In this investigation insulator ceramic body was prepared by using iraqi local materials, these are kaolin, silica sand glass, feldspar with weight percentage (45%,25%, 30%)respectively.  After the end of treating drying and milling of raw material mixing with different concentrations of sodium silicate(1%,0.7%,0.5%,0.2%,0.1%) while zinc oxide was added at fixed weight percentage.  A disc samples was prepared after compaction and then fired by sintering temperatures (1250, 1350)oC respectively.A surface morphology was studied by using optical microscope and measurements of apparent density and porosity was under taken to the sintered samples by using Archimedes method.The study showed that the microscopic images for samples sur

The effects of reinforcing polymers with glass and graphite particles on enhancing their flexural properties are investigated.   Five composites were fabricated using the same polymer matrix material with different volume fractions of reinforcement particles. They comprise glass particles and graphite particles each  having volume fractions of 20% and 30% as well as a hybrid composite having 10% glass and 10% graphite. Three-point bending tests using a Universal Testing Machine were carried out on specimens of the above mentioned composites, as well as specimens of the polymer matrix material to determine their flexural properties. The experimental test results indicate that the flexural stiffness of all the composites wer

         Polymer blended electrolytes of various concentrations of undoped PAN/PMMA (80/20, 75/25, 70/30, 65/35 and 60/40 wt%) and doped with lithium salts (LiCl, Li₂SO₄H₂O, LiNO₃, Li₂CO₃) at 20% wt have been prepared by the solution casting method using dimethylformamide as a solvent. The electrical conductivity has been carried out using an LCR meter. The results showed that the highest ionic conductivity was 2.80x10^-7 (Ω.cm)^-1 and 1.05x10^-1 (Ω.cm)^-1 at 100 kHz frequency at room temperature for undoped (60% PAN + 40% PMMA) and (80% PAN + 20% PMMA) doped with 20%wt Li₂CO₃ composite blends, respect

A progression of Polyaniline (PANI) and Titanium dioxide (TiO₂) nanoparticles (NPs) were prepared by an in-situ polymerization strategy within the sight of TiO₂ NPs. The subsequent nanocomposites were analyzed using Fourier-transform infrared spectra (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and Energy Dispersive X-Ray Analysis (EDX) taken for the prepared samples. PANI/TiO₂ nanocomposites were prepared by various compound materials (with H₂SO₄ 0.3 M and without it, to compare the outcome of it) by the compound oxidation technique using ammonium persulfate (APS) as oxidant within the sight of ultrafine grade powder of TiO₂ cooled in an ice bath.

This study investigates the ionic conduction dependence on the size of alkaline cations in gel polymer electrolytes based on double iodide can enhance by incorporating a salt having a bulky cation.

Hot mix recycling of asphalt pavements is increasingly being used as one of the major rehabilitation methods by various highway agencies. Besides general savings in costs and energy expended, it also saves our natural resources and environment.  Recycling process presents a sustainable pavement by using the old materials that could be reclaimed from the pavement; these materials could be mixed with recycling agents to produce recycled mixtures. The important expected benefits of recycling process are the conservation of natural resources and reduction of environmental impact. The primary objectives of this work are evaluating the Tensile and Shear Properties of recycled asphalt concrete mixtures, In addition to the

Thin films whose compositions can be expressed by (GeS₂)_100-xGa_x (x=0, 6,12,18) formula were obtained by thermal evaporation technique  of bulk material at a base pressure of ~10^-5 torr. Optical transmission spectra of the films were taken in the range of 300-1100 nm then the optical band gap, tail width of localized states,  refractive index, extinction coefficient were calculated. The optical constants were found to increase at low concentration of Ga (0 to12%) while they decreases with further addition of Ga. The optical band gap was found to change in opposite manner to that of optical constants. The variation in the optical parameters are explained in terms of average bond energy

Lead selenide PbSe thin films of different thicknesses (300, 500, and 700 nm) were deposited under vacuum using thermal evaporation method on glass substrates. X-ray diffraction measurements showed that increasing of thickness lead to well crystallize the prepared samples, such that the crystallite size increases while the dislocation density decreases with thickness increasing. A.C conductivity, dielectric constants, and loss tangent are studied as function to thickness, frequency (10kHz-10MHz) and temperatures (293K-493K). The conductivity measurements confirm confirmed that hopping is the mechanism responsible for the conduction process. Increasing of thickness decreases the thermal activation energy estimated from Arhinus equation is