Oilwell cementing operations are crucial for drilling and completion, preserving the well's productive life. However, weak and permeable formations pose a high risk of cement slurry loss, leading to failure. Lightweight cement, like foamed cement, is used to avoid these difficulties. This study is focused on creating a range of foamed slurry densities and examining the effect of gas concentration on their rheological properties. The foaming agent and foam stabilizer are tested, and the optimal concentration is determined to be 2% and 0.12%, respectively, by the weight of the cement.

Furthermore, the construction of samples of foam cement with different densities (0.8, 1.0, 1.2, 1.4, and 1.6) g/cc is performed to f

The zeolite's textural properties have a significant effect on zeolite's effectiveness in the different industrial processes. This research aimed to study the textual properties of the NaX and FeX zeolites using the nitrogen adsorption-desorption technique at a constant low temperature. According to the International Union of Pure and Applied Chemistry, the adsorption-desorption isotherm showed that the studied materials were mixed kinds I/II isotherms and H3 type hysteresis. The Brunauer-Emmett-Teller isotherm was the best model to describe the nitrogen adsorption-desorption better than the Langmuir and Freundlich isotherms. The obtained adsorption capacity and Brunauer-Emmett-Teller surface area values for NaX were greater than FeX. Ac

In this research, the effect of reinforcing epoxy resin composites with a filler derived from chopped agriculture waste from oil palm (OP). Epoxy/OP composites were formed by dispersing (1, 3, 5, and 10 wt%) OP filler using a high-speed mechanical stirrer utilizing a hand lay-up method. The effect of adding zinc oxide (ZnO) nanoparticles, with an average size of 10-30 nm, with different wt% (1,2,3, and 5wt%) to the epoxy/oil palm composite,  on the behavior of an epoxy/oil palm composite was studied with different ratios (1,2,3, and 5wt%) and an average size of  10-30 nm.  Fourier Transform Infrared (FTIR) spectrometry and mechanical properties (tensile, impact, hardness, and wear rate) were used to examine the composites. The FTIR

In dental and medical applications, poly-methyl methacrylate (PMMA) has been widely accepted due to the excellent biocompatibility and easy fabrication. Yet, some of the physical and mechanical characteristics of this compound are considered inferior. Seven groups of PMMA nano-composite samples were reported to be fabricated at laboratory temperature . These samples could be used in manufacturing the complete or partial maxillary denture base. The aim of this research is to prepare nano-composite materials which consist of PMMA as a matrix material and two different types of powder (prepared nanoparticles of SnO₂ and natural egg shell powder (ESP)) as strengthening materials. The selected additives were used in many cases as p

The need for optical fibers has emerged for its ability to transmit information with less attenuation and over long distances. In this work, four optical fibers with core radii from 1 μm to 4.75 μm in steps of 1.25 μm and a numerical aperture of 0.17 were studied and their modes properties have been calculated at a wavelength of 633 nm by using RP Fiber Calculator (free version 2022). Also, the effect of increasing the core radius on these properties has been studied. Multimode fibers can be obtained when the radius of the fiber core is large compared to the operating wavelength of the fiber which is less than the cutoff wavelength of the mode. Otherwise, a single-mode fiber is obtained. It has been concluded that all the calculated p

     In this paper, new integro-differential operators are introduced that defined by Salagean’s differential operator. The major object of the present study is to investigate convexity properties on new geometric subclasses included these new operators.

In this work, chemical oxidation was used to polymerize conjugated polymer "Polypyrrole" at room temperature Graphene nanoparticles were added by in situ-polymerization to get (PPY-GN) nano. Optical and Electrical properties were studied for the nanocomposites. optical properties of the nanocomposites were studied by UV-Vis spectroscopy at wavelength range (200 -800 nm). The result showed optical absorption spectra were normally determined and the result showed that the maximum absorbance wave length at 280nm and 590nm. The optical energy gap has been evaluated by direct transition and the value has decreased from (2.1 eV for pure PPy) to (1.3 eV for 5 %wt. of GN). The optical constants such as the band tail width ΔE was evaluated, the

  This researchs the preparation of particulate polymer composites from Alkyd resin and Iraqi Burn Kaolin which were added as (20%,30%,40%,50%)and comparing  with the  polymer.  It studied Thermal conductivity and Dielectric strength for both of  the Alkyd resin and  the Composite Material.        The result showed an  increase in Dielectric strength after adding the Iraqi Burn Kaolin , also the Thermal conductivity was  increased by adding the Iraqi Burn Kaolin .