective scintillation counter with ⁹⁰Sr/⁹⁰Y beta source having an energy range from 0.1-1.1 MeV. The present results show the capability of this composite to absorber beta particles and bremsstrahlung ray that yield from it. That’s mean it is useful to choice this composite for radiation shielding of beta ray with low thickness.

ABSTRACT

Naproxen(NPX) imprinted liquid electrodes of polymers are built using polymerization precipitation. The molecularly imprinted (MIP) and non imprinted (NIP) polymers were synthesized using NPX as a template. In the polymerization precipitation involved, styrene(STY) was used as monomer, N,N-methylenediacrylamide (N,N-MDAM) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The molecularly imprinted membranes and the non-imprinted membranes were prepared using acetophenone(AOPH) and di octylphathalate(DOP)as plasticizers in PVC matrix. The slopes and detection limits of the liquid electrodes ranged from)-18.1,-17.72 (mV/decade and )4.0 x 10^-

Polymers have the ability to extract water after they have been added to the mortar or concrete mixture. They provide the absorbed water during hydration functioning as internal water source. Absorption polymers can absorb up to hundred times of their own weight of pure water.This research deals with the use of water absorption polymer balls in concrete and study the volumetric change of these mixes and compared the results with reference mix (without polymers). Samples were cured both in air and in water for the mixes to compare results which show that samples in air behave for expansion while sample in water acted for shrinkage.

Gypseous soils represented one of the most complex salty soils that faced the geotechnical engineers. Structures that built on gypsum soil will undergo unexpected distortions that will eventually contribute to catastrophic failure. The purpose of this article is to understand the durability of gypsum soil against wetting drying cycles after improvement with polyurethane polymer especially investigate the effect of the wetting-drying cycle on collapsibility. The soil was brought from Sawa lake in AL-Muthanna Governorate in Iraq, with gypsum content 65.5%,  A set of Odometer tests were performed to determine the collapsibility potential (CP) for treated and untreated gypsum soil.  The result shows that adding a different per

Objective: This study aimed to evaluate the effect of coating titanium (Ti) dental implant with polyether ketone ketone (PEKK) polymer using magnetron sputtering on osseointegration, trying to overcome some of the problems associated with Ti alloys. Material and Methods: Implants were prepared from grade (II) commercially pure titanium (CP Ti), then laser was used to induce roughness on the surface of Ti. PEKK was deposited on the surface of Ti implants by radiofrequency (RF) magnetron sputtering technique. The implants were divided in to three groups: without coating (Ls), with PEKK coating using argon (Ar) as sputtering gas (Ls-PEKK-Ar), and with PEKK coating using nitrogen (N) as sputtering gas (Ls-PEKK-N). All the implants were implante