In this research TiO2 nano-powder was prepared by a spray pyrolysis technique and then adds to the TiO2 powder with particle size (0.523 μm) in ratio (0, 5, 10, 15 at %) atomic percentage, and then deposition of the mixture on the stainless steel 316 L substrate in order to use in medical and industrial applications.
Structure properties including x-ray diffraction (XRD) and scanning electron microscope (SEM0, also some of mechanical properties and the effect of thermal annealing in different temperature have been studied. The results show that the particle size of a prepared nano-powder was 50 up to 75 nm from SEM, and the crystal structure of the powders (original and nano powder) was rutile with tetragonal cell. An improvement in

Two new ligands Na2[ H3B (BDIA)].0.05H2O (L1)(BDIA = 1-Boranyl-2,3-
Dihydro-1H-Indol-3-yl)]Acetic Acid and Na3[H2B(BDIA)2].0.3H2O.0.3CH3Ph (L2)
were synthesized by reaction of NaBH4 with indole -3- acetic acid (IAA) . The
coordination properties of ligands were studied with Co(II) , Ni(II) , Cu(II) and
Pt(IV) ions. Characterization and structural aspects of the prepared compounds were
elucidated by 1HNMR, FTIR electronic spectra, magnetic susceptibility, elemental
and metal analysis, thermal analysis (TG & DTG) and conductivity measurements.
The obtained data for metal complexes suggested square planar geometry for
copper complexes, octahedral geometry for nickel and platinium complexes and
tetrahedral geom

Synthesis of new ligand, namely [bis(2-(2-methyl-5-nitro-1H-imidazol-1-yl)ethyl) hydrogen borate] (BIB), utilizing the reaction of metronidazole with boric acid in mole ratio (2:1), as well as the metal complexes with [Ni(II) and Cu(II)], were synthesized. All synthesized compounds were characterized by utilizing spectroscopic techniques such as FTIR, 1H-NMR, thermal analysis (T.G., UV-Vis), and atomic absorption (A.A.S.), as well as micro elemental analysis (C.H.N.), melting point (m.p), magnetic susceptibility, molar conductivity, and chloride content measurements. All complexes were paramagnetic, and the electrolyte and the suggested geometries were tetrahedral for nickel and octahedral for copper. In addition, all the transition meta

In this study a polymeric composite material was prepared by hand
lay-up technique from epoxy resin as a matrix and magnesium oxide
(MgO) as a reinforcement with different weight fraction (5,10,15,
and 20)% to resin. Then the prepared samples were immersed under
normal condition in H₂So₄(1 M) solution, for periods ranging up to
10 weeks. The result revealed that the diffusion coefficient
decreasing as the concentration of MgO increase. Also we studied
Hardness for the prepared samples before and after immersion. The
result revealed that the hardness values increase as the concentration
of MgO increase, while the hardness for the samples after immersion
in H₂SO₄ dec

Abstract: Microfluidic devices present unique advantages for the development of efficient drug assay and screening. The microfluidic platforms might offer a more rapid and cost-effective alternative. Fluids are confined in devices that have a significant dimension on the micrometer scale. Due to this extreme confinement, the volumes used for drug assays are tiny (milliliters to femtoliters).

 In this research, a microfluidic chip consists of micro-channels carved on substrate materials built by using Acrylic (Polymethyl Methacrylate, PMMA) chip was designed using a Carbon Dioxide (CO₂) laser machine. The CO2 parameters have influence on the width, depth, roughness of the chip. In order to have regular

Nanoparticles (NPs) based techniques have shown great promises in all fields of science and industry. Nanofluid-flooding, as a replacement for water-flooding, has been suggested as an applicable application for enhanced oil recovery (EOR). The subsequent presence of these NPs and its potential aggregations in the porous media; however, can dramatically intensify the complexity of subsequent CO2 storage projects in the depleted hydrocarbon reservoir. Typically, CO2 from major emitters is injected into the low-productivity oil reservoir for storage and incremental oil recovery, as the last EOR stage. In this work, An extensive serious of experiments have been conducted using a high-pressure temperature vessel to apply a wide range of CO2-pres

GFRP was employed in constructions as an alternative to steel, which has many advantages like lightweight, large tensile strength and resist corrosion. Existing researches are insufficient in studying the influence of hybrid reinforced concrete composite columns encased by GFRP I-section (RCCCEG) and I-section steel (RCCCES). In this study twenty one (RC) specimens of a cross-section of 130 mm × 160 mm, with different length (long 1600 mm and short 750 mm) were encased by using I-section (steel and GFRP) and tested under various loading (concentric, eccentric and flexural loads). The test was focused on the influence of many parameters; load-carrying capacity, mode of failure, deformation and drawing an interaction diagram (N-

The complexation between folic acid and a typical polyaromatic hydrocarbon, fluorene, was investigated using FTIR and UV spectra. Appearance of a new IR band at 2401cm−1 demonstrates that NH2–C=N moiety on pterin ring in folic acid is protonated when fluorene is introduced. The emergence of two charge transfer bands at 217 nm and 278 nm in UV difference spectra shows the presence of π-π complexation between folic acid and fluorene. These experiments confirm that fluorene could combine with the pterin ring of folic acid through π-π donor–acceptor interaction and induce the protonation process in folic acid upon strengthening electron accepting ability of pterin ring. The results suggest that complexatio

The focus of this research revolves around the importance level of sialic acid in the reasoning of cases, including tumors and then evaluate the patient's response to treatment and its impact on the immune response there are a lot of evidence showing that parts Alkrbu ???????? in peptides sugary and glycoproteins play an important role in Alfalitin life and responsiveness