The effect of the concentration of the colloidal nanomaterial on their optical limiting behavior is reported in this paper. The colloids of sliver nanoparticles in deionized water were chemically prepared for the two concentrations (31 ppm and 11ppm). Two cw lasers (473 nm Blue DPSS laser and 532 nm Nd:YAG laser) are used to compare the optical limiting performance for the samples. UV–visible spectrophotometer, transmission electron microscope (TEM) and Fourier Transformation Infrared Spectrometer (FTIR) were used to obtain the characteristics of the sample. The nonlinear refractive index was calculated to be in the order of 10-9 cm2/W. The results demonstrate that the observed limiting response is significant for 532nm. In addition, t

A range of macrocyclic dinuclear metal (II) dithiocarbamate-based complexes are reported. The preparation of complexes was accomplished from either mixing of the prepared ligand with a metal ion or through a template one-pot reaction. The preparation of the bisamine precursor was achieved through several synthetic steps. The free ligand; potassium 2,2'-(biphenyl-4,4'-diylbis(azanediyl))bis(1-chloro-2-oxoethane-2,1diyl)bis(cyclohexylcarbamodithioate) (L) was yielded from the addition of CS2 to a bis-amine precursor in  KOH medium.A variety of analytical and physical methods were implemented to characterise ligand and its complexes. The analyses were based on spectroscopic techniques (FTIR, UV-Vis, mass spectroscopy and 1H, 13C-NMR sp

Two hundred fifty mid-stream urine specimens were collected from Baqubah Teaching Hospital and Al-Batool Teaching Hospital from patients with urinary tract infections (UTI). Of these investigated urine specimens, 66 (26.4%) specimens showed positive growth culture of Gram-negative bacteria. From these, Escherichia coli was the most prevalent bacteria of the examined culture (41, 62.12%). Additionally, the cup assay was used to determine colicin producers while the most efficient colicin producers were estimated by the formation of larger inhibition zone. Approximately half of the investigated E. coli isolates (20, 49 %) was colicin producers. Colicins was extracted after induction by mitomycin-C showed a concentration o

This study focused on the biological synthesis of silver nanoparticles (AgNPs), using prodigiosin pigment produced by Serratia marcescens. The effect of parameters such as pH, temperature, time, with various concentrations of silver nitrate (AgNO₃) and prodigiosin on the synthesis of AgNPs were also studied.  Optimized results of the biosynthesis process revealed an increase in the intensity of Surface Plasmon Resonance (SPR) bands of nanoparticles with shifting at the wavelength of 400 nm. In addition, optimum synthesis of AgNPs was achieved at pH 12, temperature 55℃, and reaction time 24 h, with concentrations of prodigiosin, as a reducing agent, of 12.5 µg/ml and silver ion concentration of 1 mM. Measuremen

The addition of new reactive sites on the surface area of the inert sand, which are represented by layered double hydroxide nanoparticles, is the primary goal of this work, which aims to transform the sand into a reactive material. Cetyltrimethylammonium bromide (CTAB) surfactant is used in the reaction of calcium extracted from solid waste-chicken eggshells with aluminum prepared from the cheapest coagulant-alum. By separating amoxicillin from wastewater, the performance of coated sand named as "sand coated with (Ca/Al-CTAB)-LDH" was evaluated. Measurements demonstrated that pH of 12 from 8, 9, 10, 11, and 12, CTAB dosage of 0.05 g from 0, 0.03, 0.05, and 0.1 g, ratio of Ca/Al of 2 from 1, 2, 3, and 4, and mass of sand of 1 g/50 mL from

New 2-amino thiazole ,oxodiazole, sulphonilamide and diazin derivatives of N-(α-chloro aceto)-3-(tolyl imino)-5-bromo-2-oxo-indole(2) have been synthesized .The preparation process started by the reaction of 5-bromo isatin with  P-toluidine in the presence of glacial acetic acid and dimethylformamide(DMF) as a solvent to give  3-(tolyl imino)5-bromo-1H-indole-2-one.(1), Compound (1) with sodium hydride  in dimethylformamide(DMF) at 0C0 gave a suspension of the sodium salt of Schiff base derivative and subsequent reaction with monochloroacetylchloride obtained  the intermediate compound(2).Compound(2) was  reacted with different reagents  in four routes.The first route involved direct reaction with substituted  2-aminobenzothiazole u

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.