Using three-point bending experiments,  the effect of the particle size of SiO₂ on the flexural properties of epoxy composites was investigated. Young modulus and flexural strength were studied for different weight percentage of filler  (2,4,6,8 and 10) wt%.The size of SiO₂ particles varied from micro (100um) to nano (12nm) .

Flexural strength and  Young modul were found to increase with the filler content, but when the particle size decreased to the nanoscale, the  Young module  increased. Flexural strength was higher for microcomposites than nanocomposites.

In this paper, we have derived Bayesian estimation for the parameters and reliability function of Perks distribution based on two different loss functions, Lindley’s approximation has been used to obtain those values. It is assumed that the parameter behaves as a random variable have a Gumbell Type P prior with non-informative is used. And after the derivation of mathematical formulas of those estimations, the simulation method was used for comparison depending on mean square error (MSE) values and integrated mean absolute percentage error (IMAPE) values respectively. Among of conclusion that have been reached, it is observed that, the LE-NR estimate introduced the best perform for estimating the parameter λ.

Spectral and linear optical properties for a mixture of Rhodamine B (RB) and Fluorescein Sodium (Na Fl) organic laser dyes were determined at different concentrations 10-3, 10-4 M in ethanol solvent at room temperature. The intensity of absorption range is towards longer wavelengths (red shift). The quantum efficiency diminished while the radiative and fluorescence life time increased when increment concentration, organic laser dyes have a spectrum within the range 540-500 nm. Results demonstrate that a mixture of laser dyes are effective optical materials when contrasted with individual laser dyes. It can be utilized as resonator in cavity lasers.

Vibrio cholerae enterotoxin was extracted by cooling centrifugation and filtration
with milipore filter (0.22um) and was purified by using Sephacryl –S- 6 gel
filtration,the content of protein was estimated . The results showed protein
concentration was 28.5 microgram/ml,the present of enterotoxin was detected by
infant suckling mouse method.
.The cytopathic effect of enterotoxin was studied by injecting a number of mice with
purified enterotoxin, It was found caused shortening the villi of the intestine at
concentration 55 and 45 ug /ml of purified enterotoxin, while the effect on liver
showed degenerative change with necrosis at 55 ug/ml of enterotoxin and caused
necrosis and infiltration of inflammatory ce

Adsorption capacity of a waste biomass, date stones, for phenolic compounds such as phenol (Ph) and p-nitro phenol (PNPh) was investigated. The characteristics of such waste biomass were determined and found to have a surface area and iodine number of 495.71 m²/g and 475.88 mg/g, respectively. The effects of temperature, initial sorbate concentration, and contact time on the adsorption process were studied. Experimental equilibrium data for adsorption of Ph and PNPh on date stones were analyzed by the Langmuir, Freundlich and Sips isotherm models. The results show that the best fit was achieved with the Sips isotherm equation with maximum adsorption capacities of 147.09 and 179.62 mg/g for Ph and PNPh, respectively. The kinetic data wer

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

   Linde Type-A (LTA) zeolite was modified by adding  lead sulfide into cavities of zeolite. The zeolite and zeolite –pbs  were characterized by FTIR, XRD, AFM and SEM. The adsorption of congo red (CR)  dye  from aqueous solution by zeolite and zeolite – pbs were studied. Different parameters like contact time, temperature and concentration of (CR) dye were investigated. The results show that at contact time of 45, 30 min for maximum adsorption of (CR) dye onto zeolite and zeolite -pbs respectively were observed. The kinetic data was analyzed using pseudo-first-order and pseudo-second-order kinetic models. The adsorption kinetics of (CR) dye  were fitted well with the pseudo-second-order k

    Synthesis of 2-mercaptobenzothiazole (A₁) is performed from the reaction of  o-aminothiophenol and carbon disulfide CS₂ in ethanol under basic condition. Compound (A₁)  is reacted with chloro acetyl chloride to give compound (A₂). Hydrazide acid compound (A₃) is obtained from the reaction of compound (A₂) with  hydrazine hydrate in ethanol under reflux in the presence of glacial acetic acid .The reaction of hydrazide acid compound (A₃) with ethyl acetoacetate gives pyrazole compound (A₄). The new hydrazone  compound (A₅) was prepared from the reaction of compound (A₃) with  benzaldehyde. Reaction of compound

The cost-effective removal of heavy metal ions represents a significant challenge in environmental science. In this study, we developed a straightforward and efficient reusable adsorbent by amalgamating chitosan and vermiculite (forming the CSVT composite), and comprehensively investigated its selective adsorption mechanism. Different techniques, such as Fourier-transform infrared spectroscopy (FTIR), zeta potential analysis, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Brunauer, Emmett, Teller (BET) analysis were employed for this purpose. The prepared CSVT composite exhibited a larger surface area and higher mesoporosity increasing from 1.9 to 17.24 m2/g compared to pristine chitosan. The adsorption capabilities of the