The aim of this work was to prepare zeolite type 13X from locally available kaolin and to study the effects of using some binding materials through the process of agglomeration of this zeolite. This study was focused on using kaolin binder in different weight percents (10,15,25,35 and 45%).Physical and mechanical properties of the agglomerates such as porosity , apparent density , pore volume, crushing strength , loss on attrition , surface area and finally the adsorption capacity had been measured and evaluated .The preparation step was achieved by mixing the reactants consisting of metakaolin , source of silica as ( sodium trisilicate ) and sodium hydroxide . The conditions was temperature of 70° C and time of mixing as 8, 10,24,34,50,65,75 and 80 hours .The zeolite –binder was shaped in the form of cylindrical particles of 2.5 mm in diameter and 4-8 mm long using a suitable experimental technique . It was found that the suitable binder kaolin clay with 25% by weight. This gave the best properties as crushing strength, adsorption capacity and density compared with standard properties of zeolite 13X.
Objective: Econazole nitrate (ECZ) is one of the triazole antifungal drugs with poor aqueous solubility and dissolution rate; there is a need for enhancement of solubility. Therefore; inclusion complexation with β cyclodextrin (βCD) was performed. Methods: In this study kneading method and co-evaporation method of preparation of inclusion complex between βCD and ECZ using two molar ratios of βCD. The solubility of these complexes in isotonic saline solution and distilled water was studied. Complexes prepared by kneading method were used for the preparation of different ophthalmic gel formulas using carbomer (CB) and sodium carboxymethylcellulose (sod CMC) as a gelling agent. The release profile and the rheological behaviour of the gel w
... Show More
(6)
In this work, an anti-reflection coating was prepared in the region (400-1000) nm of wavelength, with a double layer of silicon dioxide (SiO2) as an inner layer and the second layer of the mixture (SiO2) and titanium dioxide (TiO2) with certain ratios, as an outer layer using the chemical spraying method with a number of 6 sprays of layer SiO2 and 12 sprays of layer SiO2 - TiO2. Using the method of chemical spraying deposited on the glass as a substrate with a different number of sprays of SiO2, and a fixed number of TiO2-SiO2. The optical and structural properties were determined using UV-Vis spectroscopy and atomic force mi
... Show More
(3)
A new macrocyclic multidentate Schiff-base ligand Na4L consisting of two submacrocyclic units (10,21-bis-iminomethyl-3,6,14,17- tricyclo[17.3.1.18,12]tetracosa-1(23),2,6,8,10,12(24),13,17,19,21,-decaene-23,24-disodium) and its tetranuclear metal complexes with Mn(II), Co(II), Ni(II), Cu(II), and Zn(II) are reported. Na4L was prepared via a template approach, which is based on the condensation reaction of sodium 2,4,6-triformyl phenolate with ethylenediamine in mole ratios of 2 : 3. The tetranuclear macrocyclic-based complexes were prepared from the reaction of the corresponding metal chloride with the ligand. The mode of bonding and overall geometry of the compounds were determined through physicochemical and spectroscopic methods. These st
... Show More
(19)
Schiff base of chitosan with Para-Dimethyl aminobenzaldehyde /PVA-Ag Nanocomposite have been prepared as antimicrobial polymer. The prepared chitosan Schiff base and chitosan Schiff base / PVA-Ag nanocomposite were characterized by FT-IR, SEM analysis and biological activity. The nanocomposite showed good activity against different types of bacteria.
Alumina thin films have significant applications in the areas of optoelectronics, optics, electrical insulators, sensors and tribology. The novel aspect of this work is that the homogeneous alumina thin films were prepared in several stages to generate a plasma jet. In this paper, aluminium nanoparticles suspended in vinyl alcohol were prepared using exploding wire plasma. TEM analysis was used to determine the size and shape of particles in aluminium and vinyl alcohol suspensions; the TEM images showed that the particle size is 17.2 nm. Aluminium/poly vinyl alcohol (Al/PVA) thin films were prepared using this suspension on quartz substrate by plasma jet technique at room temperature with an argon gas flow rate of 1 L/min. The Al/PV
... Show More
(3)
(2)
Flurbiprofen (FLB) is chemically 2-(3- fluoro-4-phenyl phenyl) propanoic acid. It is a nonsteroidal anti-inflammatory drug (NSAID) used in the treatment of rheumatoid arthritis and osteoarthritis. Oral administration of this drug is associated with severe gastrointestinal side effects like ulceration and gastrointestinal bleeding. The solution to this problem lies in the fact that topically applied NSAIDs are safer than orally. This study aims to prepare different topical semisolid formulation of FLB as cream base (o/w), (w/o) and gel base using different gel-forming agents in different concentrations. Comparing characterization properties in addition to release and diffusion study for all the prepared formulas to select the best on
... Show More
(7)
(3)
An oxidative polymerization approach was used to create polyaniline (PANI) and Fe2O3 /PANI nanoparticle combination. Various characterization approaches were used to investigate the structural, morphological, and Fe2O3 /PANI nanoparticle structures. The findings support the synthesis of polycrystalline nanoparticle PANI and Fe2O3 /PANI spherical nanoparticle composites. Gram-positive bacteria are tested for antibacterial activity. Various quantities of Nanoparticles of PANI and Fe2O3 /PANI nanoparticle composites were used to test Staph-aureus and gram-negative bacteria, E-coli, and candida species. PANI has antibacterial properties against all microo
... Show More
(3)
This article includes the preparation of luminescence materials from rare earth (Eu ) ion doping Yttrium Oxide (Y2O3) 70% and SiO2 25% and study the characteristics of phosphors for ultraviolet to visible conversion. The phosphor materials have been synthesized by two steps: Preparing the powder by solid state method using Y2O3, SiO2 and Eu2O3 with doping materials concentration (70%, 25% and 5%) respectively and different calcination temperature (1000, 1200 and 1400 oC).
The second step is to prepare the colloid solution by dispersing the produced powder in a polyvinyl alcohol solution (4%) .
Powde
... Show MoreBiomimatic basic calcium phosphate ,known as Hydroxy apatite(HA), was
synthesised using calcium acetate and disodium phosphate dilute hot (boiling) solution of
both salts were added slowly to each other. A colloidal suspension formed was aged for few
days, then boiled for one hour to induced setting and coagulation of preapatite, and left to cool
until they reached room temperature.
The precipitate was filtered and washed with distilled water, then ethanol and dried.
The dried sample was calcined at 1100
o
C.The obtained solid lumps were then crushed
reground fine powder and analyzed for calcium to phosphorous ratio. X-ray analysis was
carried out to examine the solid sample. Chemical analysis for phos
Abstract
The aim of this study was to prepare rebamipide ocular inserts in order to extend its release on the ocular surface for dry eye treatment. Solubility study was applied to the drug with or without l-arginine using different solvents. Solvent casting technique was used to prepare the inserts; l-arginine was used to solubilize the drug, hydroxypropyl methylcellulose grades (E5 and K15M) and poly ethylene glycol 200 were used as excipients. The inserts were evaluated for their physical and mechanical properties, moisture loss% and absorption %, surface pH, and in-vitro drug release. The use l-arginine exhibited an enhancement of rebamipide solubility in both deionized water and phosphate buffer (pH 7.4) by a
... Show More
(6)
(1)