An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time
Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .
The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no interaction effect between the variables studied.
Furthermore, the results show that, the crushing strength for the calcined extrudate was affected by the speed of mixing only and the optimum speed is 900rpm.
The maximum crushing strength of 38.38 after calcinations and 11.865 Kg/mm after drying were obtained
This study was carried out to find out the effect of germination of broad beans and chickpeas seeds for different periods on their antinutritional factors content ( Trypsin inhibitor and Phytic acid ) and the chemical constituents of germination seeds compared with the control samples (ungerminated seeds) . The results indicated asignificant increase (P<0.05) in crude protein content as germination period proceeded.The highest values of 28.0% and 24.0% were reached on the sixth and fourth day for germinated broad beans and chickpeas respectively, The intial values were 25.6% and 23.5% for control samples, respectively. The content of raffinose,stachyose and verbascose were reduced as germination period proceeded, Stachyose and verbascose we
... Show More
In this study, the effect of the thermal conductivity of phase change material (PCM) on the performance of thermal energy storage has been analyzed numerically. A horizontal concentric shell-and-tube latent heat thermal energy storage system (LHTESS) has been performed during the solidification process. Two types of paraffin wax with different melting temperatures and thermal conductivity were used as a PCM on the shell side, case1=0.265W/m.K and case2=0.311 W/m.K. Water has been used as heat transfer fluid (HTF) flow through in tube side. Ansys fluent has been used to analyze the model by taking into account phase change by the enthalpy method used to deal with phase transition. The numerical simulatio
... Show More
(10)
In this work, results of a mathematical analysis of the role of workpiece preheating in laser keyhole welding were presented. This analysis considered the steady-state welding as well as certain range of boundary conditions over which preheating effect would be indicated. This work is an attempt to interpret the role of preheating to increase welding depth and perform keyhole welding with high quality using physical and thermal properties of steel alloys.
The purpose of this study is designate quenching and tempering heat treatment by using Taguchi technique to determine optimal factors of heat treatment (austenitizing temperature, percentage of nanoparticles, type of base media, nanoparticles type and soaking time) for increasing hardness, wear rate and impact energy properties of 420 martensitic stainless steel. An (L18) orthogonal array was chosen for the design of experiment. The optimum process parameters were determined by using signal-to-noise ratio (larger is better) criterion for hardness and impact energy while (Smaller is better) criterion was for the wear rate. The importance levels of process parameters that effect on hardness, wear rate and impact energy propertie
... Show More
(2)
The experiment was conducted using Potato( Solanum tuberosum L.) at the eastern Radwaniyah at private field during fall season 2020/2021 and spring 2021 to study the effect of nitrogen levels to 350, 275, 200 kg N h-1 ( N1, N2, N3) and phosphorous to 100, 180, 360 kg P2O5 h-1 ( P1, P2, P3) and potassium to 100, 200, 300 kg K2O h-1 ( K1, K2, K3) to vegetative growth and yield of industrial potato, The seeds of the hybrid potato Sinora, Class A, were planted in the fall season on 15/9/2020 and Elite in the spring season on 31/1/2021. The experimental fertilizers were added in four batches and in proportions according to the stages of plant age, Factorial experiment with RCBD using three replications. The results showed that changing t
... Show More
(5)
(1)
(1)
Background: Adjustment of any premature occlusal contact of any zirconia restoration requires its polishing or glazing in order to restore the smoothness of the restoration. The objective of this in vitro study was to evaluate the effects of different polishing systems and glazing on the surface roughness of full-contour zirconia. Material and methods: Forty disks (diameter: 8 mm, thickness: 6.4 mm) were prepared from pre-sintered full-contoured zirconia block; they were colored and sintered in a high-temperature furnace at 1500ËšC for 8 hours. The specimens were then leveled and finished using grinding and polishing machine and adjusted using diamond disk. The specimens were then randomly divided into four groups (n=10), group I involves
... Show MoreAn experiment was carried out on the fields of the college of Agriculture - Abu Ghraib, of a silty clay loam soil that has moisture of 15-16%, to study the effect of plowing and pulverization systems on some plant indicators of onion. The experiment included plowing systems with three levels (plowing with a moldboard plow, plowing by chisel plow and zero tillage plowing) as a primary factor. The second factor was that pulverization for only one time and repeating the pulverization twice through the use of the rotary tiller. The plant indicators of onion that are studied: plant length, onion diameter, onion weight and onion neck diameter. The experiment has carried out according to SPLIT PLOT design according to RCBD design by three replicat
... Show MoreInSb alloy was prepared then InSb:Bi films have been prepared successfully by thermal evaporation technique on glass substrate at Ts=423K. The variation of activation energies(Ea1,Ea2)of d.c conductivity with annealing temperature (303, 373, 423, 473, 523 and 573)K were measured, it is found that its values increases with increasing annealing temperature. To show the type of the films, the Hall and thermoelectric power were measured. The activation energy of the thermoelectric power is much smaller than for d.c conductivity and increases with increasing annealing temperature .The mobility and carrier concentration has been measured also.