Experimental tests were conducted to study the behavior of skirted foundations rested on dry medium sandy soil subjected to vertical and inclined loads. To achieve this goal, a small-scale physical model was designed and performed which contained an aluminum circular footing (100 mm) in diameter and (10 mm) in thickness and skirts with different heights, local medium poorly graded dry sand is placed in a steel soil container (2 mm) thick with internal dimensions (1000 mm x 1000 mm in cross section and 800 mm in height). The main objective of this study was to evaluate the response of skirt attached to the foundation at different skirt (L/D) ratios (0.0, 0.5, 1.0 and 1.5) and is subjected to point load at different angles of inclinat

Catalytic wet air oxidation of aqueous phenol solution was studied in a pilot plant trickle bed reactor using copperoxide catalyst supported on alumina and silica. Catalysts were prepared by impregnating method. Effect of feed solutionpH (5.9, 7.3, and 9.2), gas flow rate (20%, 50%, 80%, and 100%), WHSV (1, 2, and 3 h-1), temperature (120°C, 140°C,and 160°C), oxygen partial pressure (6, 9, 12 bar), and initial phenol concentration (1, 2, and 4 g/l).Generally, theperformance of the catalysts was better when the pH of feed solution was increased. The catalysts deactivation is relatedto the dissolution of the metal oxides from the catalyst surface due to the acidic conditions. Phenol oxidation reactionwas strongly affected by WHSV,

In the present study ten samples of bottled water from Baghdad conservative were taken to measure the concentration of radon gas by using nuclear track detector LR-115.The result obtained are varying from(0.033)to(0.007)pCi.l-1and these values are very low than the allowed limits (5) pCi.l-1, and specific activity from bottled water has been calculated which was vary from (0.00027)to(0.00126) Bq.l-1 and these values are very low than allowed limits (0.0123) Bq.l-1 that mean the bottled water was treated with good treatment to decrease the side effect of radon

A fixed callus weight of 150 mg was induced from immature embryos of three bread wheat Triticum aestivum L. genotypes (Tamos 2, El-izz and Mutant 1) cultured on nutrient medium {MS) containing Polyethylene glycol (PEG-6000) supplemented with concentrations (0.0, 3.0, 6.0, 9.0 or 12.0%) to evaluate their tolerance to water stress. Cultures were incubated in darkness at temperature of 25?1 ?C. Callus fresh and dry weights were recorded and soluble Carbohydrate and the amino acid Proline concentrations were determined. Results showed that there were significant differences in studied parameters among bread wheat genotypes of which Tamos 2 was higher in callus average fresh and dry weights which gave 353.33 and 38.46 mg/cultured tube respecti

Sediment samples were collected from main water processing and supply plants in Baghdad, and tested for radioactivity from both natural and artificial sources. These stations are: East Dijla (Tigris), Al-Kadisia, Al-Karama, Al-Rasheed, Al-Sader, Al-Wathba, and Al-Wihda supply stations. Qualitative measurements were made, and the results showed that most sediments exhibited natural radioactive level and sometimes less than the international regular standards. Specially, K-40 and Ra-226 results were much less than the standards for radioactive concentrations. Ac-228 concentration was found rather than Th-232 (in Al-Sader and Al-Wihda samples) but with low concentrations of about 10-15 Bg/kg and detection confidence ~45% , and Ce-141 and Be

Resistance spot welding (RSW) aluminum alloys has a major problem of inconsistent quality from weld to weld, because of the problems of the non-uniform oxide layer. The high resistivity of the oxide causes strong heat released which influence significantly on the electrode lifetime and the weld quality. Much effort has been devoted experimentally to the study of the sheet surface characteristics for as-received sheet and surface pretreatment sheet by pickling in NaOH and glassblasted with three thicknesses (0.6, 1.0, and 1.5 mm) of AA1050. Three different welding process parameters energy setup as a low, medium, and high were carried. Tensile-shear strength tests were performed to indicate the weld quality. Moreover, microhardness tests,

The current research deals with practical studies that explain to the Iraqi consumer multiple instances about the phenomenon of water hammer which occur in the water pipeline operating with pressure. It concern a practical study of the characteristics of this phenomenon and economically harmful to the consumer the same time. Multiple pipe fittings are used aimed to reduce this phenomenon and its work as alternatives to the manufactured arresters that used to avoid water hammer in the sanitary installations, while the consumer did not have any knowledge as to the non-traded for many reasons, including the water pressure decreases in the networks and the use of consumer pumps to draw water directly from the network. Study found a number of