The crystalline zeolite, namely faujasite type Y with SiO2/Al2O3 mole ratio of 5 was used as raw material for preparation of isomerization catalysts. A 0.5 wt % Pt/HY-zeolite catalyst was prepared by impregnation of the decationized HY-zeolite with chloroplatinic acid. The dectionized HY-zeolite was treated with HCl, HNO3 and HI promoters using different normalities and with different concentrations of Sn, Ni and Ti promoters by impregnation method to obtain acidic and metallic promoters' catalysts, respectively. A 0.5 wt% of Pt was added to above catalysts using impregnation method. Isomerization of n-hexane was carried out at different prepared catalysts. The isomerization temperature varied from 250–325° C over weight hourly space velocity (WHSV) 1.6 h-1. The pressure and hydrogen to feed mole ratio were kept constant at 1bar and 2 mol/mol, respectively. The comparison between the above prepared catalysts shows that the total isomer yield during the process with Sn-Pt /HY- zeolite catalyst was higher than the other catalysts and, reached to 63.95% vol. A 0.5 wt% of W and Zr was added to Sn-Pt/HY-zeolite catalyst by impregnation method to obtain W and Zr co-metal promoters catalysts. Isomerization of n-hexane was investigated using W and Zr co-metal promoters catalyst at the same operating conditions and the yield of isomers reached to 81.14% vol.and 79.07%vol.,respectively.
The aqueous extract of banana fruits peal was tested for its effect on mitosis . The root tips of Allium cepa were used as plant test system and the bone marrow cells of the albino mice Mus musculus were used as mammalians test system in vivo .Root tips of Allium cepa were treated for four hours with five concentrations of the extract (5 , 10 , 20 , 40 ,60 mg / ml.).The Metaphase was arrested in all the treatments , the highest percentage ( 100 % ) was recorded in the first concentration , the last concentration caused stickiness and clumping of the chromosomes. The treatments did not cause significant difference in the mitotic index. The peals extract (5 mg /ml) was compared with the extracts of fruits bulb, leaves and r
... Show More
Purepolyaniline and doped with hydrochloric acid was prepared in different molarities at room temperature. The a.c electrical properties were stadied.AC conductivityσac (ω), is found to vary as ωS in the frequency range (100Hz-10MH), S< 1and decreases indicating a dominate hopping process. Thedielectric constant ε1and dielectric loss ε2 have been determined for bulk polyaniline. ε1 decrease with the increase frequency. Electrical conductivity measurements increase with the increases both of the amount of HCl and the dose of radiation. The dielectric investigations show decrease with dose radiation.
Background: Hypothyroidism is the most abundant thyroid disorder worldwide. For decades, levothyroxine was the main effective pharmacological treatment for hypothyroidism. A variety of factors can influence levothyroxine dose, such as genetic variations. Studying the impact of genetic polymorphisms on the administration of medications was risen remarkably. Different genetic variations were investigated that might affect levothyroxine dose requirements, especially the deiodinase enzymes. Deiodinase type 2 genetic polymorphisms’ impact on levothyroxine dose was studied in different populations. Objective: To examine the association of the two single nucleotide polymorphism (SNP)s of deiodinase type 2 (rs225013 and rs225014) and le
... Show More
The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the
... Show MoreThe aqueous extract of banana fruits peal was tested for its effect on mitosis . The root tips of Allium cepa were used as plant test system and the bone marrow cells of the albino mice Mus musculus were used as mammalians test system in vivo .Root tips of Allium cepa were treated for four hours with five concentrations of the extract (5 , 10 , 20 , 40 ,60 mg / ml.).The Metaphase was arrested in all the treatments , the highest percentage ( 100 % ) was recorded in the first concentration , the last concentration caused stickiness and clumping of the chromosomes. The treatments did not cause significant difference in the mitotic index. The peals extract (5 mg /ml) was compared with the extracts of fruits bulb, leaves and roots of
... Show More
(1)
(1)
This study offers the elastic response of the variable thickness functionally graded (FG) by single walled carbon nanotubes reinforced composite (CNTRC) moderately thick cylindrical panels under rotating and transverse mechanical loadings. It’s considered that, three kinds of distributions of carbon nanotubes which are uniaxial aligned in the longitudinal direction and two functionally graded in the transverse direction of the cylindrical panels. Depending on first order shear deformation theory (FSDT), the governing equations can be derived. The partial differential equations are solved by utilizing the technique of finite element method (FEM) with a program has been built by using FORTRAN 95. The results are calculat
... Show More
(3)
Zinc Oxide (ZnO) thin films of different thickness were prepared
on ultrasonically cleaned corning glass substrate, by pulsed laser
deposition technique (PLD) at room temperature. Since most
application of ZnO thin film are certainly related to its optical
properties, so the optical properties of ZnO thin film in the
wavelength range (300-1100) nm were studied, it was observed that
all ZnO films have high transmittance (˃ 80 %) in the wavelength
region (400-1100) nm and it increase as the film thickness increase,
using the optical transmittance to calculate optical energy gap (Eg
opt)
show that (Eg
opt) of a direct allowed transition and its value nearly
constant (~ 3.2 eV) for all film thickness (150
(3)
Glass Ionomer Cement (GIC) is one of the important dental temporary filing materials. The aim of this study is to evaluate the effect of adding 3, 5 and 7 wt. % of TiO2 microparticles to conventional GIC powder (Riva Self Cure) on mechanical properties and its effect on absorption and solubility processes. TiO2 particles additives improved compressive strength and biaxial flexural strength, where the compressive strength increased with increasing in the added ratio, while the highest value of the biaxial flexural strength was at 3 wt.%. The addition of TiO2 particles improved the surface Vickers microhardness values, with highest value at 5 wt. %. On other hand TiO2 addition im