Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o

Abstract : Tin oxide SnO2 films were prepared by atmospheric chemical vapor deposition (APCVD) technique. Our study focus on prepare SnO2 films by using capillary tube as deposition nozzle and the effect of these tubes on the structural properties and optical properties of the prepared samples. X-ray diffraction (XRD) was employed to find the crystallite size. (XRD) studies show that the structure of a thin films changes from polycrystalline to amorphous by increasing the number of capillary tubes used in sample preparation. Maximum transmission can be measured is (95%) at three capillary tube. (AFM) where use to analyze the morphology of the tin oxides surface. Roughness and average grain size for different number of capillary tubes have b

       Optical properties and surface morphology of pure and doped Polystyrene films with different divalent metals of Zn, Cu and Sn and one concentration percentage have been studied. Measurements of UV-Vis spectrophotometer and AFM spectroscopy were determined. The absorbance, transmittance and reflectance spectrums were used to study different optical parameters such as absorption coefficient, refractive index, extinction coefficient and energy gap in the wavelengths rang 200-800nm. These parameters have increased in the presence of the metals. The change in the calculated values of energy gaps with doping metals content has been investigated in terms of PS matrix structural modification. The value of opt

The influence of sintering and annealing temperatures on the structural, surface morphology, and optical properties of Ag2Cu2O4 thin films which deposited on glass substrates by pulsed laser deposition method have been studied. Ag2Cu2O4 powders have polycrystalline structure, and the Ag2Cu2O4 phase was appear as low intensity peak at 35.57o which correspond the reflection from (110) plane. Scan electron microscopy images of Ag2Cu2O4 powder has been showed agglomerate of oxide particles with platelets shape. The structure of thin films has been improved with annealing temperature. Atomic Force micrographs of Ag2Cu2O4 films showed uniform, homogenous films and the shape of grains was almost spherical and larger grain size of 97.85 nm has o

Polyetheretherketone (PEEK) has favorable biomechanical properties to be used as an implant material. Unfortunately, it is hydrophobic and does not promote cellular adhesion, which could result in poor integration with bone tissue. Bio-functionalization of PEEK surface with osteogenic peptides derived from bone extracellular matrix proteins is an exciting approach to encourage bone formation around the implant. In the current study, bone-forming peptide-2 was immobilized on PEEK surface using two different methods, using dopamine and a diglycidyl ether as conjugate compounds, respectively. Peptide quantification test revealed that the two strategies resulted in the most amount of peptides were attached with 0.5 mM concentration and no furth

Several azo dyes were synthesized through coupling reaetion of some substituted phenols and B.naphthol with diazonium salt of 2- amino-1,3-4- thiadiazol -5- thiol. All the synthesized compounds during this work were characterized using some speetral data (F.TIRand UV)andM.P . 2-[4 --Hydroxy napthyl-azo ] -1,3,4-Thiadiazol -5-Thiol • 2- [2-- hydroxy –4- NO2 – phenyl- azo]- 1,3,4 - Thiadiazol –5-Thiol. • 2- [3--Amino-4-Hydroxy phenyl –azo]-1,3,4 - Thiadiazol –5-Thiol. . • 2-[2--Amino-4-Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol . • 2- [3--Amino-6- Hydroxy phenyl -azo]-1,3,4 - Thiadiazol –5-Thiol. • 2-[2-- Hydroxy- 5 – chloro – Pheny - azo]- 1,3,4 - Thiadiazol –5-Thiol . • 2- [4-- Hydroxy phenyl -azo] -1,