Purpose: The purpose of this study was to compare the outcomes of 2 different anesthetic techniques (local infiltration vs infraorbital nerve block) for eliminating pain during apical surgeries that are associated with extensive periapical pathology in the anterior maxilla. Materials and Methods: Patients were randomly divided into 2 groups: patients in group I were anesthetized labially by local infiltration injections, whereas those in group II received a single infraorbital nerve block. Palatal injections were given for the 2 groups. Once the pain was initiated during surgery, the procedure was discontinued until profound anesthesia was secured. The studied variables were age, gender, onset of anesthesia, operative time, and intraoperati

Hydrogen and nanocarbon were produced by the catalytic decomposition of electrocracking gas obtained by the pyrolysis of liquid organic waste via electric arc discharge. The GIAP-16 (NiO-Al2O3) industrial catalyst was used to reduce the maximum decomposition temperature to 700 °C. In a fixed-bed reactor, under atmospheric pressure, reasonable amounts of high-purity hydrogen were produced, accompanied by deposits of nanocarbon by-product. The NiO-Al2O3 catalyst showed excellent catalytic activity. X-ray powder diffraction analysis of the NiO-Al2O3 composite revealed the presence of cubic NiO and rhombohedral Al2O3, which were chemically stable. However, above 500 °C, NiAl2O4 began to appear. The specific surface area of the catalyst was de

Abstract: Colloidal gold nanoparticles (ringworm Palm or in the form of paper willow) have been prepared from HAuCl4 containing aqueous solution by hot chemical reduction method. The colloidal gold nanoparticles were characterized by SEM, EDX, and UV-VIS absorption spectroscopy. It was found that the variation of reduction time from boiling point affects the size of the nanoparticles and also in chemical reduction approach the size of nanoparticles can be controlled by varying the amount of variation the volume of reductant material with respect to the volume of HAuCL4.

In this study, reduced graphene oxide (rGO) was synthesized from graphene oxide (GO) via an ascorbic acid-assisted reduction process. GO was synthesized from graphite powder using a modified Hummers technique. The surface morphology, structure, functional groups, and elemental compositions of the produced materials were studied using various methods, such as scanning electron microscopy (SEM)/EDX, X-ray diffraction (XRD), atomic force microscopy (AFM), Fourier transform infrared (FTIR), and UV-Vis. The removal of oxygen-containing functional groups in rGO through reduction resulted in poor sample quality. In addition, FTIR investigations revealed that GO contained more oxygen-containing functional groups than rGO. Typical peaks at 2

The whole research paper examines the impact of ozone as either a just use-alone and coagulation benefit, mainly upon the reduction of dissolved organic carbon from the water with a moderate rate of DOC 10.75 mg/land CaCO3 calcium hardness 300 mg/l. A raw water sample has been taken from the Tigris River (Baghdad, Iraq) was being adopted in research work. The performance of ozone therapy has been assessed by calculations of DOC, DOC quantities, UV254, as well as total trihalomethane (TTHM). Research findings have shown that with 0.9 mg O3/mg DOC ozone use-alone, approximately 60% UV254 reduction and approximately 28% DOC reduction will occur.DOC fractionation analysis indicates that within the water samples, ozone could alter the co

Activated carbon prepared from date stones by chemical activation with ferric chloride (FAC) was used an adsorbent to remove phenolic compounds such as phenol (Ph) and p-nitro phenol (PNPh) from aqueous solutions. The influence of process variables represented by solution pH value (2-12), adsorbent to adsorbate weight ratio (0.2-1.8), and contact time (30-150 min) on removal percentage and adsorbed amount of Ph and PNPh onto FAC was studied. For PNPh adsorption,( 97.43 %) maximum removal percentage and (48.71 mg/g) adsorbed amount was achieved at (5) solution pH,( 1) adsorbent to adsorbate weight ratio, and (90 min) contact time. While for Ph adsorption, at (4) solution pH, (1.4) absorbent to adsorbate weight ratio, and (120 min) contact

The goal of this investigation is to prepare zinc oxide (ZnO) nano-thin films by pulsed laser deposition (PLD) technique through Q-switching double frequency Nd:YAG laser (532 nm) wavelength, pulse frequency 6 Hz, and 300 mJ energy under vacuum conditions (10-3 torr) at room temperature. (ZnO) nano-thin films were deposited on glass substrates with different thickness of 300, 600 and 900 nm. ZnO films, were then annealed in air at a temperature of 500 °C for one hour. The results were compared with the researchers' previous theoretical study. The XRD analysis of ZnO nano-thin films indicated a hexagonal multi-crystalline wurtzite structure with preferential growth lines (100), (002), (101) for ZnO nano-thin films with different thi

This research paper studies the use of an environmentally and not expensive method to degrade Orange G dye (OG) from the aqueous solution, where the extract of ficus leaves has been used to fabricate the green bimetallic iron/copper nanoparticles (G-Fe/Cu-NPs). The fabricated G‑Fe/Cu-NPs were characterized utilizing scanning electron microscopy, BET, atomic force microscopy, energy dispersive spectroscopy, Fourier-transform infrared spectroscopy and zeta potential. The rounded and shaped as like spherical nanoparticles were found for G-Fe/Cu‑NPs with the size ranged 32-59 nm and the surface area was 4.452 m²/g. Then the resultant nanoparticles were utilized as a Fenton-like oxidation catalyst. The degradation efficiency of

In this work copper nanopowder was created at different liquid
medias like DDDW, ethylene glycol and Polyvinylpyrrolidone
(PVP). Copper nanopowder prepared using explosion wire process
and investigated the effects of the exploding energy, wire diameter,
the type of liquid on the particle size, and the particles size
distribution. The nanoparticles are characterized by x-ray diffraction,
UV-visible absorption spectroscopy and transmission electron
microscopy (TEM). The x-ray diffraction results reveal that the
nanoparticles continue to routine lattice periodicity at reduced
particle size. The UV-Visible absorption spectrum of liquid solution
for copper nanoparticles shows sharp and single surface Plasmon
r

SiO2 nanostructure is synthesized by the Sol-Gel method and thin films are prepared using dip coating technique. The effect of laser densification is studied. X-ray Diffraction (XRD), Fourier Transformation Infrared Spectrometer (FTIR), and Field Emission Scanning Electron Microscopy (FESEM) are used to analyze the samples. The results show that the silica nanoparticles are successfully synthesized by the sol-gel method after laser densification. XRD patterns show that cristobalite structure is observed from diode laser (410 nm) rather than diode laser (532 nm). FESEM images showed that the shape of nano silica is spherical and the particles size is in nano range (? 100 nm). It is concluded that the spherical nanocrystal structure of silica