Undoped and Al-doped CdO thin films have been prepared by vacuum thermal evaporation  on  glass  substrate  at  room  temperature  for  various  Al  doping ratios (0.5, 1 and 2)wt.% . The films are characterized by XRD and AFM surface morphology properties. XRD analysis showed that CdO:Al films are highly polycrystalline and exhibit cubic crystal structure of lattice constant averaged to 0.4696 nm with (111) preferred orientation. However, intensity of all peaks rapidly decreases which indicates that the crystallinity decreases with the increase of Al dopant. The grain size decreases with Al content (from 60.81 to 48.03 nm). SEM and AFM were applied to study the morphology an

The DC electrical conductivity properties of Ge60Se40-xTex alloy with x = 0, 5, 10, 15 and 20). The samples were formed in the form of discs with the thickness of 0.25–0.30 cm and the diameter of 1.5 cm. Samples were pressed under a pressure of 6 tons per cm2 , using a ton hydraulic press. They were prepared after being pressed using a ton hydraulic press using a hydraulic press. Melting point technology use to preper the samples. Continuous electrical conductivity properties were recorded from room temperature to 475 K. Experimental data indicates that glass containing 15% Te has the highest electrical conductivity allowing maximum current through the sample compared to Lu with other samples. Therefore, it is found that the DC co

Select 30 isolate from Bacillus to detect the ability to produce pullulanase enzyme in liquid and solid state fermentation, and use the isolate Bacillus licheniformis (Bs18) because the highest production of enzyme, the optimum condition for the production of enzyme by liquid state fermentation (LSF) in growen with: media contains starch + pullulan as a carbon source, peptone as a nitrogen source, inoculums size 2 ml, and incubated at 40 C° with pH 7 for 48 hrs. In addition pullulanase production by solid state fermentation (SSF) was investigated using isolated Bacillus licheniformis (Bs18). Optimization of process parameters were carried out ,the optimum solid substrate , Temperature , pH , incubation period , inoculation size , hydrat

A total of 116 males with primary infertility and 32 fertile males (normozoospermia;
NOR) were studied to evaluate parameters of seminal fluid analysis. Based on WHO criteria
of 2010 for general seminal fluid analysis, the patients were distributed into three groups: 32
azoospermic (AZO), 40 oligozoospermic (OLI) and 44 asthenozoospermic (AST) patients.
AZO and OLI patients and NOR shared an approximated mean of seminal fluid volume (2.25,
2.75 and 2.50 ml, respectively), while it was significantly increased (3.58 ml) in AST patients.
In NOR men, the spermatozoa concentration was 65.13 x 10
6
spermatozoa/ml, while it was
significantly decreased in AST (51.42 x 10
6
spermatozoa/ml) and OLI (5.58 x 10

The   mechanical    properties   of   fiber-reinforced-polymer   (FRP)

composites are dependent on the type amount, and orientation of fiber that is selected for a particular service. There are many commercially available reinforcement forms to meet the design requirements of the user. The ability of failure in the fiber architecture allows for optimized performance of a product that saves both weight and cost ( 12).

A modem technology is adopted to produce fibers (glass, kevelar,

and carbon) reinforced composite by using unsaturated polyester, where different volume fraction  of these fibers are used  (0, 0.2, 0.4, 0.6, 0.8,  I)

reinfor

     Tow simple, rapid and sensitive spectrophotometric methods for the determination of mesalazine in pharmaceutical preparations have been carried out. The proposed methods depend on oxidative coupling reaction of mesalazine with m-aminophenol in the existence of N-bromosuccinamide in alkaline medium (method A) and 2,6-dihydroxybenzoic acid in the existence of sodium metaperiodate in basic medium (method B) to produce colored products , show highest absorptions at 640 (nm) and 515 (nm), alternately. Beer’s law was consistent in concentrations extent of 1.25-30 and 0.5-12.5 (µg.mL^-1) with molar absorptivity of 0.36×10⁴ and 0.77×10⁴ L.mol^-1.cm<