Oxidative Desulfurization of Simulated Diesel Fuel by Synthesized Tin Oxide Nano-Catalysts Support on Reduced Graphene Oxide
...Show More Authors

   The modified Hummers method was applied to prepare graphene oxide (GO) from the graphite powder. Tin oxide nanoparticles with different loading (10-20 wt.%) supported on reduced graphene oxide were synthesized to evaluate the oxidative desulfurization efficiency. The catalyst was synthesized by the incipient wetness impregnation (IWI) technique. Different analysis methods like FT-IR, XRD, FESEM, AFM, and Brunauer-Emmett-Teller (BET) were utilized to characterize graphene oxide and catalysts. The XRD analysis showed that the average crystal size of graphene oxide was 6.05 nm. In addition, the FESEM results showed high metal oxide dispersions on the rGO. The EDX analysis shows the weight ratio of Sn is close to its theoretical weight. The reduction of metal oxide and (GO) has occurred in one step at temperatures of 400 °C for 2 hours. The performance of the catalysts for dibenzothiophene (DBT) removal using H2O2 as an oxidizing agent was determined under a range of different operating conditions. The results showed that the maximum desulfurization was 71.68% in the best conditions (DBT concentration = 385 ppm, time = 90 min, temperature = 60 oC, catalyst dosage = 0.04g, and amount of oxidant = 0.375 ml).

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Fri Apr 01 2022
Journal Name
Journal Of Engineering
Improvement of Diesel Fuel Engine Performance by Nanoparticles Additives
...Show More Authors

This study was done to investigate the impact of different nanoparticles on diesel fuel characteristics, Iraqi diesel fuel was supplied from al-Dura refinery and was treated to enhance performance by improving its characteristics. Two types of nanoparticles were mixed with Iraqi diesel fuel at various weight fractions of 30, 60, 90, and 120 ppm. The diesel engine was tested and run at a constant speed of 1600 rpm to examine and evaluate the engine's performance and determine emissions. In general, ZnO additives' performance analysis showed they are more efficient for diesel fuel engines than CeO. The performance of engine diesel fuel tests showed that the weight fraction of nanoparticles at 90 and 120 ppm give a similar performance,

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Fri Apr 01 2022
Journal Name
Journal Of Engineering
Improvement of Diesel Fuel Engine Performance by Nanoparticles Additives
...Show More Authors

This study was done to investigate the impact of different nanoparticles on diesel fuel characteristics, Iraqi diesel fuel was supplied from al-Dura refinery and was treated to enhance performance by improving its characteristics. Two types of nanoparticles were mixed with Iraqi diesel fuel at various weight fractions of 30, 60, 90, and 120 ppm. The diesel engine was tested and run at a constant speed of 1600 rpm to examine and evaluate the engine's performance and determine emissions. In general, ZnO additives' performance analysis showed they are more efficient for diesel fuel engines than CeO. The performance of engine diesel fuel tests showed that the weight fraction of nanoparticles at 90 and 120 ppm give a similar

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sat Mar 01 2008
Journal Name
Iraqi Journal Of Physics
The effect of Aluminum Oxide, Iron Oxide on the thermal conductivity of (Epoxy-Aluminum Oxide, Epoxy-Iron Oxide) Composites
...Show More Authors

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3

View Publication Preview PDF
Publication Date
Thu Jun 30 2022
Journal Name
International Journal Of Drug Delivery Technology
Synthesized Zinc Oxide Nanoparticles by The Precipitation Method on Streptococcus Spp From Dental Carries and Cytotoxicity Assay
...Show More Authors

In this article the nanoparticles synthesis of ZnO (Nps) by using the precipitation method at concentrations range (0.5, 0.25, 0.125, 0.0625, 0.03125) mg/mL and then activity was examined against Streptococcus spp that causing dental caries in vitro by well diffusion method, find these concentrations effected in these bacteria and better concentration is 0.03125. ZnO Nps were characterization by EDS to prove this particles are ZnO, and also characterized by atomic force microscope (AFM), X-ray Diffraction (XRD) and TEM, from these technic found that the average size about 30.52 nm and hexagonal shape. The UV-visible result reveals that the large band is observed at 340.8 nm, Zeta potential show that the surface charge is 30.19 mv an

... Show More
View Publication Preview PDF
Scopus (1)
Scopus Crossref
Publication Date
Thu Dec 23 2021
Journal Name
Iraqi Journal Of Science
The Effect of Nano-Zinc Oxide and Nano-Titanium Dioxide on Inhabitation of Ochratoxin A
...Show More Authors

    The experiment was conducted at the Agricultural Research Office in Baghdad during July 2020 to test the ability of nanomaterials (ZnO and TiO2) to inhibit  ochratoxin A, which is produced by a number of microbiology (fungi) including: Aspergillus ochraceus, A. niger, ,A. steynii, A. carbonarius,  Pencillume verrucosum and P. nordicum. The standard ochratoxin A, with known concentration, was treated with different concentrations of nanomaterials  (20, 40, 60, and 80 ppm) and two different particle sizes of nanoparticles approximately (15 nm) and (70 nm) for each (ZnO) and TiO2; with 16 transactions. Through an examination of the HPLC, the results showed that all tra

... Show More
View Publication Preview PDF
Scopus (1)
Crossref (1)
Scopus Crossref
Publication Date
Tue Nov 01 2016
Journal Name
Materials Science Forum
Study the Effect of Liquid Layer Level on the Formation of Zinc Oxide Nanoparticles Synthesized by Liquid-Phase Pulsed Laser Ablation
...Show More Authors

This work is focused on studying the effect of liquid layer level (height above a target material) on zinc oxide nanoparticles (ZnO and ZnO2) production using liquid-phase pulsed laser ablation (LP-PLA) technique. A plate of Zn metal inside different heights of an aqueous environment of cetyl trimethyl ammonium bromide (CTAB) with molarity (10-3 M) was irradiated with femtosecond pulses. The effect of liquid layer height on the optical properties and structure of ZnO was studied and characterized through UV-visible absorption test at three peaks at 213 nm, 216 nm and 218 nm for three liquid heights 4, 6 and 8 mm respectively. The obtained results of UV–visible spectra test show a blue shift accomp

... Show More
View Publication Preview PDF
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Fri Sep 17 2021
Journal Name
Canadian Journal Of Physics
Synthesis, characterization, photoluminescence, and antibacterial activities of silica-graphene oxide composites
...Show More Authors

In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO2 nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in turn confirmed the formation of Si

... Show More
Preview PDF
Publication Date
Wed Dec 01 2021
Journal Name
Canadian Journal Of Physics
Synthesis, characterization, photoluminescence, and antibacterial activities of silica-graphene oxide composites
...Show More Authors

In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO2 nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in tur

... Show More
View Publication
Scopus (2)
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Sun Mar 01 2020
Journal Name
Iop Conference Series: Materials Science And Engineering
Characterization of nickel oxide nanocatalyst electrodes for an alkaline fuel cell
...Show More Authors
Abstract<p>In this paper had been studied the characterization of the nanocatalyst (NiO) Mesh electrodes. For fuel cell. The catalyst is prepared and also the electrodes The structural were studied through the analysis of X-ray diffraction of the prepared nanocatalyst for determining the yielding phase and atomic force microscope to identify the roughness of prepared catalyst surface, Use has been nanocatalyst led to optimization of cell voltage, current densities & power for a fuel cell.</p>
View Publication
Scopus (2)
Crossref (1)
Scopus Crossref
Publication Date
Tue Feb 12 2019
Journal Name
Iraqi Journal Of Physics
Laser wavelength and energy effect on optical and structure properties for nano titanium oxide prepared by pulsed laser deposit
...Show More Authors

Nano TiO2 thin films on glass substrates were prepared at a constant temperature of (373 K) and base vacuum (10-3 mbar), by pulsed laser deposition (PLD) using Nd:YAG laser at 1064 nm wavelength. The effects of different laser energies between (700-1000)mJ on the properties of TiO2 films was investigated. TiO2 thin films were characterized by X-ray diffraction (XRD) measurements have shown that the polycrystalline TiO2 prepared at laser energy 1000 mJ. Preparation also includes optical transmittance and absorption measurements as well as measuring the uniformity of the surface of these films. Optimum parameters have been identified for the growth of high-quality TiO2 films

... Show More
View Publication Preview PDF
Crossref (3)
Crossref