Introduction and Aim: Bacteriocins are antimicrobial peptides that have bactericidal and/or bacteriostatic activity against other bacteria. The aim of this study was to assess the antibacterial efficiency of Klebocin a K. pneumoniae bacteriocin, against biofilm formation by clinical isolates of methicillin resistant Staphylococcus aureus MRSA.   Materials and Methods: S. aureus isolated from clinical samples was identified according to vitek 2 system Antibiotic susceptibility test was performed according to disc diffusion method. Vitek 2 compact system was also used to detect MRSA strains. Agar well diffusion method was used to evaluate the antibacterial activity of klebocin from K. pneumoniae towards 11 strains of S. aureus by

Eleven yoghurt samples were collected from local markets in Baghdad to isolate Lactobacillus buchneri. Only 3 isolates of L. buchneri were found and the isolate No. 3 was the most producer of bacteriocin. Bacteriocin was adsorbed 100% onto silicic acid at pH 6.0-7.0. Below or above these pH values, adsorption was decreased, ranging between 35 and 90%. Therefore, pH 6.0 was used for the purification procedure. The purification procedure including silicic acid adsorption/desorption and cation-exchange chromatography (CEC) resulted in a 11.11 fold increase in the final specific activity of pure bacteriocin (1176.47 Au/mg) compared to the culture supernatant which was 32.64 Au/mg. The molecular weight was determined to be about 3.4 kDa. The bac

International news websites, including Russia Today, pay special attention to the media image of Afghan women, especially after the Taliban movement took control of Afghanistan. Therefore, it was necessary to know the image of the Afghan woman, the fate of the rights she acquired in recent years, and the transformations that affected her after the Taliban took control of the government, and studied them on international news sites, specifically Russia Today.

          The researcher summarized the problem of this study in the following question: What is the media image of the Afghan woman on the Russia Today news site?

In this work, porous silicon gas sensor hs been fabricated on n-type crystalline silicon (c-Si) wafers of (100) orientation denoted by n-PS using electrochemical etching (ECE) process at etching time 10 min and etching current density 40 mA/cm2. Deposition of the catalyst (Cu) is done by immersing porous silicon (PS) layer in solution consists of 3ml from (Cu) chloride with 4ml (HF) and 12ml (ethanol) and 1 ml (H2O2). The structural, morphological and gas sensing behavior of porous silicon has been studied. The formation of nanostructured silicon is confirmed by using X-ray diffraction (XRD) measurement as well as it shows the formation of an oxide silicon layer due to chemical reaction. Atomic force microscope for PS illustrates that the p

The effect of three ionic liquids viz., 1-hexyl-3-methylimidazolium tetrafluoroborate (ILE), 1-hexyl-3-metylimidazolium hexafluorophosphate (ILF) and 1-octyl-3-methylimidazolium tetrafluoroborate (ILG) when used as surfactants on the performance of dissolved air floatation (DAF) was investigated.

   Experiments were conducted at a temperature of 30-35 ºC, 10ppm ferric chloride as coagulant, 50% recycle ratio, pH 8, and 10 minutes treatment time  to find oil and grease (OG) and turbidity removal efficiencies at saturation pressure (2-6) bar.

ILs were used at concentration of 50 µl/liter of treated water in two positions in DAF system; the saturation vessel and the treatment tank. The performance using ILs

Zinc oxide thin films were deposited by chemical spray pyrolysis onto glass substrates which are held at a temperature of 673 K. Some structural, electrical, optical and gas sensing properties of films were studied. The resistance of ZnO thin film exhibits a change of magnitude as the ambient gas is cycled from air to oxygen and nitrogen dioxide

The gas sensing properties of Co₃O₄ and Co₃O₄:Y nano structures were investigated. The films were synthesized using the hydrothermal method on a seeded layer. The XRD, SEM analysis and gas sensing properties were investigated for Co₃O₄ and Co₃O₄:Y thin films. XRD analysis shows that all films are polycrystalline in nature, having a cubic structure, and the crystallite size is (11.7)nm for cobalt oxide and (9.3)nm for the Co₃O₄:10%Y. The SEM analysis of thin films obviously indicates that Co₃O₄ possesses a nanosphere-like structure and a flower-like structure for Co₃O₄:Y.

The sen