Corrosion- induced damage in reinforced concrete structure such as bridges, parking garages, and buildings, and the related cost for maintaining them in a serviceable condition, is a source of major concern for the owners of these structures.
Fly ash produced from south Baghdad power plant with different concentrations (20, 25 and 30) % by weight from the cement ratio were used as a corrosion inhibitor as a weight ratio from the cement content.
The concrete batch ratio under study was (1:1.5:3) cement, sand and gravel respectively which is used in Iraq. All the raw materials used were locally manufactured.
Concrete slabs (250x250x70) mm dimensions were casted, using Poly-wood molds. Two steel bars were embedded in the central position of each slab at the mid- height (about 35 mm), with a space of 100 mm between each other.
A 16 concrete slabs were prepared (0, 20, 25 and 30) wt. % of fly ash. The specimens were partially immersed in 3.5 wt. % NaCl solution in order to predict the corrosion.
Half-cell potential test technique was used to estimate the corrosion rate which is occurred in the steel bar due to the migration of chloride ions through the concrete, depending on the ASTM C876-08.
The result shows that the potential values of steel in concrete were shifts to the positive direction with increasing the percentage of fly ash, because the reduction of porosity by the addition of fly ash which fill the pores and inhibit the chloride ions to reach to steel.
The results also show that the further increase of fly ash (30%) the possibility of carbonation is increased which result in reduction its alkalinity, thereby permitting corrosion of embedded steel.
There are no single materials which can withstand all the extreme operating conditions in modern technology. Protection of the metals from hostile environments has therefore become a technical and economic necessity.
In this work, for enhancing their wear-resistance, boride layers were deposited on the surface of low carbon steel by a pack cementation method at 850 °C for (2, 4, and 6) h using vacuum furnace. The boronizing process was achieved using different concentration of boron source (20, 25, and 30) % wt. into coating mixture to optimize the best conditions which ensure the higher properties with lower time. The coating was characteristic by X ray diffraction (XRD), and it is confirmed t
... Show MoreTodays, World is faced an energy crisis because of a continuous increasing the consumption of fuels due to intension demand for all types of vehicles. This study is one of the efforts dealing with reduce the weight of vehicles by using a new material of sandwich steel, which consists of two skin steel sheets with core of a polymer material. Resistance spot welding (RSW) can be easily implemented on metals; however a cupper shunt tool was designed to perform the resistance welding of sandwich steel with DP800 cover sheets to resolve a non-conductivity problem of a polymer core. Numerical simulations with SORPAS®3D were employed to test the weldability of this new material and supported by many practical experiments. In conclus
... Show MoreThis Investigation aims to study the effect of adding Steel fibers with different volume fractions Vf (o.5, 0.75, and 1% by volume of concrete) with aspect ratio 100 on mechanical properties of concrete, and also
finding the influence of petroleum products (Kerosene and Diesel) on mechanical properties of Steel Fiber Reinforced Concrete (SFRC).
The experimental work consists of two groups: group one consists of specimens (cubes and prisms) plain and concrete reinforced with steel fiber exposed to continuous curing with water. Group two consists of
specimens (cubes and prisms) plain and concrete reinforced with steel fiber exposed to kerosene and diesel after curing them in water for 28 days before exposure. The results of all te
يعتبر "تاج الأشواك" أو نبات شوكة المسيح، وهو من نباتات الزينة الطبية ، ينتمي إلى جنس يوفوربيا. E. milii يحتوي كميات وفيرة من المركبات الفينولية ، التربينات، الستيرويدات والقلويدات. كانت الأهداف الرئيسية لهذه الدراسة هي فحص مستخلصات الفلافونويد والنانو فلافونويد ضد نوعين من خطوط الخلايا السرطانية. تم تصنيع مركبات الفلافونويد النانوية عن طريق تفاعل مركب الكيتوسان والماليك اسد. تم تحليل مركبات الفلافونويد ال
... Show More
(1)
Some types of the fungus Aspergillus were isolated from some hospitals in the city of Baghdad (Imam Ali Hospital and Sadr General Hospital). The samples were taken by Transport media at a rate of three replicates of each place isolated from samples from different places within the hospital (waste, baths, the sick beds, corridors and room floors) for the purpose of isolating and diagnosing the fungus on the Czapeck Dox Agar media. It was noticed that the spread rate of fungus Aspergillus was 70% compared to other species that have emerged during the isolation process of the Sabouraud's Dextrose Agar media. The species A.niger (56.25%) was considered the most common type of fungus visible during the isolation process of the Imam Ali Hospit
... Show MorePseudomonas aeruginosa is a common and major opportunistic human pathogen, its causes many and dangersinfectious diseases due to death in some timesex: cystic fibrosis , wounds inflammation , burns inflammation , urinary tract infection , other many infections otitis external , Endocarditis , nosocomial infection and also causes other blood infections (Bacteremia). thereforebecomes founding fast and exact identification of P. aeruginosafrom samples culture very important.However, identification of this species may be problematic due to the marked phenotypic variabilitydemonstrated by samples isolates and the presence of other closely related species. To facilitate species identification, we used 16S ribosomal DNA(rRNA) sequence data
... Show More
(8)