Corncob is an agricultural biomass waste that was widely investigated as an adsorbent of contaminants after transforming it into activated carbon. In this research carbonization and chemical activation processes were achieved to synthesize corncob-activated carbon (CAC). Many pretreatment steps including crushing, grinding, and drying to obtain corncob powder were performed before the carbonization step. The carbonization of corncob powder has occurred in the absence of air at a temperature of 500 °C. The chemical activation was accomplished by using HCl as an acidic activation agent. Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), X-ray diffraction (XRD), and Brunauer–Emmett–Teller (BET) facilitate

This work investigates the effect of the gas nitriding process on the surface layer microstructure and mechanical properties for steel 37, tool steel X155CrVMo12-1 and stainless steel 316L. Nitriding was conducted at a temperature of 550 °C for 2 hours during the first stage and at 750 °C for 4 hours during the second stage. SEM and X-ray diffraction tests were performed to evaluate the microstructural features and the major phases formed after surface treatment. SEM and X-ray diffraction tests were performed to assess the microstructural features and the primary phases formed after surface treatment. The new secondary precipitates were identified as γ′-Fe4N, ε (Fe2–3N), and α-Fe, exhibiting an uneven chain-like pattern wit

Background: Generally, genetic disorders are a leading cause of spontaneous abortion, neonatal death, increased morbidity and mortality in children and adults as well. They a significant health care and psychosocial burden for the patient, the family, the healthcare system and the community as a whole. Chromosomal abnormalities occur much more frequently than is generally appreciated. It is estimated that approximately 1 of 200 newborn infants had some form of chromosomal abnormality. The figure is much higher in fetuses that do not survive to term. It is estimated that in 50% of first trimester abortions, the fetus has a chromosomal abnormality. Aim of the study: This study aims to shed some light on the results of chromosomal studies per

From different hospitals in Baghdad city, 25 clinical isolates of Proteus spp. were collected from different clinical samples, all isolates were identified as Proteus mirabilis by using bacteriological and biochemical assays in addition to Vitek-2 identification system. 15 (60%) isolates were identifying as Proteus mirabilis. The susceptibility of P. mirabilis isolates towards cefotaxime and ceftazidime was (66.6 %), (20%) consecutively; while extended spectrum β-lactamases producing P. mirabilis percentage was (30.7 %). Because blaVEB-1 was documented as an important indicator for increasing risk of extended spectrum beta ßlactamases producing P. mirabilis isolates that began to spread from many geographic area to Far east which inc

The red palm weevil Rhynchophorus ferrugineus (Olivier, 1790), which belongs to the family Curculionidae, order Coleoptera, is one of the most important palm pests, which leads to heavy losses in date palms. In the last few years, it has been recorded in Iraq, from Safwan city south of Iraq, where it was detected on date palm trees (Phoenix dactylifera L, Arecales: Arecaceae). In the current study, specimens of adult weevils were collected from infested date palms (Phoenix dactylifera), that showed signs of infection in Safwan district, south of Basra province. The results of the investigation showed the presence of phoretic mites associated with the red palm weevil Rhynchophorus ferrugineus (Olivier,

Bacteriocins were partially purified by ammonium sulphate 50% concentraction, bacteriocin activity of Pediococcus acidilactici-FMAC278 was 25600 U/ml with 5.8 folds and 7.6% yeild, the activity decrease to 12800 U/ml after dialysis with 6.3 folds and 3% yield, On the other hand the bacteriocin activity of Weissella paramesenteroides-DFR6 was 12800 U/ml with 2.7 folds and 8.8% yeild, after dialysis the activity became 6400 U/ml with 5.1 fold and 3.4% yield, Chicken Sausage were made by adding 0.25, 0.5 and 1% particaly purified bacteriocin to study its effect on microorganisms and increasing shelf life of Sausage. It is found that bacterial numbers were decreased after 3 days of storage at refrigerator at 0.5% conc. While the molds decrea

      Protease enzyme production was studied and optimized as  a first step to collect information about solid state fermenter) to produce protease enzyme. A local isolated Aspergillus niger was used for this study with constant spores feeding in every experiment at (10⁵/g). Experiments carried out in conical flasks with (250 ml) containing (10 g) of wheat straw as a substrate with different conditions included temperature, pH, hydration ratio, and fermentation time, the results comprised by measuring protease activity (u). The results showed that the best activity can be obtained at (T = 32°C, t= 100 hrs, pH= 2.5 and hydration ratio is 1:3). On the other hand the results is courage to p

The current research was conducted to report the synthesis of alumina powder from Iraqi kaolin. The kaolin was transformed to metakaolin by calcinations at temperature 800 °C for three hours. Then the calcined kaolin was treated with (1.5 M) from H2SO4 for 6 hours to form Al2(SO4)3.12H2O solution. The precipitate was dried at 80oC for 10 hours and calcinations at different temperatures for two hours. The samples which result was characterized by X–Ray diffraction (XRD) and X–Ray fluorescence (XRF). The results indicate to the crystalline hydrate aluminum sulfate for the sample that be as – synthesis and when calcinations at 600 oC transformed into aluminum sulfate phase. The phases of alumina which we obtain consisted of a gamma a

The artificial silk (Rayon) was produced from the fronds of date palms which was taken from date palm trees (type Al-Zahdi) from the Iraqi gardens. Two main parts of the frond, namely leaves and stalks were used in this study to produce rayon. The palm fronds were converted into a powder of 90-180 micrometers. Major steps were used to produce rayon; delignification, bleaching and finally dissolution. Modified organosolv method which uses organic solvent method was applied to remove high lignin content. Three variables were studied in the delignification process: temperature, the ratio of ethanol to water and digestion time. The results showed that the best percent of lignin removal was (97%) which occured at; digestion time (80 minutes), te