In the present work, a closed loop circulation system consist of three testing sections was designed and constructed. The testing sections made from (3m) of commercial carbon steel pipe of diameters(5.08, 2.54 and 1.91 cm) . Anionic surfactant (SDBS )with concentrations of (50, 100, 150, 200 and 250 ppm) was tested as a drag reducing agent. The additive(SDBS)studied using crude oil from south of Iraq. The flow rates of crude oil were used in 5.08 and 2.54 cm I.D. pipes are (1 - 12) m3/hr while (1-6) m3/hr were used in 1.91 cm J .D. pipe . Percentage drag reduction (%Dr) was found to increase by increasing solution velocity, pipe diameter and additives concentration (i.e. increasing Renolds number). Also it was found that there is no change in apparent physical properties (viscosity) of crude oil after the addition of SDBS. The higher value of drag reduction of 54% in 5.08 cm I.D. was observed using 250 ppm SDBS surfactant dissolved in the used crude oil at flow rate of 12 m3/hr. Friction factor was calculated from experimental data. The friction factors values for pure solvent lies near or at Blasius asymptote suggested for flow of Newtonian fluids. After the addition of small amount of SDBS, the friction factor values were positioned below Blasius asymptote toward Virk maximum drag reduction asymptote, which was never reached.
Drag Reduction of Crude Oil Flow in Pipelines Using Sodium Dodecyl Benzene Sulfonate Surfactant
drag reduction surfactants
Publication Date
Tue Jan 18 2022
Journal Name
Materials Science Forum
The Effect of Gamma Radiation on the Manufactured HgBa<sub>2</sub>Ca<sub>2</sub>Cu<sub>2.4</sub>Ag<sub>0.6</sub>O<sub>8+δ</sub> Compound
Gamma doses radiation
crystal size
strain
degree of crystallinity
Scherrer
crystallinity and Williamson equations.
In this article four samples of HgBa2Ca2Cu2.4Ag0.6O8+δ were prepared and irradiated with different doses of gamma radiation 6, 8 and 10 Mrad. The effects of gamma irradiation on structure of HgBa2Ca2Cu2.4Ag0.6O8+δ samples were characterized using X-ray diffraction. It was concluded that there effect on structure by gamma irradiation. Scherrer, crystallization, and Williamson equations were applied based on the X-ray diffraction diagram and for all gamma doses, to calculate crystal size, strain, and degree of crystallinity. I