Double hydrothermal method was used to prepare nano gamma alumina using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, CTAB (cetyltrimethylammonium bromide) as surfactant, and variable acids: weak acids like; citric, and acitic acids, and strong acids like; hydrochloric and nitric acids as a bridge between aluminum salts and surfactant. Different crystallization times 12, 24, 48, and 72 hrs were applied. All the batches were prepared at pH equals to 9. XRD diffraction technique was used to investigate the crystalline nano gamma alumina pure from surfactant. N2 adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the average particle size and the morphology of the surface of nano gamma alumina were estimated using AFM and SEM techniques, respectively. The sharpness of the peaks increased with increasing of crystallization time. The surface area, pore volume, and average particle size were decreased with increasing crystallization time. The best result of surface area was 383 m2/gm obtained using citric acid at 12 hr crystallization time, while the best results of pore volume and average particle size were 0.54cm3/gm and 72.37nm obtained using hydrochloric acid at12 hr crystallization time. Low agglomeration with hexagonal structure obtained using weak acids, while agglomeration occurred and clusters formed using strong acids.
A theoretical calculation of the reorganization energies is demonstrated for semiconductor (TiOâ‚‚, ZnO) and organic dye (safranine T, and coumarin) with a variety solvent such that (water, 1Âpropanol, Formamide, Acetonitrile and Ethanol). The reorganization energy values for dye –semiconductor interface system are large in high polar solvent (water 741 .0 ï¬ , Acetonitrile 708 .0 ï¬ , Ethanol 669 .0 ï¬ ) and small in low polar solvent(1Âpropanol 635 .0 ï¬ . The reorganization energy in safranine T –semiconductor system is larger ( 635 741.0 ï€ )than in coumarin –semiconductor for with the same solvents ( 612
... Show MoreHydrogen peroxide was determined by a new , accurate , sensitive and rapid method via continuous mode of FIA coupled with total luminescence measurement which include the chemiluminescence generated ,based on the oxidation of Luminol which is loaded on poly acrylic acid gel beads by hydrogen peroxide in presence of Cobalt (II) ion as a chemiluminescence catalyst and the fluorescence that was created by the insitu radiation of the released chemiluminescence light. Fluorescien molecule was used as an accepter fluorophore where it is irradiated internally and instantly by the generation of luminol chemiluminescence light as internal source for irradiation of fluorescien molecule (Fluorescence Energy Transfer (FRET) ) . It can easily give fl
... Show MoreIn this paper, we used two monomers, 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA) and m,m'-diaminobenzophenone (m, m’-DABP), to produce polyamide acid and then converted it to polyimide (PI). The effects of phosphoric acid (H3PO4) molarity (1, 2, and 3 M) on the structural, thermal, mechanical, and electrical characteristics of the polyimides/polyaniline (PI/PANI) nanocomposites were studied. Two sharp reflection peaks were developed by the addition of PANI to PI. When 3 M H3PO4 is added, the crystalline sharp peak loses some of its intensity. The complex formation of PI/PANI-H3PO4 was confi
... Show More
(11)
(9)
The present study investigated the impact of fuel kind on the emitted emissions at the idling period. Three types of available fuels in Iraq were tested. The tests conducted on ordinary gasoline with an octane number of 82, premium gasoline with an octane number of 92, and M20 (consist of 20% methanol and 80% regular gasoline). The 2 liters Mercedes-Benz engine was used in the experiments.
The results showed that engine operation at idle speed emits high levels of CO, CO2, HC, NOx and noise. The produced emission levels depend highly on fuel type. The premium gasoline (ON=92) represents the lower emissions level except for noise at all idling speed. Adding methanol to ordinary gasoline (ON=82) showed high levels of emi
... Show More
(2)
A non-destructive assay (NDA) for radioactive waste drum has been studied
using a local manufacturing gamma scanning system. The gamma system has been
designed and implemented using scanning system contains a high efficiency
portable HPGe detector for characterization and surveying the radioactive waste
drums at Al-Tuwaitha site- Baghdad. To achieve identification with nonhomogenous
radioactive waste drum, six parallel plastic pipes (2cm in diameter)
were inserted inside the cement type Portland contain radioactive sources and
located at different distances from the outer diameter of the drum. The efficiency
calibration is measured by conventional technique, using five miscellaneous radio
nuclides with drum. Th
Nano γ-Al2O3 support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) oC. Then nano NiMo/γ-Al2O3 catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al2O3 support at calcination temperature 550 oC. Make the characterizations for prepared nano γ-Al2O3 support at different temperatures and for nano NiMo/γ-Al2O3 catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.
The N
... Show MoreBackground: Dental implant considers a unique treatment option for the replacement of missing dentition. The new trend of implants is looking for materials which accelerate bone formation in bone implant interface and enhance osseointegration to provide immediate loading directly after placement and decrease the time period which is disturbs patients and uncomfortable. The aim of the study was to evaluate the effect of nano zirconium oxide (ZrO2) and nano hydroxyapatite (Hap) mixture coating of screw shaped commercially pure titanium (cpTi) implants on bond strength at the bone implant interface with torque removal test and histological analysis in comparison with non coated implants. Materials and methods: Forty screws were machined from c
... Show More
(3)
The present paper is an experimental study to improve the productivity of the conventional solar still. This done by modifying conventional still in a way that the distilled basin is larger than distillation basin, thus providing an increase in the condensation surface and speeding up the condensation process. Moreover, increase in the dimensions of the distilled base helps coupling reflective panels to the distilled base to reflect incident solar radiation to the distillation basin. For this purpose , two solar stills were made, one conventional designand another made according to the proposed design. The two solar stills were tested during the period from February to July 2009 under varying weather conditions of Basra, Iraq (latitude o
... Show MoreBackground: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirement. The purpose of this study was to evaluate the effect of addition of 3% wt of treated (silanized) Titanium oxide Nano filler on some physical and mechanical properties of heat cured acrylic denture base material. Materials and methods: 100 specimens were constructed, 50 specimens were prepared from heat cure PMMA without additives (control) and 50 specimens were prepared from heat cure PMMA with the addition of TiO2 Nano fillers. Each group was divided into 5 sub groups according to the test performed which was mixed by probe ultra-sonication machine. Results: A highly
... Show More