The isomerization of n-hexane on platinum loaded acidic zeolite was studied at atmospheric pressure, H2/nC6 molar ratios of 1-4 and temperature range of 240-270ºC. The measured kinetic data were fitted to an equation based on the bifunctional mechanism and by using independently obtained dehydrogenation and adsorption data. The activation energies of protonation (ΔHpro) and the elementary isomerization step (Eact,iso) and as well as the corresponding preexponential factor were simultaneously determined. The observed values of both ΔHpro and Eact,iso are in agreement with the results of quantum-chemical calculations.

For desulfurization of naphtha, NaY zeolite was prepared from Dewekhala kaolin clay (Al-Anbar region). For the prepared zeolite adsorbent, x-ray diffraction, sodium content, silica to alumina ratio, surface area, bulk density and crushing strength were determined. From the x-ray diffraction of the prepared NaY zeolite and by a comparison with the standard NaY zeolite, it was found that the prepared adsorbent in this work has approximately the same crystal structure as the standard. Adsorption process was done in a laboratory unit at 25

The study of properties of space of entire functions of several complex variables was initiated by Kamthan [4] using the topological properties of the space. We have introduced in this paper the sub-space of space of entire functions of several complex variables which is studied by Kamthan.

          Purpose  :This study seeks to provide the point of view stands on the marketing performance of the banks in the context of Dynamic Equilibrium  of marketing. It aims to develop a prototype of measuring marketing performance under the umbrella of marketing dynamic prototype, embodied of the strategic alliance and competition, and the  laws and legislation, and to explore any of the dimensions more effective in achieving performance.  This study aims to discusses the importance of the Dynamic Equilibrium  of marketing and it role in achieving the marketing performance <

Thin films of (Cu2S)100-x( SnS2 )x at X=[ 30,40, &50)]% with thickness (0.9±0.03)µm , had been prepared by chemical spray pyrolysis method on glass substrates at 573 K. These films were then annealed under low pressure of(10-2) mbar ,373)423&473)K for one hour . This research includes , studying the the optical properties of (Cu2S)100-x-(SnS2)x at X=[ 30,40, &50)]% .Moreover studying the effect of annealing on their optical properties , in order to fabricate films with high stability and transmittance that can be used in solar cells. The transmittance and absorbance spectra had been recorded in the wavelength range (310 - 1100) nm in order to study the optical properties . It was found that these films had direct optical band

A new  light-weight nanocarbon prepared by spray-drying method  to obtain  particle size is 21.7 nm based of polylactic acid biodegradable film in antistatic packaging .Bio carbon (biochar) is  obtained from  plants and soils to naturally absorb and store carbon dioxide from the atmosphere . Therefor it has been used to support biodegradable polylactic acid (PLA) with to obtain 100% recyclable material.

Using plasticizer thymol of polylactic acid and biochar (bio carbon) as composites were prepared by a solution casting method with (0.5-10)wt% biochar. The composites  characterized by  FTIR, electrical conductivity, mechanical properties , contact angle and Colar and Brightness . Results show th

This study focuses on producing wood-plastic composites using unsaturated polyester resin reinforced with Pistacia vera shell particles and wood industry waste powder. Composites with reinforcement ratios of 0%, 20%, 30%, and 40% were prepared and tested for thermal conductivity, impact strength, hardness, and compressive strength. The results revealed that thermal conductivity increases with reinforcement, while maintaining good thermal insulation, reaching a peak value of 0.633453 W/m·K. Hardness decreased with increased reinforcement, reaching a minimum nominal hardness value of 0.9479. Meanwhile, impact strength and compressive strength improved, with peak values of 14.103 k/m² and 57.3864568 MPa, respectively. The main aim is to manu

Gel polymer electrolytes (GPEs) have attracted considerable attention for rechargeable battery applications because of their high ionic conductivity, mechanical flexibility, and enhanced safety. In the present work, copper-ion-conducting PVA/HPMC gel polymer electrolytes were successfully prepared by the solution casting method using a 50:50 PVA/HPMC blend. Different CuSO₄ concentrations (10, 20, and 30 wt%) were incorporated into the polymer matrix, followed by the addition of 3 mL PANI/[BMIM][BF₄] polyionic liquid. The prepared electrolytes were characterized using scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and electrochemical impedance spectroscopy (EIS). SEM analysi