The catalytic activity of faujasite type NaY catalysts prepared from local clay (kaolin) with different Si/Al ratio was studied using cumene cracking as a model for catalytic cracking process in the temperature range of 450-525° C, weight hourly space velocity (WHSV) of 5-20 h1, particle size ≤75μm and atmospheric pressure. The catalytic activity was investigated using experimental laboratory plant scale of fluidized bed reactor.
It was found that the cumene conversion increases with increasing temperature and decreasing WHSV. At 525° C and WHSV 5 h-1, the conversion was 42.36 and 35.43 mol% for catalyst with 3.54 Si/Al ratio and Catalyst with 5.75 Si/Al ratio, respectively, while at 450° C and at the same WHSV, the conversion was decreased to 29.15 and 21.86 mol% respectively, and the catalyst of 5.75 Si/Al ratio gave the higher cumene activity than the catalyst with 3.54 Si/Al ratio.
The effect of Wood Flour addition to the gamma alumina powder used in the preparation of gamma alumina (ɤ-Al2O3) catalyst carrier extrudates on the pore volume and BET surface area physical properties was investigated. Two parameters which are size of wood flour particles and its quantity were studied. The sizes of wood flour particles used are 150 µm, 212 µm and 500 µm and the weight percentage added to the gamma alumina powder during the preparation of the extrudates are (1%, 3%, 5% and 10%). The results showed that the addition of wood flour to the gamma alumina powder in order to get gamma alumina extrudates used as catalyst carrier is one of the successful methods to improve the pore volume
... Show More
The cost-effective carbon cross-linked Y zeolite nanocrystals composite (NYC) was prepared using an eco-friendly substrate prepared from bio-waste and organic adhesive at intermediate conditions. The green synthesis method dependent in this study assures using chemically harmless compounds to ensure homogeneous distribution of zeolite over porous carbon. The greenly prepared cross-linked composite was extensively characterized using Fourier transform infrared, nitrogen adsorption/desorption, Field emission scanning electron microscope, Dispersive analysis by X-ray, Thermogravimetric analysis, and X-ray diffraction. NYC had a surface area of 176.44 m2/g, and a pore volume of 0.0573 cm3/g. NYC had a multi-function nature, sustained at a long-
... Show More
(39)
AlPO4 solid acid catalyst was prepared in order to use it in transesterification reaction of edible oil after supporting it with tungsten oxide. The maximum conversion of edible oil was obtained 78.78% at catalyst concentration (5gm.), temperature 70°Ϲ, 30/1 methanol/edible oil molar ratio, and time 5hr. The study of kinetics of the transesterification reaction of edible oil indicates that the reaction has an order of 3/2, while the value of activation energy for transesterification reaction is 51.367 kJ/mole and frequency factor equal 26219.13(L/ mol.minute).
(1)
AlPO4 solid acid catalyst was prepared in order to use it in transesterification reaction of edible oil after supporting it with tungsten oxide. The maximum conversion of edible oil was obtained 78.78% at catalyst concentration (5gm.), temperature 70°Ϲ, 30/1 methanol/edible oil molar ratio, and time 5hr. The study of kinetics of the transesterification reaction of edible oil indicates that the reaction has an order of 3/2, while the value of activation energy for transesterification reaction is 51.367 kJ/mole and frequency factor equal 26219.13(L/ mol.minute).
(1)
Indium oxide In2O3 thin films fabricated using thermal evaporation of indium metal in vacuum on a glass substrate at 25oC using array mask, after deposition the indium films have been subjected to thermal oxidation at temperature 400 °C for 1h. The results of prepared Indium oxide reveal the oxidation method as a strong effect on the morphology and optical properties of the samples as fabricated. The band gap (Eg) of In2O3 films at 400 °C is 2.7 eV. Then, SEM and XRD measurements are also used to investigate the morphology and structure of the indium oxide In2O3 thin films. The antimicrobial activity of indium oxide In2O3 thin films was assessed against gram-negative bacterium using inhibition zone of bacteria which improved higher ina
... Show More
(5)
This work deals with the separation of benzene and toluene from a BTX fraction. The separation was carried out using adsorption by molecular sieve zeolite 13X in a fixed bed. The concentration of benzene and toluene in the influent streams was measured using gas chromatography. The effect of flow rate in the range 0.77 – 2.0 cm3/min on the benzene and toluene extraction from BTX fraction was studied. The flow rate increasing decreases the breakthrough and saturation times. The effect of bed height in the range 31.6 – 63.3 cm on benzene and toluene adsorption from BTX fraction was studied. The increase of bed height increasing increases the break point values. The effect of the concentration of benzene in the range 0.0559 – 0.2625g/
... Show MoreThe present study aims to remove nickel ions from solution of the simulated wastewater using (Laminaria saccharina) algae as a biosorbent material. Effects of experimental parameters such as temperature at (20 - 40) C⁰, pH at (3 - 7) at time (10 - 120) min on the removal efficiency were studied.
Box-Wilson method was adopted to obtain a relationship between the above three experimental parameters and removal percentage of the nickel ions. The experimental data were fitted to second order polynomial model, and the optimum conditions for the removal process of nickel ions were obtained.
The highest removal percentage of nickel ions obtained was 98.8 %, at best operating conditions (Temperature 35 C⁰, pH 5 and Time 10 min).
This study is aimed to use the aerobic packed bed in biotreatment of the wastewater which is discharge from AL-KARAMA teaching hospital in Baghdad. The performance of packed-bed treatment method was examined for elimination of the organic compounds from wastewater under aerobic conditions. In this research different parameters were studied. They were: inoculums concentration, circulation rate of wastewater through the bed, packing type and the temperature. Results showed that the system efficiently removed about 82% of the chemical oxygen demand (COD) and 80% of the Biological oxygen demand (BOD). Percent reduction in turbidity was about 92% and reduction in nitrate concentration was about 87%. It was found that best performance of the pack
... Show More
An International Publisher for Academic and Scientific Journals The mucilage of white and black chia seeds were extracted and determining their contents of bioactive compounds such as tannins, glycosides, flavonoids, phenols, and studying their activity as anti-filamentary and anticancer. Results showed that tannins exist in white chia seeds with 35%while it is 38% in black seeds, flavonoids represent 0.98mg/ml in white chia seeds and 1.5 mg/ml for black seeds. Both kinds of seeds showed anti-filamentaryactivity, the inhibition ratio was 86.5% for white seeds and 97.3% for black seeds. Chia black seeds showed anticancer activity and the inhibition of the tumor muscle cell line ratio (GI%) was 34.8% at 50mg/ml concentration and 88.4%
... Show More