In this research we investigated the corrosion behavior of the commertialy pure titanium and Ti-6Al-4V alloy that coated with hydroxyapatite by electrochemical deposition with applied voltage (6,9,12) Volt from aqueous solution containing Ca(NO3)2.H2O =7.0 gm/l , (NH4)2HPO4 =3.5 gm/l , Na(NO3)2 = 8.5 gm/l in order to improve the bonding strength of hydroxyapetite and medical metals and alloys and increasing the biocompatibility. The coating layer morphology was investigated by XRD, Optical microscope , and SEM tests, the corrosio tests was made by use senthesys simulated body fluid (SBF) , and we found that the propreate voltage for coatint on Ti was 9 Volt and for Ti-6Al-4Vwas12Volt.

Background: Fixed orthodontic appliances impede the maintenance of oral hygiene and result in plaque accumulation leads to enamel demineralization caused by acids produced by bacteria. Studies on plaque control strategies in orthodontic populations are limited. This might be caused by difficulties in the quantitative evaluation of dental plaque because the teeth have various levels of bracket coverage, and different tooth sizes and malocclusions, making the traditional categorical indices complex. The present study aims to evaluate the effect of different hygiene protocols on plaque quantity on bands with different attachments. Materials and method: Twenty patients had four bands within the orthodontic appliance. Then randomly divided into

Architecture forms theoretical summaries and multi systems that have the essence of change, and that what distinguishes Architecture from other sciences and their systems. Architecture means way of life via its expressional products and that appears through its systems. These systems are based on formative and technological properties in form, structure, services and materials as well as
their moral forms. All these are associated with techniques and facilities in order to establish integrated system.
Architectural creation does not come from void but it depends on a conception base to create a new condition for creative architectural product. The general problem of the research concentrated on limited theoretical and practica

Abstract  :

The present study aims at identifying the status of the two research variables in the organization under study and specifying the relationship and impact of the authentic leadership with all its four branch dimensions of (self-awareness, transparent relations, balanced processing of information and the moral perspective) on business process reengineering.

The basic problem of the study lies in the attempt to present a new leadership style that is more responsive to the dynamic changes surrounding it based on the authentic leadership behaviors. This is because this pattern has an impact on the nature of the organization's work and its progress.

The research

Microbial antibiotics resistance is considered a serious health issue in the Middle East and developing countries. In this study, the Fe₂O₃ nanoparticles was prepared chemically, and the particles size and shape were analyzed by using Scan electron microscope (SEM) and X-Ray diffraction (XRD). Different concentration of Fe₂O₃ nanoparticles were used and examined on E.coli and S. aureus. Using liquid dilution and in vitro cytotoxicity assay by microplate toxicity test (MTT). The microbial cell metabolic activity was measured on gram-negative, gram-positive bacteria and fungi after treating with different concentrations of Fe₂O₃ nanoparticl

In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C,

The effect of mixed corrosion inhibitors in cooling system was evaluated by using carbon steel specimens and weight loss analysis. The carbon steel specimens immersed in mixture of sodium phosphate (Na₂ HPO₄) used as corrosion inhibitor and sodium glocunate (C₆ H₁₁ NaO₇) as a scale dispersant at different concentrations (20,40, 60, 80 ppm) and at different temperature (25,50,75 and 100)ºC for (1-5) days. The corrosion inhibitors efficiency was calculated by using uninhibited and inhibited water to give 98.1%. The result of these investigations indicate that the corrosion rate decreases with the increase the corrosion inhibitors concentration at 80 ppm and at 100ºC for 5 days, (i.e,

The special core analysis tests were accomplished on a set of core plugs for Mishrif Formation (mA, mB1, and mB2cde/mC units) in West Qurna/1 oilfield, southern Iraq. Oil relative permeability (K_ro) data and the Corey-type fit of the data as functions of the brine saturation at the core outlet face for individual samples in the water-oil imbibition process to estimate relative permeability measurements by the centrifuge method were utilized. Identical correlations for oil and water relative permeabilities were extracted by steady-state and unsteady-state methods. For the mA samples, the gas-water capillary pressure curves were within a narrow range (almost identical) indicating that mA is a homogeneous unit. Kro curves for thr