N-type Tin dioxide thin films with thickness (350 nm) prepared by thermal evaporation method. The thin film SnO2 was doped with Ag by the rate (0.01, 0.02 and 0.03). Atomic Force Microscopic (AFM) was adopted to determine the grain size and roughness of the film surface. The electrical properties were determined by mean of Hall Measurement system and mobility was calculated. SnO2: Ag/P–Si photodetectors demonstration the highest described visible responsivity of (0.287 A/W) with the Ag ratio of (0.03). I–V characteristics with different power density were measured. The best sensitive value of the spectral response, specific detectivity and quantum efficiency at wavelength (422 nm).

The eff ect of partial substitution for lanthanum (La) on the structural properties of the compound Y1-xLaxBa4Cu7O15+δ were studied. The variation of (x) are x=0.1, 0.2 and 0.3, which was synthesized by solid state reaction method. The mixed powder was pressed with pressure (7 ton / cm2) as a disc (1.5 cm) diameter and a thickness of (0.25 to 0.3 cm). The samples were sintering by 120 °C / hour with a changing rate from room temperature to 850 ° C through 72 hours. XRD analysis using to calculate crystal size, strain and degree of crystallinity. It was found all samples have orthorhombic structure and change of structure with increasing lanthanum concentration. It was shown that the change lanthanum concentrations of all our samp

Fe2O3/ MgO composites with various ratios (90/10,80/20,70/30,60/40 and 50/50 %wt.) were synthesized. Their structure was determined using the X-ray diffractometer. The observed X-Ray patterns showed that the prepared composites were polycrystalline with rhombohedral Hematite (α-Fe2O3) whereas the preferred planes for crystal growth are (104) and (110).The dielectric properties of the Fe2O3/ MgO, with various ratios, were studied as function of frequency over the range (50Hz – 1MHz). The conductivity as function to frequency σa.c(ω) obey the power law relation σa.c(ω) =Aωs where the factor s was found to be in the range 0.329-0.491. The dielectric constant is increasing; but not in a regular way, with the increasing MgO content. The

Mortar of ordinary Portland cement was blended with cockles shell
powder at different weight ratios to investigate the effect of powder
admixture on their strength and thermal conductivity. Results showed
that addition of cockles shell powder at 50% of mortar weight
improves hardness and compressive strength notably and reduces the
thermal conductivity of the end product. Results suggest the
possibility to incorporate cockles shell powders as constituents in
cement mortars for construction and plastering applications.

   This study demonstrates a sustainable, "trash-to-treasure" approach by synthesizing silica (SiO2) and alumina (Al2O3) nanoparticles (30–80 nm) from local waste materials—specifically bentonite clay and aluminum wire waste—and evaluating their performance as eco-friendly additives in 350 mL water-based drilling fluids at concentrations ranging from 0 to 1 g. Tested under harsh subsurface conditions, the incorporated nanoparticles significantly enhanced the fluids' rheological properties, lubricity, filtration control, and swelling inhibition, with performance scaling alongside nanoparticle concentration. Notably, at a 1 g dosage, the fluid's yield point spiked from a baseline of 9 to 42 for SiO2 and 32 for (Al2O3), while h

in this paper copper oxide (cuO thin films were prepared by the method of vacum thermal evaporation a pressure.

The purpose of this work was to study the effects of the Nd:YAG laser on exposed dentinal
tubules of human extracted teeth using a scanning electron microscope (SEM). Eighty 2.5mm-thick
slices were cut at the cementoenamel junction from 20 extracted human teeth with an electric saw. A
diamond bur was used to remove the cementum layer to expose the dentinal tubules. Each slice was
sectioned into four equal quadrants and the specimens were randomly divided into four groups (A to D ).
Groups B to D were lased for 2 mins using an Nd:YAG laser at 6 pulses per second at energy outputs of
80 , 100 and 120 mJ. Group A served as control. Under SEM observation, nonlased specimens showed
numerous exposed dentinal tubules. SEM o

Background: clinically significant macular edema (CSME) is the commonest cause of visual loss in patients with diabetes mellitus and laser focal photocoagulation is the golden standard for treating it. Patients and Methods: A frequency doubled Nd: YAG laser was used to treat all eyes included in this study with diabetic maculopathy. Thirty eyes of three insulin dependent and twenty six non insulin dependent diabetic Iraqi patients were included. The study involved twenty six males, three females and followed for one year. Their ages were ranging between 36- 59 years, all of them from patients attending ophthalmic out-patient department in the medical city in the period between January 2005 and June 2006. Eyes divided in to two groups (fifte