Most studies on deep beams have been made with reinforced concrete deep beams, only a few studies investigate the response of prestressed deep beams, while, to the best of our knowledge, there is not a study that investigates the response of full scale (T-section) prestressed deep beams with large web openings. An experimental and numerical study was conducted in order to investigate the shear strength of ordinary reinforced and partially prestressed full scale (T-section) deep beams that contain large web openings in order to investigate the prestressing existence effects on the deep beam responses and to better understand the effects of prestressing locations and opening depth to beam depth ratio on the deep beam performance and behavior. A total of seven deep beam specimens with identical shear span-to-depth ratio, compressive strength of concrete, and amount of horizontal and vertical web reinforcement ratios have been tested under mid-span concentrated load applied monotonically until failure. The main variables studied were the effects of depth of the web openings and the prestressing location on deep beam performance. The test results showed that the enlargement in the size of web openings substantially reduces the element’s shear capacities while prestressing strands location above the web openings has more effect at increasing the element’s shear capacities. The numerical study considered three-dimensional finite element models that have been developed in Abaqus software to simulate and predict the performance of prestressed deep beams. The results of numerical simulations were in good agreement with the experimental ones.
In this work, a test room was built in Baghdad city, with (2*1.5*1.5) m3 in dimensions, while the solar chimneys (SC) were designed with aspect ratio (ar) bigger than 12. Test room was supplied by many solar collectors; vertical single side of air pass with ar equals 25, and tilted 45o double side of air passes with ar equals 50 for each pass, both collectors consist of flat thermal energy storage box collector (TESB) that covered by transparent clear acrylic sheet, third type of collector is array of evacuated tubular collectors with thermosyphon in 45o instelled in the bottom of TESB of vertical SC. The TESB was
... Show MorePhase change materials are known to be good in use in latent heat thermal energy storage (LHTES) systems, but one of their drawbacks is the slow melting and solidification processes. So that, in this work, enhancing heat transfer of phase change material is studied experimentally for in charging and discharging processes by the addition of high thermal conductive material such as copper in the form of brushes, which were added in both PCM and air sides. The additions of brushes have been carried out with different void fractions (97%, 94% and 90%) and the effect of four different air velocities was tested. The results indicate that the minimum brush void fraction gave the maximum heat transfer in PCM and reduced the time
... Show MoreThe poor hole cleaning efficiency could causes many problems such as high torque, drag, poor hydraulics and pipe stuck. These inherent problems result in an avoidable high operation cost which this study tried to address. In this study, the effect of cutting density on hole cleaning efficiency in deviated and horizontal wells was investigated. Experiments were conducted using 40 feet (12 m) long of flow loop made from iron and PVC. However, the test section was made from PVC with (5.1m) long and (4” ID) for outer pipe and (2” OD) inner pipe. The cutting transport ratio (CTR) was determined from weight measurements for each test. Cutting Transport Ratio has been investigated for effects of the following parameters; flow rate, cu
... Show MoreBackground: To evaluate the effect of antierosive agents (10% Nano-Hydroxyapatite (NHA), 10% Casein Phophopeptide-Amorphous Calcium Phosphate (CPP-ACP), and combination of 10% NHA and 10% CPP-ACP) on loss of minerals from enamel surface of permanent teeth treated with antierosive agents when exposed to an acidic beverage and investigate the morphological changes of treated enamel surface after demineralization with cola based beverage under Scanning Electron Microscope (SEM). Materials and Methods: Sixty maxillary first premolars were randomly divided into four groups, 15 teeth for each group. Group I treated with 10% NHA, Group II treated with 10% CPP-ACP, Group III treated with 10% NHA and 10% CPP-ACP, and Group IV did not treat with any
... Show MoreIn this research, we will discuss how to improve the work by dealing with the factors that
participates in enhancing small IT organization to produce the software using the suitable
development process supported by experimental theories to achieve the goals. Starting from
the selecting of the methodology to implement the software. The steps used are and should be
compatible with the type of the products the organization will produce and here it is the Web-Based Project Development.
The researcher suggest Extreme Programming (XP) as a methodology for the Web-Based
Project Development and justifying this suggestion and that will guide to know how the
methodology is very important and effective in the software dev
Background: Green Tea is made from the leaf of the plant “Camellia sinensisâ€. Green tea is reported to contain thousands of bioactive ingredients including catechins which have shown great promise for having antimicrobial effects. Periodontal diseases represent one of the most prevalent diseases around the world and the main etiologic factor behind it, is plaque accumulation, in addition certain kinds of bacteria have been detected frequently in subjects suffering from periodontitis, Several studies suggested that the outcome of periodontal treatment is better if particular pathogens including Aggregatibacteractinomycetemcomitans can no longer be detected after therapy. Materials and Methods: plaque samples were collected from 2
... Show MoreGamma - irradiation effect on polymethylmethacrylate (PMMA) samples has been studied using Positron Annihilation Lifetime (PAL) method. The orthopositronium (o-Ps) lifetime τ3, hence the o-ps parameters, the volume hole size (Vh) and the free volume fraction (Ꞙh) in the irradiated samples were measured as a function of gamma-irradiation dose up to 28.05 kGy. It has been shown that τ 3, Vh, and Ꞙh, are increasing in general with increasing gamma-dose, to reach a maximum percentage increment of 22.42% in τ3, 60% in Vh and 29.5% in Ꞙh, at. 2.55 kGy, whereas τ2 reaches maximum increment of 119. 7% at 7.65 kGy. The results s
... Show More