An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a residual deflection of 46.4 mm. The greatest deterioration occurred when exposed to 700ºC, at this temperature, a higher unrecoverable permanent deflection was recorded (160.3 mm) of the maximum measured burning deflection (173.8mm), indicating that the percent recovered deflection was 8%. Then, all composite SB-RC deck floors were loaded until failure to determine the percent decrease in their ultimate capacity. The results were compared with the behavior of composite SB-RC deck floor without burning (reference specimen).
The slurry infiltrated fiber concrete (SIFCON) is nowadays considered a special type of high fiber content concrete; it is high strength and high performance material. This paper investigates the effect of spread steel fiber into the slurry mortar on some properties of SIFCON. According to fiber distribution, two sets were used in this investigation. The first set consisted of randomly distributing fibers inside the slurry. The second set was by placing the fibers in an orderly manner inside the slurry. Crimped steel fibers with an aspect ratio of (60) were used. Two different volume fractions percentage of (7% and 9%) by volume of mold were used in both sets for this study. Also, a w/c ratio of (0.35) and superplasticiz
... Show More
(7)
Objective: The aim of this study was to assess the knowledge and attitude of Iraqi dentists towards cone beam computed tomography (CBCT) applications in endodontics by using an online survey. Materials and Methods: A questionnaire, consisting of 31 questions, targeted general dental practitioners and specialists in different dental specialities. A total of 306 participants were included. Data were assessed according to the frequency of distribution and the chi-square test was applied to analyse the difference in responses between two independent groups. Results: Among the participants 63.4% were using digital radiography in their daily practice, and 84% had awareness about CBCT's uses, with higher statistically significant responses among e
... Show More
(2)
Abstract:
Purpose\The researcher paper aims to determine the impact of information technology on the job performance, for Iraq private ban as through the use of technology dimensions of job performance.
The aim of this research: this study aims to discuss the importance of information technology and its role in achieving job performance and its impact on the Iraq banking sector design/ methodology/ approach used entrance design/methodology/approach- pilot, the questionnaire was used to collect data in order to develop a model to measure reliably and correctly to the variables of information technology and job performance, and hypotheses were tested through the use of some statisti
... Show More
In this study, chemical oxidation was employed for the synthesis of polypyrrole (PPy) nanofiber. Furthermore, PPy has been subjected to treatment using nanoparticles of neodymium oxide (Nd2O3), which were produced and added in a certain ratio. The inquiry centered on the structural characteristics of the blend of polypyrrole and neodymium oxide after their combination. The investigation utilises X-ray diffraction (XRD), FTIR, and Field Emission Scanning Electron Microscopy (FE-SEM) for PPy, 10%, 30%, and 50% by volume of Nd2O3. According to the electrochemical tests, it has been noted that the nanocomposites exhibit a substantial amount of pseudocapacitive activity.
سمير خلف فياض * و محسن طالب د.نوال عزت عبد اللطيف*, مجلة الهندسة والتكنولوجيا, 2010
Two arylenedisuccinamic acids, namely 1,4-phenylene-disuccinamic acid and 4,4'biphenyl-disuccinamic acid were prepared from the reaction of two moles of succinic anhydride with one mole of 1,4-phenylenediamine dihydrochloride and beinzidine respectively.Dehydration of arylenedisuccinamic acid in the pressence of polyvinyl alcohol (PVA) and catalytic amount of concentrated.H2SO4,gives N,N'-arylenedisuccinimidesPVAcomposite polymers. Dehydration of arylenedisuccinamic acid (without PVA) in the pressence of catalytic amount of conc. H2SO4 gives N,N'-arylenedisuccinimides. Arylenedisuccinamic acid and arylenedisuccinimides characterized by CHN-analysis,FT.IR and 1H,C13-NMR.Spectral analysis
Polymers, being one of the most important materials in dentistry, offer great physical and mechanical qualities, as well as good biocompatibility. Aim of this study was done to evaluate the Polyetherketoneketone and Polyetherketoneketone polymer composite material used as dental implant through tensile strength, Fourier Transform Infrared analysis FTIR, and wettability). Polyetherketoneketone composites (Polyetherketoneketone and Strontium-containing hydroxyapatite) with selected weight percentage ratios of (0, 10%, 20%, 30%), were fabricated using a compression molding technique”, The study involved Samples preparation (sheets) shaped and form into the desired shape according to standard for tests which included tensile strength,
... Show More
(6)
(5)
To fabricate an inexpensive surface coating with excellent mechanical properties with good water resistance and thermal diffusion, white eggshell fibers with particle size (~1micrometer) has been added by different weight percentages (1,2,3,4,5,6,7 and 8 %) to Unsaturated Polyester.
The weight ratio (4%) of eggshell powder is a good ratio to be added to polyester to improve its mechanical properties, such as hardness, impact strength, and wear resistance. The hardness was improved by (3.75%); impact strength has the same value as polyester, flexural strength by (8.43%) and high improvement in wear resistance (74.4%), as well as to get further improvements in mechanical properties of polyester, the eggshell powder was added
... Show More
(7)
In this study, the mechanical properties of an epoxy and unidirectional woven carbon with fiberglass composite were experimentally investigated. When preparing the composite samples, American Society for Testing and Materials (ASTM)standard was used. Tensile, impact and flexural test were conducted to investigate the mechanical properties of the new produced epoxy Unidirectional Woven Carbon and Epoxy Fiberglass composites. The outcome showed that the strength of the produced samples increased with the increase in the number of unidirectional woven carbon layers added. Two methods were utilized: (1) woven carbon composite with glass fiber (2) woven carbon composite). The two methods of composite were compared with each other. The resul
... Show More
(2)
(1)