An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time
Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .
The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no interaction effect between the variables studied.
Furthermore, the results show that, the crushing strength for the calcined extrudate was affected by the speed of mixing only and the optimum speed is 900rpm.
The maximum crushing strength of 38.38 after calcinations and 11.865 Kg/mm after drying were obtained
Background: Fixed orthodontic appliances impede the maintenance of oral hygiene and result in plaque accumulation leads to enamel demineralization caused by acids produced by bacteria. Studies on plaque control strategies in orthodontic populations are limited. This might be caused by difficulties in the quantitative evaluation of dental plaque because the teeth have various levels of bracket coverage, and different tooth sizes and malocclusions, making the traditional categorical indices complex. The present study aims to evaluate the effect of different hygiene protocols on plaque quantity on bands with different attachments. Materials and method: Twenty patients had four bands within the orthodontic appliance. Then randomly divided into
... Show MoreThe aim of this paper is to find out the effects of the strategy of productive thinking upon the student’s achievement for the subject of research methodology in the College of Islamic Sciences. Achieving this objective, the researchers set the null hypotheses: (1) No difference is noticed to be statistically significant at the level of significance (0.05) among the student’s mean scores in the experimental group who were taught by the strategy of productive thinking, and the student’s mean scores in the control group who studied by the traditional method in the achievement test. (2) At level of sig. (0.05), there is no statistically significant difference in the mean of scores of the pre-tests and post ones in the achievement test of
... Show MoreThe aim of this paper is to find out the effects of the strategy of productive thinking upon the student’s achievement for the subject of research methodology in the College of Islamic Sciences. Achieving this objective, the researchers set the null hypotheses: (1) No difference is noticed to be statistically significant at the level of significance (0.05) among the student’s mean scores in the experimental group who were taught by the strategy of productive thinking, and the student’s mean scores in the control group who studied by the traditional method in the achievement test. (2) At level of sig. (0.05), there is no statistically significant difference in the mean of scores of the pre-tests and post ones in the achievement test of
... Show MoreExperiment Factorial conducted with two factor in field texture silt clay loam soil, the first factor were Two Rotavator plow which different in number of rotary blades on flanges, weight, width, made and type, the second factor were four speeds tractor 2.62, 5.10, 7.55, 9.23 km/hr to compare performance two Rotavator under depth 12 cm and knowledge slippage, distance between beat blades, practical productivity, disturbed soil volume, percentage of the soil clods which have diameter less than 5 cm under complete block design with three replications using Least Significant Design 0.05. Results showed Galucho Rotavator recorder the higher practical productivity 0>7089 ha/hr, disturbed soil volume 809.8 m3/hr, percentage of the soil clods 96.1
... Show MoreObjective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa
In this study, SnO2 nanoparticles were prepared from cost-low tin chloride (SnCl2.2H2O) and ethanol by adding ammonia solution by the sol-gel method, which is one of the lowest-cost and simplest techniques. The SnO2 nanoparticles were dried in a drying oven at a temperature of 70°C for 7 hours. After that, it burned in an oven at a temperature of 200°C for 24 hours. The structure, material, morphological, and optical properties of the synthesized SnO2 in nanoparticle sizes are studied utilizing X-ray diffraction. The Scherrer expression was used to compute nanoparticle sizes according to X-ray diffraction, and the results needed to be scrutinized more closely. The micro-strain indi
... Show MoreA pots experiment was conducted in the plastic house of Kalar Horticulture station Province of Sulaimania, by using soil brought from one of Kalar region fields during growing season of 2007-2008, to study the effect of increasing levels of urea fertilizer which is (0, 0.20,0.40,0.80) g/pot which equals to (0,100,200,400) kg urea/ha, and super phosphate fertilizer which is (0,0.24,0.48)gm/pot which is equal (0,120,240) kg sup/ha, in nutrition state of wheat IPA 95 component, clay determining Nitrogen, Phosphor and Potassium content in green part and seeds. The Completely Randomized Design was used with three replication per t
... Show MoreA thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.
Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3
Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect