This work is focused on studying the effect of liquid layer level (height above a target material) on zinc oxide nanoparticles (ZnO and ZnO2) production using liquid-phase pulsed laser ablation (LP-PLA) technique. A plate of Zn metal inside different heights of an aqueous environment of cetyl trimethyl ammonium bromide (CTAB) with molarity (10-3 M) was irradiated with femtosecond pulses. The effect of liquid layer height on the optical properties and structure of ZnO was studied and characterized through UV-visible absorption test at three peaks at 213 nm, 216 nm and 218 nm for three liquid heights 4, 6 and 8 mm respectively. The obtained results of UV–visible spectra test show a blue shift accompanied with decreasing the liquid level above the target due to the increase in ablation rate and particles production. This blue shift indicates getting a smaller size of nanoparticles and the quantum confinement property of nanoparticles. Also the FTIR transmittance spectra of ZnO2 nanoparticles prepared in these states show a characteristic ZnO absorption at 435 cm−1 – 445 cm-1.
The performance and lifetime of the flexible asphalt pavement are mainly dependent on the interfacial bond strength between layer courses. To enhance the bond between layers, adhesive materials, such as tack coats, are used. The tack coat itself is a bituminous material, which is applied on an existing relatively non-absorbent surface to ensure a strong bond between the old and newly paved layer. The primary objective of this study was to evaluate the effects of various types of tack coat materials on interlayer bond strength and to determine the optimal application rate for each type. The tack coat types used in this paper were RC-70, RC-250, and CSS-1h. Both laboratory-prepared and field-constructed hot mix asphalt concrete pavements usin
... Show MoreIn this paper, we calculate the electron energy distribution function (EEDF) and transport parameters including the electron mean energy, mobility, drift velocity and diffusion coefficient for the gas mixtures of the H2 and N2 using the EEDF program. It is concentrated on the effect of assorted concentrations of the mixtures on the EEDF and the electron transport coefficients. The work exhibits the variation amongst the different mixtures on the EEDF and the transport parameter. The results are graphically offered and discussed. In this concept, it is shown that for each mixture has a specific impact on EEDF and the transport parameter. The important of this study comes from the usage of these mix
... Show MoreKlebseilla pneumoniae possesses many virulence factors and survival strategies to persist and overcome host defenses; one of these strategies is biofilm formation. Therefore, the aims of this study was to determine the antibacterial and antibiofilm effect of Rosmarinus officinelis L. essential oil (EO) and its effect on the genes encoding of fimbrial adhesions. The antimicrobial activity was investigated by MIC. The ability to form biofilm as well as inhibition of initial cell attachment and biofilm formation was performed. PCR was carried out to detect fimH-1 and mrkD genes of type 1 and type 3 fimbrial adhesions at different time of incubation. The study revealed that MIC value of EO was 104 μg/ml on 24 (83%) of isolates, 93% of them
... Show MoreIn the region of the north of Iraq using the method of analyzing thin section microfacies to 38 of rockyslices which were gathered from a place near Aqra city. These slides are divided into seven microfacies depending on lithologcal component and fossils.
1) Dolostone facies.
2)Recrystallized bioclastic wackestone facies.
3) Bioclastic packstone microfacies
4)Sucrosic dolomite facies.
5) Bioclastic grainstone in microfacies.
According to water energy, these facies were divided to three zone:
- a) Low energy environment.
- b) Transitional zone.
- c) High energy environment.
In this research, the results of the Integral breadth method were used to analyze the X-ray lines to determine the crystallite size and lattice strain of the zirconium oxide nanoparticles and the value of the crystal size was equal to (8.2nm) and the lattice strain (0.001955), and then the results were compared with three other methods, which are the Scherer and Scherer dynamical diffraction theory and two formulas of the Scherer and Wilson method.the results were as followsScherer crystallite size(7.4nm)and lattice strain(0.011968),Schererdynamic method crystallite size(7.5 nm),Scherrer and Wilson methodcrystallite size( 8.5nm) and lattice strain( 0.001919).And using another formula for Schearer and Wilson methodwe obtain the size of the c
... Show MoreThe corrosion of carbon steel in single phase (water with 0.1N NaCl ) and two immiscible phases (kerosene-water) using turbulently agitated system is investigated. The experiments are carried out for Reynolds number (Re) range of 38000 to 95000 corresponding to rotational velocities from 600 to 1400 rpm using circular disk turbine agitator at 40 0C. In two-phase system test runs are carried out in aqueous phase (water) concentrations of 1 % vol., 5 % vol., 8% vol., and 16% vol. mixed with kerosene at various Re. The effect of Reynolds number (Re), percent of dispersed phase, dispersed drops diameter, and number of drops per unit volume on the corrosion rate is investigated and discussed. Test runs are carried out using two types of
... Show MoreIn this work, new Schiff bases of quinazolinone derivatives (Q1-Q5) were synthesized from methyl anthranilate. The synthesis involved three steps. In the first step, methyl anthranilate was reacted with isothiocyanatobenzene, producing the thiourea derivative K1. The second step entailed reacting K1 with hydrazine hydrate, synthesizing 3-amino-2-(phenylamino) quinazolin-4(3H)-one (K2). The third step involved reaction of K2 with various aromatic aldehydes, yielding the Schiff bases derivatives Q1-Q5. The chemical structures of these compounds were identified by FT-IR,1H NMR and 13C NMR spectroscopy. The newly synthesized derivatives (Q1-Q5) were subjected to rigorous evaluation to assess their efficacy as corrosion inhibitors for ca
... Show MoreIn this work, lead oxide (PbO) thin films were deposited using D.C. sputtering method on a surface of glass substrates and then thermally annealed at a temperature of 473K with annealing times of (1,2 and 3) hours. The structural, morphological, and optical properties of films were determined using X-ray diffraction (XRD), atomic force microscopy (AFM), FT-IR, and UV-Visible spectroscopy. The structure studies confirmed that PbO films are polycrystalline structures in an orthorhombic phase with average grain size (24.51, 29.64, 46.49, 16) nm with increasing annealing time. From AFM, the roughness of the film surface (3.26, 1.76, 1.61, 1.79) nm as the film annealing time increases. The optical band gap values of the PbO thin fi