In the present study, MIG welding is carried out on low carbon steel type (AISI 1015) by using electrode ER308L of 1.5mm diameter with direct current straight polarity (DCSP). The joint geometry is of a single V-butt joint with one pass welding stroke for different plate thicknesses of 6, 8, and 10 mm. In welding experiments, AISI 1015 plates with dimensions of 200×100mm and edge angle of 60^o from both sides are utilized. In this work, three main parameters related to MIG welding process are investigated, which are welding current, welding speed, heat input and plate thickness, and to achieve that three groups of plates are employed each one consists of three plates. The results indicate that increasing the weld heat input (t

The aim of the research is to prepare practical volleyball lessons by using the four pillars strategy for middle school students, and to identify the effect of the four pillars strategy in performing the transmission and volleyball skills in the second intermediate students, to assume that the two researchers assume that there are no statistically significant differences between the results of my skill performance tests Sending and preparing tribal and remote volleyball for the experimental and controlled groups, and there are no statistically significant differences between the results of the performance of the transmission and preparation skills of the volleyball between the two experimental and control groups, and the research co

Background: obesity is a major global health problem with more than 200 million obese men and almost 300 million obese women. Melatonin is a well-known molecule for its involvement in circadian rhythm regulation and has multiple pathological actions including control of appetite, sleep wake cycle and metabolic syndrome.

Aim: to estimate the effect of melatonin supplements on obese patients on a calorie restricted diet in comparison to patients on lifestyle measures only in the form of weight loss, waist circumference and sleep quality.

Subjects and Method: one hundred patients with body mass index > 24 were collected, fifty patients were starte

Background: the aim of this study was to evaluate the effect of different surface acids treatments (37%phospjoric acid, 5%hydrofluoric acid, 1.23 acidulated phosphate fluoride) of feldspathic ceramic VITA 3D MASTER , and the effect of thermocycling on shear bond strength using a ceramic repair kit (ivoclar/vivadent). Material and Methods: sixty Nickel-Chromium metal base plates were prepared(9mm diameter,3mm depth) using lost wax technique, 2mm thick layer of ceramic(VITA 3D MASTER) fused to metal plates, all specimens were embedded in acrylic resin blocks except their examined surfaces and divided into 3 main groups 20 specimens each, Grp A: treatment with 37%phosphoric acid for 2 mins, Grp B: etching with 5% hydrofluoric acid for 2mins,

The aqueous extract of banana fruits peal was tested for its effect on mitosis . The root tips of Allium cepa were used as plant test system and the bone marrow cells of the albino mice Mus musculus were used as mammalians test system in vivo .Root tips of Allium cepa were treated for four hours with five concentrations of the extract (5 , 10 , 20 , 40 ,60 mg / ml.).The Metaphase was arrested in all the treatments , the highest percentage ( 100 % ) was recorded in the first concentration , the last concentration caused stickiness and clumping of the chromosomes. The treatments did not cause significant difference in the mitotic index. The peals extract (5 mg /ml) was compared with the extracts of fruits bulb, leaves and roots of

                In this investigation a high density polyethylene (HDPE) was used as a substitute to polyvinylchloride in the production of lead acid battery separators. This has been achieved by preparing mixtures of different percentages of the feed materials which include a high density polyethylene (HDPE) locally produced, filler materials such as silica and oils such as dioctylphthalate (DOP) or paraffin which were added to the mixture to improve the final properties of the separator. The materials were compounded by two roll-mills under the same conditions. The following parameters are involved:           &nb

A high Tc superconductor with a nominal composition
(Bi1-xPbx)2(Sr1-yBay)2Ca2Cu3O10+δ for (0 £ x £ 0.5) and (0 £ y £ 0.5) was prepared by
a solid state reaction method. The effect of the substitution of Pb for Bi and Ba for Sr and
quenching temperature on the superconductivity has been investigated to obtain the
optimum conditions for the formation and stabilization of the high Tc phase (2223).
The results showed that the optimum sintering temperature for the pure composition is
equal to 875°C and the sintering time is equal to 240h with heating and cooling rate of
60°C/h . Our results indicated that a small amount of (Ba = 0.1) could raise the transition
temperature (Tc), but enhancing Ba to 0.4 has raised