In the present work effect of recycled heating and cooling on the values of concrete compressive strength due to high temperature of 400⁰C was studied.

    The tests show that the percent of reduction in compressive strength of the samples which exposed to a temperature of 400⁰C for one cycle was 32.5%, while the reduction was 52.7% for the samples which were exposed to recycled heating and cooling of ten times .      

   Moreover a study of the effect of specimen sizes on the percentages of compressive strength reduction due to high temperature

Phase change materials are known to be good in use in latent heat thermal energy storage (LHTES) systems, but one of their drawbacks is the slow melting and solidification processes. So that, in this work, enhancing heat transfer of phase change material is studied experimentally for in charging and discharging processes by the addition of high thermal conductive material such as copper in the form of brushes, which were added in both PCM and air sides. The additions of brushes have been carried out with different void fractions (97%, 94% and 90%) and the effect of four different air velocities was tested. The results indicate that the minimum brush void fraction gave the maximum heat transfer in PCM and reduced the time

Background: Poly (methyl methacrylate) has been widely utilized for fabrication of dentures for many years as it has good advantages but not achieved all demands of the mechanical properties such as low transverse strength, low impact strength, low surface hardness, high water solubility and high water sorption. Material and method: To provide bonding between ZrO2 nanoparticles and PMMA matrix, the ZrO2 Nano-fillers were surface-treated with a saline coupling agent. Plasma surface treatment of polyethylene (PE) fiber was done to change surface fiber by using DC- glow discharge system. For characterization of interring any functional groups, the (FTIR) spectrum were done .then the mechanical properties studied to choose the appropriate perc

Abstract In the current contribution, a novel binuclear nickel(II) and zinc(II) complexes were prepared from a hexadentate ligand prepared via condensation of 3,3'-Bipyridine-6,6'-dicarbaldehyde , 2-amino-5-chlorobenzaldehyde and 2-Aminophenol .The symmetric ligand (H2DTPE) and its metal complexes were illustrated utilizing various techniques of physicochemical containing magnetic moment, analytical analysis and spectroscopy of mass, IR, 13C and 1H NMR, TGA and UV-Vis. The particles of MO Nanoscale were created from the labeled complex applying the ways of pyrolysis and utilizing methods of XRD, FT-IR, and FE-SEM, that specified close compatibility with the typical pattern for nanoparticles of NiO, ZnO and appeared the reasonable size in

Industrial development has recently increased, including that of plastic industries. Since plastic has a very long analytical life, it will cause environmental pollution, so studies have resorted to reusing recycled waste plastic (sustainable plastic) to produce environmentally friendly concrete (green concrete). In this research, producing environmentally friendly load-bearing concrete masonry units (blocks) was considered where five concrete mixtures were compressed at the blocks producing machine. The cement content reduced from 400 kg/m³ (B-400) to 300 kg/m³ (B-300) then to 200 kg/m³ (B-200). While (B-380) was produced using 380 kg/m³ cement and 20 kg/m³ nano-sil

In this work, the experimental data of four eco-friendly soil stabilizers—recycled concrete aggregate (RCA), recycled aggregate concrete (RAC), Class F fly ash, and nano-MgO— used for low plasticity clay (CL) are synthesized in a comparative manner. A well-organized secondary database was developed for OMC and MDD, UCS, soaked CBR, ultimate bearing capacity, and settlement. Differences between studies were controlled by limiting the data to similar test conditions and calculating changes from each source study’s respective untreated control. OMC was raised by the fly ash from 17.2% to 20.2%, while MDD was decreased from 1.80 g/cm3 (3% dosage) to 1.69 g/cm3 (9% dosage). RCA and RAC yielded maximum dry density (MDD) of 1.86

synthesis, Composition, Spectral, Geometry and Antibacterial Applications ofMn(||),Ni(||),Co(||),Cu(||) and Hg(||) schiff Base complexes of N2O2 mixed donor with 1,10-phenanthroline