Aluminum oxide thin films were prepared by dc reactive sputtering technique using different mixing ratios of argon and oxygen gases (90:10, 70:30, 50:50, 30:70, and 10:90). These films were characterized to introduce their crystalline structures, surface morphology, and elemental composition. A progressive transition occurs from a predominantly amorphous to a highly crystalline Al2O3 film as the oxygen content in the Ar:O2 gas mixture is increased. Increasing the oxygen content leads to a progressive decrease in surface roughness, resulting in smoother and more uniform films with finer granular features. The oxygen-rich environments yield the smoothest surfaces, while argon-rich environments result in significantly rougher surfaces. These f

Erbium, as optical probe, doped silicate sol-gel glass with
different Er concentrations was formed by wet chemical synthesis
method using ethanol, water and tetraethaylorthosilicate
[Si(OC2H5)4] precursor. Erbium ions were incorporated into silica
sol-gel matrix via dissolution of Erbium chloride solution into the
initial Si(OC2H5)4 precursor sol. Aluminum (Al) as a co-dopant was
added to the final precursor in the form of Aluminum chloride
(AlCl3) solution. The prepared samples were analyzed using atomic
absorption analysis, X-ray diffraction and spectroscopic tests. The
experimental results concerned with the transmission spectra suggest
that the final samples have a good transparency and homogeneity.
A

Abstract

            Rayleigh distribution is one of the important distributions used for analysis life time data, and has applications in reliability study and physical interpretations. This paper introduces four different methods to estimate the scale parameter, and also estimate reliability function; these methods are Maximum Likelihood, and Bayes and Modified Bayes, and Minimax estimator under squared error loss function, for the scale and reliability function of the generalized Rayleigh distribution are obtained. The comparison is done through simulation procedure, t

Schiff base N,N'-Bis-(4-dimethylamino-benzylidene)-benzene-1,4-diamine has been synthesized from 4-dimethylaminobenzenaldehyde and benzene-1,4-diamine. The structure of Schiff base was obtained by (C.H.N.) microanalysis, Mass, 1HNMR, FT-IR and UV-Vis spectral methods and thermal analysis. Metal mixed ligand complexes of some metal(II) salts with Schiff base ligand and anthranilic acid were prepared in the molar ratio (1:2:2), (Metal):(SBL)2:(Anthra)2, (SBL)= Schiff base ligand, (Anthra) =anthranilic acid and Metal= Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Hg(II). The thermal behaviour (TGA) of the complexes was studied. The prepared complexes identified by using mass, thermal analysis, FT.IR and UV-Vis spectrum methods, on otherwise flame

Abstract

The present paper focuses in a particular on the study of the biochar production conditions by the thermal pyrolysis of biomass from local Iraqi palm fronds, in the absence of oxygen. The biochar product can be used as soil improvers. The effect of temperature on the extent of the thermal pyrolysis process was studied in the range from 523 to 773K with a residence time of 15 minutes and nitrogen gas flow rate of 0.1 l/min. The produced biochar was characterized as will as biomass and degradation products. The results showed that the rate of biochar production decreases with the increasing in temperature, also it was noted that the normalized biochar surface area and pore size increases with the increasin

Background: The isthmus is a difficult area in the root canal complex to manage. The research aimed to evaluate the efficiency of three different obturation techniques (lateral condensation, EandQ (thermoplasticized gutta percha system) and Soft Core (thermoplasticized core carrier gutta percha system)) to obturate the isthmus area of roots prepared by two different instrumentation techniques (rotary ProTaper universal and ProTaper Next systems). Material and method: Sixty freshly extracted teeth were randomly divided into two main groups (A and B) of 30 teeth each. Group A was prepared by rotary ProTaper Universal whereas group B was prepared by ProTaper Next system. Each main group was then randomly subdivided into three subgroups of 10 t

Magnesium Phthalocyanine (MgPc) was deposited on a glass substrate by pulsed laser deposition (PLD) using Q-Switching Nd:YAG laser with wavelength 1064 nm, repetition rate 6 Hz, at room temperature (300K) and different annealing temperatures (373, 473, and 573)K under vacuum condition of 10-3 torr. All films were annealed for one hour to attain crystallinity. X-ray diffraction (XRD) of MgPc powder indicated that MgPc crystallizes in polycrystalline with a monoclinic structure. While comparing the MgPc films, it was observed that the intensity of the characteristic peak increases with temperature, and the crystallization exhibited a monoclinic structure typical of the β-form. The Miller indices, hkl, values for each diffraction peak

Abstract\

preparation process of performance evaluation in organizations is of extreme importance, and under development in organizations and the opening of markets and technological developments in the industry and heightened competition among industrial organizations imposed systems are built for performance give a clear picture about performance and competition,  And centered research problem in answering the following questions: Is performance evaluation system is available in Wasit State Company for Textile Industries(Research sample ), This research aims to assess the performance of policies and programs in the company, according to guide performance evaluation of programs and policies prepared by the Dutch Cou