Two different composite materials were prepared by stir casting method of AA 6061 alloy as a matrix reinforced with two addition different ceramic materials Al₂O₃ and B₄C of grain size   20 µm by 2.5, 5, 7.5 and10% in weight. The composite material with aluminum alloy as a matrix possesses a unique mechanical properties such as: high specific strength and hardness, low density, and high resistance to corrosion and friction wear. This composite is widely used in automotive parts space and marine applications.

Pin-on-disc technique was used to calculate the wear rate for each addition of Al₂O₃ and B₄C particles. Rockwell hardness test and

The determiner phrase is a syntactic category that appears inside the noun phrase and makes it definite or indefinite or quantifies it. The present study has found wide parametric differences between the English and Arabic determiner phrases in terms of the inflectional features, the syntactic distribution of determiners and the word order of the determiner phrase itself. In English, the determiner phrase generally precedes the head noun or its premodifying adjectival phrase, with very few exceptions where some determiners may appear after the head noun. In Arabic, parts of the determiner phrase precede the head noun and parts of it must appear after the head noun or after its postmodifying adjectival phrase creating a discontinu

Background: Developing Goalkeeper’s performance is imperative to defence the goal. As the Football match’s nature needs implementning the skill with strength, and speed. so, the Goalkeeper demands special physical abilities that enabling him the ball blocking skill masterly. Objetive: The study aimed to identify the effect of developing some special physical abilities on the goalkeeper’s performance level while blocking executed balls from the penalty mark in football using plyometric training. Methodology: The experimental approach (continuous training that divided into two phases: General preparation, and Special preparation stage) was adopted for one experimental group by pre/post-measurements. The research sample was delib

Thirty swabes of medical implants were collected from Al-Yarmouk's hospital which were cultured on manitole agar to isolate Staphelococcus aureus . Only four samples gave positive results with this media. It was used ten types of antibiotics to test the sensitivity of this bacterium against them. All isolates of S. aureus were recorded as multidrug resistant and were considered as MRSA. One pledge alternative therapy is the utilize of certain pure bacterocin MIC (32.5 to 62.5 μg/ml) and it was compared with vancomycin (200-400 μg/ml) with average of (8 – 15) mm diameter of inhibition zones recpectively. The first reduction of biofilm formation ability has been proved in catheters when treatedby pure bacterocin. The test shows the highes

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: The aim of this in vitro study was to evaluate and compare the effect of preheating microleakage among three different filler size composites which include Filtek^tm Z250 micro hybrid, Z250^xt Nano hybrid and nanocomposite Z350^xt.  in Class II cavity preparation .

Materials and methods: sixty maxillary first premolars were prepared with class II cavities. Samples were divided into three groups according to material used    group A (FiltekZ250 micro hybrid). Group B(Z250^xt Nano hybrid). Group C (nanocomposite Z350^xt)and each group divided into two subgroups of ten teeth according to temperature of  composite: