Pyrolysis of high density polyethylene (HDPE) was carried out in a 750 cm3 stainless steel autoclave reactor, with temperature ranging from 470 to 495° C and reaction times up to 90 minute. The influence of the operating conditions on the component yields was studied. It was found that the optimum cracking condition for HDPE that maximized the oil yield to 70 wt. % was 480°C and 20 minutes. The results show that for higher cracking temperature, and longer reaction times there was higher production of gas and coke. Furthermore, higher temperature increases the aromatics and produce lighter oil with lower viscosity.

The loose sand is subject to large settlement when it is exposed to high stresses. This settlement is due to the nature of the high drainage of sand, which displays foundations and constructions to a large danger. The densification of loose sandy soils is required to provide sufficient bearing capacity for the structures. Thus soil stabilization is used to avoid failure in the facilities. Traditional methods of stabilized sandy soil such as fly ash, bituminous, and cement often require an extended curing period. The use of polymers to stabilize sandy soils is more extensive nowadays because it does not require a long curing time in addition to being chemically stable. In this study, the effect of adding different percent

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

In this study, iron was coupled with copper to form a bimetallic compound through a biosynthetic method, which was then used as a catalyst in the Fenton-like processes for removing direct Blue 15 dye (DB15) from aqueous solution. Characterization techniques were applied on the resultant nanoparticles such as SEM, BET, EDAX, FT-IR, XRD, and zeta potential. Specifically, the rounded and shaped as spherical nanoparticles were found for green synthesized iron/copper nanoparticles (G-Fe/Cu NPs) with the size ranging from 32-59 nm, and the surface area was 4.452 m2/g. The effect of different experimental factors was studied in both batch and continuous experiments. These factors were H2O2 concentration, G-Fe/CuNPs amount, pH, initial DB15

     This study observed the formation of struvite crystals in wastewater using natural zeolite activated with Mg²⁺ ions. Mg²⁺ ions released from natural zeolite would react with PO₄^3- and NH₄⁺ ions from in wastewater to form struvite crystals. The results showed that at pH 8.5, the removal of PO₄^3- and NH₄⁺ ions was more effective using the modified zeolite than the natural zeolite. Adding 40 g/L Zeo-Mg (1) produced the best results, with PO4^3- (93.32%) and NH₄ (40%) adsorption. Meanwhile, 40g/L Zeo-Mg (2) adsorbed 81% PO₄^3- ions and 27.12% NH₄⁺ ions. The eqil

Abstract

 Nano-crystalline ZSM-5 zeolite was synthesized by hydrothermal method using chelating agent and two gel compositions:Compositionɪ:Al₂O₃:86SiO₂:5.5TPA:12.7Na₂O:3.4Trien:3320H₂O.Compositionɪɪ:Al₂O₃:68SiO₂:5.4TPA:10Na₂O:2.6Trien:2626H₂O.Study of hydrothermal reaction factors on characteristics of nano- sized zsm-5 has been carried on ,among them are crystallization temperature, crystallization time and concentration of template ( TPAOH ) solution. Synthesis was accomplished in PTFE lined autoclave ( reactor ) . The product were characterized by X-ray diffraction ( XRD ),Atomic force microsc

     In this study, wax worm larvae (Galleria mellonella) were used to examine their ability to degrade and assimilate polyethylene (PE) as an energy source. This idea came from the similarity of wax, that is used as the sole diet for larvae, with PE in composition. Morphology changes, weight loss, FTIR analysis and GC-Mass test were studied to prove the degradation of PE by G. mellonella. The maximum depth of holes on the plastic surface and 16% PE weight loss was due to extensive cutting. The creation of a novel O-H stretching alcohols/phenols group absorbance peak at 3293cm^-1 observed in wax worm larvae PE frass samples may be due to the oxidation in their gut. Accordingly, the biodegradation of PE by

  A dynamic experimental study of thermal decomposition of low density polyethylene has been carried out with two different heating rates  .As usual , we can determine the activation energy of any polymer using( 3 - 6 ) TGA experiment as minimum , but  in  this work , we estimate the activation energy of  LDPE  using two of  TGA  experiments only