This study was undertaken to provide more insight on the optimum injection temperature used for the production of PE crates, thereby saving time and money, and improving part quality. The work included processing trails of HDPE crates in an injection
molding machine at five temperatures ranged from 220 to 300°C. Both Rheological and mechanical characterization was conducted in order to understand the effect of injection temperature on the properties of crates. Oven aging was also applied for (4 weeks) to evaluate the long-term thermal stability. The results revealed that producing the crates at a temperature range of (260-280 °C) gives the best rheological and mechanical result. The lowest drop in thermal stability has been observed

Blend solid polymer electrolytes (BSPEs) comprising PVA/HPMC/CuSO4 were prepared using a solution casting approach. BSPEs were synthesized with varying weight percentages of CuSO4 (0, 10, 20, and 30 wt.%). A variety of experimental methods, including X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and linear sweep voltammetry (LSV), were used to characterize these BSPE systems. The polymer blend matrix underwent structural alterations, according to the XRD data. The standard data from JCPDS card numbers for copper sulfate matches well with the observed strong peaks of PVA/HPMC+20 wt.% of CuSO4 BSPE. The complex

      The current study objective is to synthesize activated carbon (AC) from compressed wood using the ZnCl2 activating agent and to assess the ciprofloxacin (CIP) elimination efficiency in simulated wastewater. The produced AC was characterized using multiple techniques, including SEM, BET, FTIR, AFM, and XRD. The adsorbent demonstrates high adsorption performance, achieving 91% removal of CIP within 5 hours at an initial pollutant concentration of 100 mg/L with an AC dose of 2 g/L. Experimental data correspond to the Freundlich isotherm model (R² = 0.995) as well as the Langmuir competitive fitting (R² = 0.99), while the root mean square error (RMSE) equation best fits the Langmuir model. Moreover, the pseudo-second-order

Concrete filled steel tube (CFST) columns are being popular in civil engineering due to their superior structural characteristics. This paper investigates enhancement in axial behavior of CFST columns by adding steel fibers to plain concrete that infill steel tubes. Four specimens were prepared: two square columns (100*100 mm) and two circular columns (100 mm in diameter). All columns were 60 cm in length. Plain concrete mix and concrete reinforced with steel fibers were used to infill steel tube columns. Ultimate axial load capacity, ductility and failure mode are discussed in this study. The results showed that the ultimate axial load capacity of CFST columns reinforced with steel fibers increased by 28% and 20 % for circular and square c

This research explored the performance of steel fiber concrete-filled stainless-steel tube columns stiffened with embedded carbon steel T-sections with various steel fiber ratios under biaxial bending conditions. A numerical parametric analysis was adopted, using finite element modeling with Abaqus CAE/2021 to evaluate the effects of the fiber ratio (ranging from 0% to 1.5%) on the load-bearing capacity and deflection behavior of columns. In addition, the compressive strength of concrete ranged between 45 and 65 MPa. An increase in the fiber ratio led to a substantial improvement in the ultimate load-bearing capacity (up to 24%), a reduction in deflection (of approximately 49%), and an improvement in column ductility, which were obt

ABSTRACT

Naproxen(NPX) imprinted liquid electrodes of polymers are built using polymerization precipitation. The molecularly imprinted (MIP) and non imprinted (NIP) polymers were synthesized using NPX as a template. In the polymerization precipitation involved, styrene(STY) was used as monomer, N,N-methylenediacrylamide (N,N-MDAM) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The molecularly imprinted membranes and the non-imprinted membranes were prepared using acetophenone(AOPH) and di octylphathalate(DOP)as plasticizers in PVC matrix. The slopes and detection limits of the liquid electrodes ranged from)-18.1,-17.72 (mV/decade and )4.0 x 10^-