Effect of etchant type and the use of silane on the shear bond strength of composite resin to porcelain
...Show More Authors

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transparent split mold (4mm- diameter and 4mm-height). Specimens were stored in distilled water for 24 hours then thermocycled for 100 cycles. Shear bond strength was determined by a Zwick universal machine at a cross-head speed 5 mm/minute. Results: Mean shear bond strength values were 21.02(group I), 23.31(group II), 4.00(group III), and 18.60(group IV). Paired-t revealed that specimens treated with 5%hydrofluoric acid were significantly higher than those treated with 37%phosphoric acid regardless the use of silane. The use of silane dramatically enhanced the bond strength of composite resin to porcelain for both acids. All specimens treated with 37%phosphoric acid without silane showed adhesive failure, while those treated with 5%hydrofluoric acid showed mostly cohesive failure within ceramic. Conclusion: Silane improved the shear bond strength of composite to ceramic, and hydrofluoric acid performed greater bond strength compared to phosphoric acid.

Preview PDF
Quick Preview PDF
Publication Date
Sat Mar 01 2008
Journal Name
Al-khwarizmi Engineering Journal
Study the Effect of Carbon Fiber Volume Fraction and their Orientations on the Thermal Conductivity of the Polymer Composite Materials.
...Show More Authors

      The effect of fiber volume fraction of the carbon fiber on the thermal conductivity of the polymer composite material was studied. Different percentages of carbon fibers were used (5%, 10%, 15%, 20%, and 25%). Specimens were made in two groups for unsaturated polyester as a matrix and carbon fibers, first group has parallel arrangement of fibers and the second group has perpendicular arrangement of fibers on the thermal flow, Lee's disk method was used for testing the specimens. This study showed that the values of the of thermal conductivity of the specimens when the fibers arranged in parallel direction was higher than that when the fibers arranged in the perpendicular direction  

 &nbsp

... Show More
View Publication Preview PDF
Publication Date
Thu Jul 10 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of addition of hydroxyapatite microscopic fillers on surface roughness and some mechanical properties of heat cured acrylic resin
...Show More Authors

Background: this study aimed to evaluate the effect of addition of hydroxyapatite micro filler in three concentrations (5%, 10%, 15%) on surface roughness, impact strength, flexural strength and hardness. Material and methods: One hundred sixty acrylic samples were used in this study,40 samples were used for each test(impact strength ,flexural strength ,hardness and surface roughness).The test group divided into four subgroups(n=10) for controlgroup,5%,10% ,15%H,A.concentration addition groups .Impact testing device, flexural strength testing device, shore hardness tester and profilometer device were used to measure the four tests examined in this study. Results: the results showed a significant increase in impact strength, hardness in all

... Show More
View Publication Preview PDF
Publication Date
Thu Jul 10 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of addition of untreated and oxygen plasma treated polypropylene fibers on some properties of heat cured acrylic resin
...Show More Authors

Background: The polymethyl methacrylate is the most reliable material for the construction of complete and partial dentures, despite satisfying esthetic demand itsuffered from having unsatisfactory properties like impact strength and transverse strength. This study was designed to improve the impact strength and transverse strength of heat cure acrylic resin by adding untreated and oxygen plasma treated polypropylene fibers and investigate the effect of this additive on some properties of acrylic resin materials. Materials and methods: Untreated and oxygen plasma treated polypropylene fibers was added to PMMA powder by weight 2.5 %. Specimens were constructed and divided into 5 groups according to the using tests; each group was subdivided

... Show More
View Publication Preview PDF
Publication Date
Fri Mar 01 2019
Journal Name
Al-khwarizmi Engineering Journal
Studying the Effect of Volume Fraction of Glass Fibers on the Thermal Conductivity of the Polymer Composite Materials
...Show More Authors

In this study the effect of fiber volume fraction of the glass fiber on the thermal conductivity of the polymer composite material was studied. Different fiber volume fraction of glass fibers were used (3%, 6%, 9%, 12%, and 15%). Specimens were made from polyester which reinforced with glass fibers .The fibers had two arrangements according to the direction of the thermal flow. In the first arrangement the fibers were parallel to the direction of the thermal flow, while the second arrangement was perpendicular; Lee's disk method was used for testing the specimens. The experimental results proved that the values of the thermal conductivity of the specimens was higher when the fibers arranged in parallel direction than that when the fibers

... Show More
View Publication Preview PDF
Publication Date
Fri Dec 15 2017
Journal Name
Journal Of Baghdad College Of Dentistry
In Vitro Comparative Assessment Of The Effect Of Gutta-Fusion Obturation On The Push Out Bond Strenght Of Three Types Of Sealers
...Show More Authors

Background: The bond strength of the root canal sealers to dentin is very important property for maintaining the integrity and the seal of root canal filling. The aim of this study was to evaluate and compare the push-out bond strength of root filled with total fill Bioceramic, AH Plus and Gutta-flow®2 sealers using GuttaFusion®obturation system versus single cone obturation technique. Materials and method: sixty of mandibular premolars teeth with straight roots were used in this study, these roots were instrumented using Reciproc system, instrumentation were done with copious irrigation of 3 mL 5.25% sodium hypochlorite solution (NaOCl) during all the steps of preparation, and smear layer will be removed with 1 ml of 17% EDTA kept in

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Thu Jul 10 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation of the effect of addition of polyester fiber on some mechanical properties of heat cure acrylic resin
...Show More Authors

Background: This study aimed to evaluate the effect addition of polyester fibers on the some mechanical properties of heat cured acrylic resin (implant strength, flexural strength and hardness) Materials and methods: Ninety specimens were used in the study. Thirty specimens were used for impact strength measurements (80mm X 10mm X 4mm) length, width and thickness respectively. The specimens divided into three test groups (n=10), first group formed from heat cure acrylic resin without fiber reinforcement. Second group was formed from heat cure acrylic resin was reinforced with 2 mm length polyester fiber and third group was formed from heat cure acrylic resin reinforced with 4mm length polyester fiber, impact strength measured by impact test

... Show More
View Publication Preview PDF
Publication Date
Thu Sep 15 2022
Journal Name
Journal Of Baghdad College Of Dentistry
The push out bond strength of bioceramic seal-er(Total Fill) after warm and cold obturation tech-niques An in vitro comparative
...Show More Authors

Background: The goal of a root canal treatment is three dimensional obturation with a complete seal of the root canal system. The aim of this study was to evaluate and compare the effect of two warm obturation techniques, warm vertical compaction (WVC) and, carrier based obturation technique Gutta Core (GC), versus two cold obturation techniques, cold lateral compaction (CLC) and, single cone (SC) on push-out bond strength of bioceramic sealer (Total Fill) at three different root levels. Materials and Methods: Forty extracted maxillary first molars teeth with a straight round palatal root canal and mature apices were selected for this study. After sectioning the palatal roots to 11 mm from the root apex, the canals were

... Show More
View Publication Preview PDF
Scopus (6)
Crossref (5)
Scopus Crossref
Publication Date
Thu Sep 15 2022
Journal Name
Journal Of Baghdad College Of Dentistry
The push out bond strength of bioceramic seal-er(Total Fill) after warm and cold obturation tech-niques An in vitro comparative
...Show More Authors

Background: The goal of a root canal treatment is three dimensional obturation with a complete seal of the root canal system. The aim of this study was to evaluate and compare the effect of two warm obturation techniques, warm vertical compaction (WVC) and, carrier based obturation technique Gutta Core (GC), versus two cold obturation techniques, cold lateral compaction (CLC) and, single cone (SC) on push-out bond strength of bioceramic sealer (Total Fill) at three different root levels. Materials and Methods: Forty extracted maxillary first molars teeth with a straight round palatal root canal and mature apices were selected for this study. After sectioning the palatal roots to 11 mm from the root apex, the canals were prepared wit

... Show More
Preview PDF
Crossref (5)
Crossref
Publication Date
Wed Aug 30 2023
Journal Name
Al-kindy College Medical Journal
The Effect of Melatonin on Body Weight and the Potential use of Melatonin as an Anti-Obesity Agent
...Show More Authors

Background: obesity is a major global health problem with more than 200 million obese men and almost 300 million obese women. Melatonin is a well-known molecule for its involvement in circadian rhythm regulation and has multiple pathological actions including control of appetite, sleep wake cycle and metabolic syndrome.

Aim: to estimate the effect of melatonin supplements on obese patients on a calorie restricted diet in comparison to patients on lifestyle measures only in the form of weight loss, waist circumference and sleep quality.

Subjects and Method: one hundred patients with body mass index > 24 were collected, fifty patients were starte

... Show More
View Publication Preview PDF
Scopus (2)
Scopus Crossref
Publication Date
Mon Mar 08 2021
Journal Name
Baghdad Science Journal
Effect of storage duration on the Type and concentration of aflatoxin in local paddy and polished rice.
...Show More Authors

?Natural Occurrence of aflatoxin Bi and B2 was investigated monthly in paddy rice stored for duration of six months. Aflatoxin B| was detected at the beginning of storage. The concentration of aflatoxin Bi in paddy and polished rice was found to be (0.3 and ()) ppb respectively while aflatoxin B2 W'as not detected in both paddy and polished rice afler six months of storage, concentration of aflatoxin Bi ‘ ’ ' reached 3 ppb in paddy rice and 0.9 ppb in polished rice, while the study proved that the concentration of aflatoxin in paddy rice was higher than polished rice as a result of processing which reduce the toxin

View Publication Preview PDF