In the present work, a z-scan technique was used to study the nonlinear optical properties, represented by the nonlinear refractive index and nonlinear absorption coefficients of nanoparticles cadmium sulfide thin film. The sample was prepared by the chemical bath deposition method. Several testing were done including, x-ray, transmission and thickness of thin film. z-Scan experiment was performed at two wavelengths (1064 nm and 532 nm) and different energies. The results showed the effect of self-focusing in the material at higher intensities, which evaluated n2 to be (0.11-0.16) cm2/GW. The effect of two-photon absorption was studied, which evaluated β to be (24-106) cm/GW. In addition, the optical limiting behavior has been studied.

Phase change materials (PCMs) such as paraffin wax can be used to store or release large amount of energy at certain temperature at which their solid-liquid phase changes occurs. Paraffin wax that used in latent heat thermal energy storage (LHTES) has low thermal conductivity. In this study, the thermal conductivity of paraffin wax has been enhanced by adding different mass concentration (1wt.%, 3wt.%, 5wt.%) of (TiO₂) nano-particles with about (10nm) diameter. It is found that the phase change temperature varies with adding (TiO₂) nanoparticles in to the paraffin wax. The thermal conductivity of the composites is found to decrease with increasing temperature. The increase in thermal conductivity ha

In this study, silver nanoparticles (AgNPs) are synthesized using different chemical routes to obtain different sizes and shapes of nanoparticles by colloid chemistry with using stabilizing and reducing agent, which make them interesting for variety of physical applications. The morphology and structure of the synthesized AgNPs were characterized by UV-VIS spectra, Scanning Electron Microscopy (SEM) and Zeta potential to demonstrate that different sizes and shapes can by synthesized by different reductants in the presence of various stabilizing agents.

A huge potential from researchers was presented for enhancing the nonlinear optical response for materials that interacts by light. In this work, we study the nonlinear optical response for chemically prepared nano- fluid of silver nanoparticles in de-ionized water with TSC (Tri-sodium citrate) protecting agent. By the means of self-defocusing technique and under CW 473 nm blue laser, the reflected diffraction pattern were observed and recorded by CCD camera. The results demonstrate that, the Ag nano-fluid shows a good third order nonlinear response and the magnitude of the nonlinear refractive index was in the order of 10−7 cm2/W. We determine the maximum change of the nonlinear refractive index and the related phase shift for the mat

In this work, the fine structure macro-porous silicon (macroPS) substrate was prepared by photo-electro-chemical etching of n-type silicon wafer. Ultraviolet illumination condition of wavelength 360nm wavelength and intensity of about 100mW/cm2 with etching current density of about 50 mA/cm2 and etching time 5
min was employed. The Hybrid device gold nanoparticles /macroPorous Silicon (AuNPs/macroPS) was fabricated by deposition AuNPs into mPS substrate Via immersion plating process of macroPS in the solution of HAuCl4 with the (10-3M) concentration and 2min immersion time. The characteristics of PS before and after
immersion process were investigated by scanning electron microscopy (SEM), EDS,&nb

An aqueous chemical reaction has been used to prepare antifungal ZnS: Mn nanostructures, from manganese chloride, zinc acetate and thioacetamide in aqueous solution. The nanoparticle size has been controlled using thioglycolic acid as a capping factor. The major feature of the ZnS:Mn nanoparticles of average diameter ~ 2.73 nm is that possible preparing the sample from sources non-toxic precursors. The manufactured ZnS:Mn nanoparticles were identified and characterized to investigate the structure, morphology, composition of components of the nanoparticles and optical properties using (XRD, SEM, EDS and UV-Vis spectroscopy) techniques respectively. The agar dilution mechanism used to evaluate of the antifungal activity using ZnS:Mn nanopart

      Biocompatible gold nanoparticles were successfully synthesized by hibiscus plant leaf extract as a bioreactor. The prepared nanoparticles were evaluated using UV/Vis spectroscopy, Atomic Force Microscopy (AFM), Fourier Transform Infrared Spectroscopy (FT-IR), X-ray Diffraction and Scanning Electron Microscopy (SEM) . The study also investigated the effect of the different gamma irradiation doses on the size and dispersion of the produced nanoparticles. In UV- Vis spectra, the peak of Au NPs' surface plasmon resonance (SPR) was detected as a single peak at 543 nm. The gamma irradiation induced a blue shift in the SPR peak, which indicates that it might be applied as affective factor for size control.  Physical as well as chemi

                The characteristics of sulfur nanoparticles were studied by using atomic force microscope (AFM) analysis. The atomic force microscope (AFM) measurements showed that the average size of sulfur nanoparticles synthesized using thiosulfate sodium solution through the extract of cucurbita pepo extra was 93.62 nm. Protecting galvanized steel from corrosion in salt media was achieved by using sulfur nanoparticles in different temperatures. The obtained data of thermodynamic in the presence of sulfur nanoparticles referred to high value as compares to counterpart in the absence of sulfur nanoparticles, the high inhibition efficiency (%IE) and corrosion resistance were at high temperature, the corrosion rate or weig

Colloidal silver nanoparticles were prepared by single step green synthesis using aqueous extracts of the leaves of thyme as a function of different molar concentration of AgNO₃ (1,2,3,4 mM(. The Field Emission Scanning Electron Microscopy (FESEM), UV-Visible and X-ray diffraction (XRD) were used to characterize the resultant AgNPs. The surface Plasmon resonance was observed at wavelength of 444 nm. The four intensive peaks of XRD pattern indicate the crystalline nature and the face centered cubic structure of the AgNPs. The average crystallite size of the AgNPs ranged from 18 to 22 nm. The FESEM image illustrated the well dispersion of the AgNPs and the spherical shape of the nanoparticles with a particle size distribution be