Due to its association with hepatocellular carcinoma and being one of the ten most common malignancies worldwide, hepatitis C viral infection has become a severe public health concern. Therefore, establishing an accurate, reliable and sensitive diagnostic test for this infection is strongly advised. Real-time polymerase chain reaction (PCR) has been created to achieve this purpose. The current study was established to investigate the hepatitis C virus among Iraqi patients with chronic renal failure and to detect the virus immunologically by the fourth generation enzyme-linked immunosorbent assay technique and molecularly by real-time PCR. As a result, out of 50 patients with chronic renal failure undergoing dialysis, 39 patients tes

Background and objective: Viral Hepatitis Type B&C is serious public health challenge throughout the world.Hepatitis B and C viruses still remain to be the major causes of chronic hepatitis.It is estimated that around 350-400 million people in the world are chronic carriers of HBV, which represents approximately 7% of the total populationwhereas infection with HCV is found in approximately 3% of the world population, which represents 160 million people. Hepatitis B infection has a wide range of seroprevalence in the Mediterranean countries ranging from intermediate (=>2% ) to high prevalence ( =>7%). World Health Organization estimated a prevalence rate for HCV infection of about 4.6% in Eastern Mediterranean in 1999. During the eightieths

      Compounds from tin oxide doped with gallium oxide and cerium oxide were synthesized. Thin films from (SnO2:Ga2O3,CeO2) with different doping ratios were prepared on glass and single crystal silicon as substrates with the use of the pulsed laser deposition technique. The results of FTIR spectrums analysis was presented. Varies heterojunctions were fabricated from (SnO2:Ga2O3,CeO2 /Cu2S/c-pSi) heterojunctions solar cell which are formed from two layers: the first was Cu2S and the second was layer from tin oxide doped with two oxides named gallium oxide and cerium oxide with different doping ratios (0, 0.03, 0.05, and 0.07). The heterojuntion (SnO2:5%Ga2O3 /Cu2S/c-pSi photovoltaic structure exhibits open circuit voltage (Voc

Due to design errors and changes in the use of buildings, reinforced concrete (RC) columns must often be strengthened to support additional live loads. The column must be designed to withstand both axial loads and bending moments, and an interaction diagram is necessary to demonstrate the column failure. The most common technique for strengthening RC columns uses a steel jacket consisting of four steel angles and battens. In this study, another strengthening technique was proposed that uses two steel C-sections with steel battens. A new approach for constructing an axial force-bending moment interaction diagram for RC columns strengthened with steel C-section jackets using an analytical model based on the plastic stress distribution

The isolates of Staphylococcus aureus were isolated from patients with various infections in hospitals, the isolates were identified and accurately diagnosed by phenotypic examination and biochemical tests, as well Vitek-2, and then genetic detection and diagnosis of many of the pathogenic factors associated with Staphylococcus aureus using conventional polymerase chain reaction (PCR) and testing for association by antibiotic resistance and production of some toxins by Staphylococcus aureus. After performing analysis of statistical, it was set up that the correlation coefficient of the PCR technique using virulence genes, sensitivity test to antibiotics and other virulence factors were significant at p < 0.05, but was insignificant with the

This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59%  have been achieved for reinforced RPC contains  910 kg/m³ cement content, silica fume content 185 kg/m³ of cement weight and fiber volume fraction 2%. The water absorption values w

The study investigated the behaviour of asphalt concrete mixes for aggregate gradations, according to the Iraqi specification using the Bailey method designed by an Excel spreadsheet. In mixing aggregates with varying gradations (coarse and fine aggregate), The Bailey method is a systematic methodology that offers aggregate interlocking as the backbone of the framework and a controlled gradation to complete the blends. Six types of gradation are used according to the bailey method considered in this study. Two-course prepared Asphalt Concrete Wearing and Asphalt Concrete binder, the Nominal Maximum Aggregate Sizes (NMAS) of the mixtures are 19 and 12.5 mm, respectively. The total number of specimens was 240 for both layers (15 samp

This work investigates generating of pure phase Faujasite-type zeolite Y at the ranges chosen for this study via a static aging step in the absence of seeds synthesis. Nano-sized crystals may result when LUDOX AS-40 is used as a silica source for gel composition of range 6 and the crystallization step may be conducted for a period of 4 to 19 hr at 100 ⁰C. Moreover, large-crystals with high crystallinity pure phase Y zeolite can be obtained at hereinabove conditions but when hydrous sodium metasilicate is used as a silica source. The other selected ranges also offer pure phase Y zeolite at the same controlled conditions.

This work investigates generating of pure phase Faujasite-type zeolite Y at the ranges chosen for this study via a static aging step in the absence of seeds synthesis. Nano-sized crystals may result when LUDOX AS-40 is used as a silica source for gel composition of range 6 and the crystallization step may be conducted for a period of 4 to 19 hr at 100 ⁰C. Moreover, large-crystals with high crystallinity pure phase Y zeolite can be obtained at hereinabove conditions but when hydrous sodium metasilicate is used as a silica source. The other selected ranges also offer pure phase Y zeolite at the same controlled conditions.