Lactococcus lactis ssp. lactis isolated from raw milk was used for titanium dioxide (TiO2) nanoparticles biosynthesis. Biosynthesized TiO2 nanoparticles were characterized using UV-vis spectroscopy, Atomic Force Microscopy (AFM) (1.97 nm), X-ray diffraction (XRD) appa-ratus, Field Emission Scanning Electron Microscopy (FE-SEM), Energy dispersive X-ray anal-ysis (EDX) spectra and Fourier Transform Infrared Spectroscopy (FTIR). Result was 408.21 cm-1 that belong to anatase Titania. L. lactis ssp. Lactis isolates had the ability to synthesize TiO2 nanoparticles, the characterization results presented that the biosynthesized nanoparti-cles were at wavelength (344-347) nm; approving the formation of anatase phase of TiO2 NPs; spherical c

ABSTRACT: In this research SnO2 thin films have been prepared by using hot plate atmospheric pressure chemical vapor deposition (HPCVD) on glass and Si (n-type) substrates at various temperatures. Optical properties have been measured by UV-VIS spectrophotometer, maximum transmittance about (94%) at 400 0C. Structure properties have been studied by using X-ray diffraction (XRD) , its shows that all films have a crystalline structure in nature and by increasing growth temperature from(350-500) 0C diffraction peaks becomes sharper and grain size has been change. Atomic force microscopy (AFM) uses to analyze the morphology of the Tine Oxides surface structure. Roughness & Root mean square for different temperature have been investigated. The r

ZnxNi1-x-yCuyFe2O4 spinel ferrite were prepared using solid state reaction method with (y=0.1, x=0.2, 0.3, 0.4, 0.5, 0.6 ) . X-ray diffraction with diffractometer CuKα analysis have been carried out and studied showing single phase spinel cubic with space group FD͞ 3m for all prepared samples . Lattice parameters and crystallite grain size and x-ray density(ρx-ray) bulk density and porosity ratio's were calculated and showed good agreement with the international data reported in the scientific research's.

The article presents the synthesis and liquid crystalline properties of some of new bent and linear core compounds containing a 1,3,4-oxadiazole, piperazine and thiazolidin-4-one rings as a central core. The new synthesized compounds were characterized by elemental analysis and FTIR, ¹HNMR and mass spectroscopy). The liquid crystalline properties were studied by polarized optical microscopy and differential scanning calorimetry. All Schiff bases compounds with 1,3,4-oxadiazole and piprzaine ring in central core presented liquid crystalline properties. The liquid crystallinity of compounds containing 1,3,4-oxadiazole and thiazolidin-4-one rings as a central core were found depending on the type of terminal substituents.

This research includes the synthesis of some new nucleoside analogues via 1,3-
dipolar cycloadditon reaction starting with 1,3,4,6- Tetra- O-benzoyl –2 – azido-2-
deoxy- β – D- fructofuranose (F3) which was prepared in three steps ,protection
(benzoylation ) , bromination and azotation ((F1-F3) from D- fructose as sugar
moiety while the base moiety , 2-substituted benzimidaole derivatives (A1-A5)
were synthesized by condensation of O-phenylenediamine with different aromatic
aldehyde .
Nucleophilic substitution of propargyl bromide with benzimidaole derivatives (gave
the N- substituted compounds (B1-B5) which were reacted with azido sugar through
1,3- dipolar cycloadditon reaction to give nucleoside analo

New metal complexes of some transition metal ions Co(II), Cu(II) , Cd(II) and Zn(II) were prepared by their reaction with previously prepared ligands HLI= (P-methyl anilino) phenyl acetonitrile and HLII = (P-methyl anilino) –P– chloro phenyl acetonitrile . The two ligands were prepared by Strecker’s procedure which includ the reaction of p- toluidine with benzaldehyde and P- chlorobenzaldehyde respectively. Structures were proposed depending on atomic absorption , i.r. and u.v.visible spectra in addition to magnetic susceptibility and electrical conductivity measurements.

A new series of schiff base and aminothiadiazole derivatives of N- substituted phthalimide (I-VI) were synthesized. In this work, the intermediate 4-(1,3-dioxoisoindolin-2-yl)benzaldehyde compound (I), was formed by reaction of 4-amino benzaldehyde with phthalic anhydride in glacial acetic acid(GAA). A series of Schiff bases (IV-VI) was prepared by the reaction of benzidine with compound (I) in ethanol and presence of GAA as a catalyst to form compound (IV) which react with compound (I) and p-nitro benzyldehyde to give compound (V) and (VI) respectively. A new phthalimide thiosemi-carbazone derivative (ll) was prepared by reaction of compound (l) with thiosemi-carbazide HCl in the presence of equimolar amount of sodium acetate. Fina

In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/