In this research, the performance of asphalt mixtures modified with polyethylene polymer (PE) by adding 2%, 4%, and 6% percentages was evaluated. Two kinds of PE are employed: Low-Density PE (LDPE) and High-Density PE (HDPE). The semi-wet mixing technique (SWM) was conducted to avoid stability issue for PE-modified binder during storage condition. Many experimental tests were conducted to evaluate the ability of these mixtures to withstand the effects of loads and moisture. The hardness index of these mixtures was also measured to determine their resistance to the effects of high temperatures without causing permanent deformations. The results showed that adding PE led to a remarkable enhancement in the performance of PE-modified mixtures.

When dye is present in wastewater, it is considered a hazardous organic pollutant and must be eliminated. The goal of the current study was to evaluate the elimination of Malachite green (MG) and Methyl violet (MV) dyes using Ni foam (NiF) as an anode, along with stainless steel mesh electrodes as cathodes, and alum sludge (AS) as a third particle electrode in a three-dimensional electrocoagulation-flotation system (3DECF). With an electrolysis period of 30 minutes and pH = 7, response surface method was used to estimate the optimum conditions of studied parameters. These parameters were current density within the range of 1–5 mA/cm², concentration of NaCl within the range of 0.4 –1 g/L, and air flow rate within a range of 1–5 L/min.

Complexes of 1-phenyl-3-(2(-5-(phenyl amino)-1,3,4-thiadiazole-2-yl)phenyl) thiourea have been prepared and characteizedby elemental analysis, Ff-[R, and u.v./ visible spectra moreover,determination of metal content M%o by flame atomic absorptionspectroscopy, molar conductance in DMSO solution and magneticmoments (peffl.The result showed that the ligand (L) was coordinated to Mn+2, Ni+2,Ct+2,2n+2,Cd+2, and Hg+2 ions through the nitrogen atoms and sulpheratoms.From the result obtained, rhe following general formula [MLCl2] hasbeen given for the prepared complexes with an octahedral geometryaround the metal ions for all complexes.where M= Mn+2, Ni+2, cu+2, zn+2, cd+2, and Hg+2 l= l-phenyl-3-(2-(5-(phenyl amino

Spray pyrolysis technique was used to make Carbon60-Zinc oxide (C60-ZnO) thin films, and chemical, structural, antibacterial, and optical characterizations regarding such nanocomposite have been done prior to and following treatment. Fullerene peaks in C60-ZnO thin films are identical and appear at the same angles. Following the treatment of the plasma, the existence regarding fullerene peaks in the thin films investigated suggests that the crystallographic quality related to C60-ZnO thin films has enhanced. Following plasma treatment, field emission scanning electron microscopy (FESEM) images regarding a C60-ZnO thin film indicate that both zinc oxide and fullerene particles had shrunk in the size and have an even distribution. In addition

This study was conducted at the field of poultry-Abu Gharib/department of Animal Production/college of agricultural engineering Sciences-university of Baghdad, during the period from 12/10/2019 to 24/11/2019 duration (42 days), to demonstrate the effect of adding different levels of Allicin to broiler diet on Glutathione level in blood and histological of thymus gland, total of 225 Ross 308 chicks was used. Birds were randomly distributed into five treatment groups which were: First treatment T1: without additives to diet (control), other treatments T2, T3, T4, T5 was added Allicin at a rate of (800,600,400,200 mg/Kg diet) respectively, and Allicin was added from first day until the end of the experiment for all addition treatments, results

Background: this study aimed to evaluate the effect of addition of hydroxyapatite micro filler in three concentrations (5%, 10%, 15%) on surface roughness, impact strength, flexural strength and hardness. Material and methods: One hundred sixty acrylic samples were used in this study,40 samples were used for each test(impact strength ,flexural strength ,hardness and surface roughness).The test group divided into four subgroups(n=10) for controlgroup,5%,10% ,15%H,A.concentration addition groups .Impact testing device, flexural strength testing device, shore hardness tester and profilometer device were used to measure the four tests examined in this study. Results: the results showed a significant increase in impact strength, hardness in all

New azo ligand 2-((4-formyl-3-hydroxynaphthalen-2-yl) diazenyl) benzoic acid (H2L) was synthesized from the reaction of 2-aminobenzoic acid and2-hydroxy-1-naphthaldehyde. Monomeric complexes of this ligand, of general formulae [MII(L)(H2O)] with (MII = Mn, Co, Ni, Cu, Zn, Pd, Cd and Hg ) were reported. The compounds were isolated and characterized in solid state by using 1H-NMR, FT-IR, UV–Vis and mass spectral studies, elemental microanalysis, metal content, magnetic moment measurements, molar conductance and chloride containing. These studies revealed tetrahedral geometries for all complexes except PdII complex is Square planar. The study of complexes formation via molar ratio of (M:L) as (1:1). Theoretical treatments of compounds in gas

In this research ,Undoped Nio and 1%Li doped Nio thin films were deposited utilizing chemical spray pyrolysis on the glass substrates heated (450C). The effects of non-thermal plasma on the structural and optical properties were studied. XRD measurement shows that Nio and Nio:1%Li films were found to be polycrystalline and have cubic structure with a preferred orientation (111). Decreased crystal size after exposure especially at (7) sec. AFM data indicate that the surface roughness average and (RMS) values of the prepared doped films are increasing after exposure to plasma, the transmittance increases after doped samples exposure to plasma, it was found that the energy gap value decreased when doped samples exposure to plasma, also, thickn

Tin dioxide doped silver oxide thin films with different x content (0, 0.03, 0.05, 0.07) have been prepared by pulse laser deposition technique (PLD) at room temperatures (RT). The effect of doping concentration on the structural and electrical properties of the films were studied. Atomic Force Measurement (AFM) measurements found that the average value of grain size for all films at RT decrease with increasing of AgO content. While an average roughness values increase with increasing x content. The electrical properties of these films were studied with different x content. The D.C conductivity for all films increases with increasing x content. Also, it found that activation energies decrease with increasing of AgO content for all films.