Zinc oxide nanoparticles sample is prepared by the precipitation method. This method involves using zinc nitrate and urea in aqueous solution, then (AgNO3) Solution with different concentrations is added. The obtained precipitated compound is structurally characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Atomic force microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR). The average particle size of nanoparticles is around 28nm in pure, the average particle size reaches 26nm with adding AgNO3 (0.05g in100ml =0.002 M) (0.1g in100ml=0.0058M), AgNO3 (0.2g in 100ml=0.01M) was 25nm. The FTIR result shows the existence of -CO, -CO2, -OH, and -NO2- groups in sample and oxides (ZnO, Ag2O).and used an

Two common iron oxide-bearing wastes—a drinking water treatment residual and a passive mine water treatment sludge (MWTS)—were utilised with and without modification as media in microcosm experiments to treat artificial benzene, toluene, ethylbenzene, and xylene (BTEX)-contaminated wastewater. In all cases, the removal of BTEX was observed over the 160-day experiments, with benzene being the most recalcitrant. The solubilisation of iron was observed, which, alongside the syntropic relationship between the methanogens and firmicutes, allowed several anaerobic processes to occur, including iron reduction in concert with the biodegradation of BTEX. Nitrogen sparging prior to microcosm establishment, compared to aeration, was seen t

Background: Polymethyl methacrylate (PMMA) resin is extensively utilized in prosthodontics and orthodontics, particularly in fabricating artificial teeth, provisional crowns, denture bases, and orthodontic retainers. Aims: This study aimed to evaluate the effects of incorporating cerium oxide and polyether ether ketone nanoparticle (CP) composite into PMMA resin on transverse strength, impact strength, surface hardness, and denture base adaptation. Materials and Methods: A total of 120 PMMA specimens were divided into three groups based on the concentration of CP composite added to PMMA resin, with each group consisting of 40 specimens: a control group without fillers, group (A) containing 1% wt. of composite filler with a ratio of

Abstract: This paper presents the results of the structural and optical analysis of CdS thin films prepared by Spray of Pyrolysis (SP) technique. The deposited CdS films were characterized using spectrophotometer and the effect of Sulfide on the structural properties of the films was investigated through the analysis of X-ray diffraction pattern (XRD). The growth of crystal became stronger and more oriented as seen in the X-ray diffraction pattern. The studying of X-ray diffraction showed that; all the films have the hexagonal structure with lattice constants a=b=4.1358 and c=6.7156A°, the crystallite size of the CdS thin films increases and strain (ε) as well as the dislocation density (δ) decreases. Also, the optical properties of the

Thin films of CdS:Cu were deposited onto glass substrate temperature 400 °c. The optieal properties have been studied for Cds doped with (1,3, 8) wt% of Cu before and after Gamma irradiation. It was found that the irradiation caused an ( Frenkel defects) where the atom is displaced from its original site leaving vacancy and forming on interstitial atom. It was found the irradiation caused an absorption edge shifting towards long wavelength as a result of the increasing of Cu concentration.

Measurements of Hall effect properties at different of annealing temperature have been made on polycrystalline Pb0.55S0.45 films were prepared at room temperature by thermal evaporation technique under high vacuum 4*10-5 torr . The thickness of the film was 2?m .The carrier concentration (n) was observed to decrease with increasing the annealing temperature. The Hall measurements showed that the charge carriers are electrons (i.e n-type conduction). From the observed dependence on the temperature, it is found that the Hall mobility (µH), drift velocity ( d) carrier life time ( ), mean free path (?) were increased with increasing annealing temperature

Background: Limited data are available on the dimensional stability and surface roughness of ThermoSens, which is a material used in denture processing. This study aimed to measure the vertical teeth changes and surface roughness of ThermoSens dentures prepared using three different investment materials. Materials and methods: For the dimensional changes test, 30 complete maxillary dentures were prepared using different investment methods: group I, dental stone; group II, silicone putty; and group III, a mixture of dental stone and plaster (ratio, 1:1; n = 10 for each group). Four screws were attached to the dentures: two were attached to the buccal surface of the canine and first molar, and the other two were attached in the flange areas o

This work studies the impact of input machining parameters of Electrical Discharge Machining (EDM) on the machining process performance. Tool steel O1 was selected as the workpiece material, copper as the electrode material, and kerosene as the dielectric medium. Experimental runs have been carried out with a Design of Experiment (DOE) technique. Twenty tests are accomplished with the current range of (18 to 24 Ampere), a pulse duration range of (150 to 200 µs), and a pulse-off time range of (25 to 75 µs). Based upon the experimental study's output results, the EDM parameter's effect (voltage of power supply, discharge current, pulse duration, and pulse pause interval) on the responses of the process represented by sur