Reinforcement Steel Corrosion Reduction by Using Fly Ash from South Baghdad Power Plant
...Show More Authors

Corrosion- induced damage in reinforced concrete structure such as bridges, parking garages, and buildings, and the related cost for maintaining them in a serviceable condition, is a source of major concern for the owners of these structures.
Fly ash produced from south Baghdad power plant with different concentrations (20, 25 and 30) % by weight from the cement ratio were used as a corrosion inhibitor as a weight ratio from the cement content.
The concrete batch ratio under study was (1:1.5:3) cement, sand and gravel respectively which is used in Iraq. All the raw materials used were locally manufactured.
Concrete slabs (250x250x70) mm dimensions were casted, using Poly-wood molds. Two steel bars were embedded in the central position of each slab at the mid- height (about 35 mm), with a space of 100 mm between each other.
A 16 concrete slabs were prepared (0, 20, 25 and 30) wt. % of fly ash. The specimens were partially immersed in 3.5 wt. % NaCl solution in order to predict the corrosion.
Half-cell potential test technique was used to estimate the corrosion rate which is occurred in the steel bar due to the migration of chloride ions through the concrete, depending on the ASTM C876-08.
The result shows that the potential values of steel in concrete were shifts to the positive direction with increasing the percentage of fly ash, because the reduction of porosity by the addition of fly ash which fill the pores and inhibit the chloride ions to reach to steel.
The results also show that the further increase of fly ash (30%) the possibility of carbonation is increased which result in reduction its alkalinity, thereby permitting corrosion of embedded steel.

View Publication Preview PDF
Quick Preview PDF
Publication Date
Tue Jan 01 2019
Journal Name
Plant Archive
The enhancement of drought tolerance for plant onion (allium cepa l.) inoculated by arbuscular mycorrhizal fungi
...Show More Authors

Scopus (3)
Scopus
Publication Date
Tue Dec 01 2009
Journal Name
Bulletin Of The Iraq Natural History Museum (p-issn: 1017-8678 , E-issn: 2311-9799)
MICROFCIES OF TEL HAJAR FORMATION IN SOUTH-WEST IRAQ
...Show More Authors

The Tel Hajar formation in the studied area has been divided into five microfacics units:

1) Fine hiogenic dolomite facies.

2) Sandy rich dolomite facies.

3) Dolomite diagenetic facies.

4) Recrystal1ized wackestone in microfacies.

5) Mudsione facies.

Microfacics reflect shallow marine water with open Circulation in the lower part of the formation and the environment of the upper is enclosed between upper tide and tide. The most important diagenesis was recrystallization and spary calcite deposit inside fossils chambers and pores.

View Publication Preview PDF
Publication Date
Sun Dec 01 2013
Journal Name
Political Sciences Journal
International and domestic political conflicts in south Yemen1869-1918
...Show More Authors

In the South of yement, when the accupation of Aden in 1839 by the British, British politics has proceeded in accordance with interests in promoting the existence and exploitation of this important site to implement their interests. Historians believe that Britain played a major role in the conflicts that have taken place on the land of Yemen, through a series of military and political dealings between them and the Ottoman Empire prior to withdrawal of Yemen and between local authorities and power to Yemen, such interactions have led to very serious consequences for the future of Yemen and Yemen was often divided into three parts, the northern areas under the authority of Imam Yahya, and the South, under the control of Britain, Asir and

... Show More
View Publication Preview PDF
Crossref
Publication Date
Fri Jan 01 2021
Journal Name
E3s Web Of Conferences
Behavioral Investigation of Reinforced Concrete T-Beams with Distributed Reinforcement in the Tension Flange
...Show More Authors

Current design codes and specifications allow for part of the bonded flexure tension reinforcement to be distributed over an effective flange width when the T-beams' flanges are in tension. This study presents an experimental and numerical investigation on the reinforced concrete flanged section's flexural behavior when reinforcement in the tension flange is laterally distributed. To achieve the goals of the study, numerical analysis using the finite element method was conducted on discretized flanged beam models validated via experimentally tested T-beam specimen. Parametric study was performed to investigate the effect of different parameters on the T-beams flexural behavior. The study revealed that a significant reduction in the

... Show More
View Publication
Scopus (3)
Crossref (3)
Scopus Crossref
Publication Date
Sun Jun 11 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Evaluation of Mechanical Strength of Epoxy Polymer Concrete Reinforcement with Different Types of Fibers
...Show More Authors

 Polymer composite materials were prepared by mixing epoxy resin with sand particles in three different grain size (150-300 ), (300-600 ) and (600- 1200) μm . The weight of epoxy was 15%, 20%, 25% and 30% of the total weight. Compression  strength and flexural strength tests were carried out for the prepared samples .The percentages of epoxy resin at 20% wt and 25% wt showed best mechanical properties for all grain sizes .These percentages were adopted to fill the void between particles sand which have two different size ranges (150-600) μm and {(150-300) & (600-1200)} μm respectively to obtain more dense material. The results showed that the strength of polymer composite at 20% resin is higher than 25% resin. The

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sat Dec 01 2012
Journal Name
Journal Of Engineering
Database for Baghdad Soil Using GIS Techniques
...Show More Authors

teen sites Baghdad are made. The sites are divided into two groups, one in Karkh and the other in Rusafa. Assessing the underground conditions can be occurred by drilling vertical holes called exploratory boring into the ground, obtaining soil (disturbed and undisturbed) samples, and testing these samples in a laboratory (civil engineering laboratory /University of Baghdad). From disturbed, the tests involved the grain size analysis and then classified the soil, Atterberg limit, chemical test (organic content, sulphate content, gypsum content and chloride content). From undisturbed samples, the test involved the consolidation test (from this test, the following parameters can be obtained: initial void ratio eo, compression index cc, swel

... Show More
View Publication Preview PDF
Crossref (6)
Crossref
Publication Date
Mon Mar 15 2021
Journal Name
Journal Of Baghdad College Of Dentistry
Comparison between the mesiodistal crown dimensions of second primary molar with stainless steel crowns from different companies
...Show More Authors

Background: Due to the variations in tooth anatomy and size among different populations, this study aimed to compare the mesiodistal width of primary second molars in Iraqi children with the mesiodistal width of stainless-steel crowns from different companies. Materials and Methods: This cross-sectional study was conducted on 220 intact maxillary and mandibular primary second molars selected from boys and girls’ Iraqi children aged 8-9 years collected from different primary schools in Baghdad city. The mesiodistal dimensions of the selected teeth and the available maxillary and mandibular stainless-steel crowns from three different companies were measured by using a 3-D scanner, and then the whole measurements were calculated usin

... Show More
View Publication Preview PDF
Scopus Crossref
Publication Date
Sun Dec 09 2018
Journal Name
Baghdad Science Journal
Anticorrosion Behavior of Deposited Magnetite on Galvanized Steel in Saline Water Using RF-Magnetron Sputtering
...Show More Authors

Thin films of Magnetite have been deposited on Galvanized Steel (G-S) alloy using RF-reactive magnetron sputtering technique and protection efficiency of the corrosion of G-S. A Three-Electrodes Cell was used in saline water (3.5 % NaCl) solution at different temperatures (298, 308, 318 & 328K) using potentiostatic techniques with. Electrochemical Impedance Spectroscopy (EIS) and fitting impedance data via Frequency Response Analysis (FRA) were applied to G-S alloy with Fe3O4 and tested in 3.5 % NaCl solution at 298K.Results taken from Nyquist and Bode plots were analyzed using software provided with the instrument. The results obtained show that the rate of corrosion of G.S alloy increased with increasing the temperatures from 298 t

... Show More
View Publication Preview PDF
Scopus Clarivate Crossref
Publication Date
Wed Dec 01 2010
Journal Name
Al-khwarizmi Engineering Journal
Improvement of Surface Roughness Quality for Stainless Steel 420 Plate Using Magnetic Abrasive Finishing Method
...Show More Authors

     An experimental study was carried out to improve the surface roughness quality of the stainless steel 420 using magnetic abrasive finishing method (MAF). Four independent operation parameters were studied (working gap, coil current, feed rate, and table stroke), and their effects on the MAF process were introduced. A rotating coil electromagnet was designed and implemented to use with plane surfaces. The magnetic abrasive powder used was formed from 33%Fe and 67% Quartz of (250µm mesh size). The lubricant type SAE 20W was used as a binder for the powder contents. Taguchi method was used for designing the experiments and the optimal values of the selected parameters were found. An empirical equation representing the r

... Show More
View Publication Preview PDF
Publication Date
Sun Feb 03 2019
Journal Name
Journal Of The College Of Education For Women
Improvement of the surface hardness and wear resistant of low carbon steel using laser radiation
...Show More Authors

0

View Publication Preview PDF