The aim of this study is to investigate the ability of malachite green (MG) combined with 650nm diode laser to kill Candida albicans and to spectrally study the MG photodegradation after photodynamic therapy (PDT) spectrally. Cultures of Candida albicans were exposed to 40mW, 650 nm diode laser in the absence of MG. In PDT group, the MG was added to the Candida suspension for 5 min then exposed to diode laser for (5, 10, 15, 20) min at power density of 0.59W/cm2. The absorption spectrum of the photosensitized fungal suspension was obtained. The data were submitted to T-test (p<0.05). A 650nm diode laser in the presence of MG reduced the number of CFU/ml in 98.4%. Laser with 650nm alone and MG alone did not reduce significantly the number of CFU/ml of Candida albicans. Absorption spectrum showed that MG is photodegraded after irradiation .In conclusions, diode laser with 650nm was effective tool to photoinactivate Candida albicans in the presence of MG and that the dye is photodegraded following irradiation.
Improvement of optoelectrical characteristics of phosphorus diffused silicon photodiodes by Q-switched Nd:YAG laser pulses was investigated. Laser pulses have dissolved the precipitation of phosphorus resulted during thermal diffusion process. The experimental data show that responsivity higher than (0.32 A/W) at 850 nm can be achieved after laser annealing with (1.5 MW/cm2) for 6 shots.
Polyaniline films were successfully synthesized in this study using an oxidative polymerization method at temperatures ranging from 0 to 4 ° C. Polyaniline films were deposited using a single step of chemical oxidative polymerization rather than electrochemical polymerization. The polyaniline was examined using FTIR, XRD, SEM, AFM, and Four Point Probe. This result demonstrates that polyaniline synthesized using this method has a uniform morphology, small size (17 to 40) nm, high crystallinity, and high conductivity (9.42 s/cm).
(5)
(1)
Periodontal diseases are inflammatory diseases, for which, scaling and root planning is the main approach. Diode laser therapy as an adjunct to non-surgical periodontal treatment has shown some beneficial effects.
Aim: The objective of this single randomized controlled clinical study was to assess the effect of a 940 nm diode laser as an adjunct to SRP therapy in the treatment of periodontal pockets.
Methods: In this study, twenty patients in need of periodontal treatment with periodontal pocket ≥ 4 mm were selected for this split-mouth clinical study. Test group treated by diode laser 940 nm as an adjunct with SRP, control group treated by SRP in contralateral quadrants. Clinical
... Show MorePulsed liquid laser ablation is considered a green method for the synthesis of nanostructures because there are no byproducts formed after the ablation. In this paper, a fiber laser of wavelength 1.064 µm, peak power of 1 mJ, pulse duration of 120 ns, and repetition rate of 20 kHz, was used to produce carbon nanostructures including carbon nanospheres and carbon nanorods from the ablation of asphalt in ethanol at ablation speeds of (100, 75, 50, 10 mm/s). The morphology, composition and optical properties of the synthesized samples were studied experimentally using FESEM, HRTEM, EDS, and UV-vis spectrophotometer. Results showed that the band gap energy decreased with decreasing the ablation speed (increasing the ablation time), the mi
... Show More
(3)
(1)
In this paper, two types of iron oxide nanomaterial (Fe3O4) and nanocomposite (T-Fe3O4) were created from the bio-waste mass of tangerine peel. These two materials were utilized for adsorption tests to remove cefixime (CFX) from an aqueous solution. Before the adsorption application, both adsorbents have been characterized by various characterizations such as XRD, FTIR, VSM, TEM, and FESEM. The mesoporous nano-crystalline structure of Fe3O4 and T-Fe3O4 nanocomposite with less than 100-nm diameter is confirmed. The adsorption of the obtained adsorbents was evaluated for CFX removal by adjusting several operation parameters to optimize the removal. The optimal conditions for CFX removal were found to be an initial concentration of 40 and 50 m
... Show More
(17)
اتجهت دول العالم الى تسخير جميع الإمكانيات والخبرات والعلوم من اجل الوصول الى مستويات متقدمة في الرياضات المختلفة ويهدف التدريب الرياضي إلى إعداد اللاعبين إعدادا جيدا تكمن مشكلة البحث من خلال خبرة الباحثتان الميدانية ومتابعة تدريبات لاعبي المدرسة التخصصية كرة اليد فقد لوحظ هناك ضعف واضح في الأداء المهاري ولابد من تطوير أوجه الضعف لتحقيق مستوى انجاز افضل . ويهدف البحث اعداد تمرينات خاصة بأستخدام جهاز ا
... Show More
(1)
(1)
(1)
This work demonstrated a simple and environmentally friendly method for synthesizing silica-supported copper nanocubes (CuNCs/SiO2). The copper nanocubes, with a size of 15 ± 5 nm, were synthesized using green reagents and conditions. Ascorbic acid, water, and di-n-butyl sulfide were employed as reducing agent, solvent, and stabilizing ligand, respectively. The designed nanoscale catalyst was utilized for the esterification of acetic acid to methyl acetate at room temperature. The catalyst exhibited high efficiency, converting 80% of the reactant to the desired product (methyl acetate) after 24 hours of reaction at room temperature. The size and shape of copper nanocubes were characterized by transmission electron microsco
... Show More
(1)
(2)
(1)